Nickel is widely used as a bleaching element in white gold alloys, but it is a potential allergen. In this paper, a popular 18 KW gold alloy, often called ＂safe nickel,＂ was chosen as the experimental material; its ...Nickel is widely used as a bleaching element in white gold alloys, but it is a potential allergen. In this paper, a popular 18 KW gold alloy, often called ＂safe nickel,＂ was chosen as the experimental material; its nickel release rates under six different processing conditions were evaluated according to the EN1811 standard. The results reveal that both the surface processing method and heat treatment technology significantly affect the nickel release rate. A coarse surface releases more nickel ions than a smooth surface. The sample normalized at 700 ~C in the single region has a lower nickel release rate than the one treated at 550 ~C in the two-phase phase region, while high temperature normalizing at 800 ~C will accelerate it. All the measured nickel release rates of the experimental material under various processing conditions exceed the permitted threshold value in the Nickel Directive, which indicates that there exists the potential risk of nickel- induced allergy when it is used to make jewelries, espe- cially for piercing types.展开更多
基金financially supported by the united foundation of the National Natural Science Foundation of China and Guangdong province (No. U1034002)
文摘Nickel is widely used as a bleaching element in white gold alloys, but it is a potential allergen. In this paper, a popular 18 KW gold alloy, often called ＂safe nickel,＂ was chosen as the experimental material; its nickel release rates under six different processing conditions were evaluated according to the EN1811 standard. The results reveal that both the surface processing method and heat treatment technology significantly affect the nickel release rate. A coarse surface releases more nickel ions than a smooth surface. The sample normalized at 700 ~C in the single region has a lower nickel release rate than the one treated at 550 ~C in the two-phase phase region, while high temperature normalizing at 800 ~C will accelerate it. All the measured nickel release rates of the experimental material under various processing conditions exceed the permitted threshold value in the Nickel Directive, which indicates that there exists the potential risk of nickel- induced allergy when it is used to make jewelries, espe- cially for piercing types.