The corrosion behavior of 16Mn steel was studied in saturated H2S or H2S/CO2 solutions containing different Cl^-concentrations at 80℃.The microstructure and chemical composition of the corrosion products were investi...The corrosion behavior of 16Mn steel was studied in saturated H2S or H2S/CO2 solutions containing different Cl^-concentrations at 80℃.The microstructure and chemical composition of the corrosion products were investigated through scanning electron microscopy,energy-dispersive X-ray spectroscopy,EPMA,and X-ray diffraction.Results showed that the corrosion rate decreased with increasing Cl^-concentration in saturated H2S or H2S/CO2 solution at pH 4.Conversely,the corrosion rate increased with increasing Cl^-concentration in saturated H2S solution at pH 6.The relative H^＋concentration decreased because of the increase of Cl^-concentration at pH 4,and Cl^-acted as a catalyst in the corrosive medium at pH 6 because the net H^＋concentration decreased obviously compared with the condition at pH4.Cl^-promoted the formation of Fe-deficient iron sulfide at pH 4,and the opposite effect was observed in the nearly neutral solution.The corrosion rate increased firstly with increasing Cl^-concentration and then decreased in the saturated H2S/CO2solution at pH 6.The corrosion products were mainly composed of two kinds of iron sulfide.Sulfide FeS（1-x） was a kind of tetragonal crystal,whereas the other was the hexagonal/monoclinic iron sulfide Fe（1-x）S.The corrosion film that was mainly composed of FeS（1-x） did not confer a protective effect on the base metal.The atomic ratio of Fe/S was more than 1 for FeS（1-x）.The appearance of sulfide FeS（1-x） resembled a square block or small,needlelike,flocculent particles.The atomic ratio of Fe/S was less than 1 for Fe（1-x）S,and the corrosion film mainly composed of Fe（1-x）S conferred some protective property on the base metal.The sulfide FeS（1-x） exhibited a long claviform morphology with a hexagonal or quadrilateral cross-sectional shape.展开更多
The resistance spot welding of 6063-T6 aluminum alloy and 16Mn steel was studied by nugget alloying. The results indicated that the Al-steel joint had characteristics of welding-brazing. The nugget zone consisted main...The resistance spot welding of 6063-T6 aluminum alloy and 16Mn steel was studied by nugget alloying. The results indicated that the Al-steel joint had characteristics of welding-brazing. The nugget zone consisted mainly of α-Al solid solution with dislocations and fine Mg2Si particles. The interface zone had a double-layer structure： Fe2Al5 layer at steel side and Fe4Al13 layer at Al nugget side. The nugget alloying has a significant effect on the joint properties by changing phase composition and refinement of grains. When alloy elements Cu, Zn, Ti and Ni were added, the tensile shear load of Al-steel joints reached 2 780 N, 2 910 N, 2 915 N and 2 929 N respectively, which increased by 24. 1%, 29.9%, 30. 1% and 30. 7% respectively compared with that （2 241 N） of joint without nugget alloying. Therefore, it is an effective way for improving mechanical properties of resistance spot welded Al-steel joints.展开更多
基金Funded by National Natural Science Foundation of China(No.51765035)
文摘The corrosion behavior of 16Mn steel was studied in saturated H2S or H2S/CO2 solutions containing different Cl^-concentrations at 80℃.The microstructure and chemical composition of the corrosion products were investigated through scanning electron microscopy,energy-dispersive X-ray spectroscopy,EPMA,and X-ray diffraction.Results showed that the corrosion rate decreased with increasing Cl^-concentration in saturated H2S or H2S/CO2 solution at pH 4.Conversely,the corrosion rate increased with increasing Cl^-concentration in saturated H2S solution at pH 6.The relative H^＋concentration decreased because of the increase of Cl^-concentration at pH 4,and Cl^-acted as a catalyst in the corrosive medium at pH 6 because the net H^＋concentration decreased obviously compared with the condition at pH4.Cl^-promoted the formation of Fe-deficient iron sulfide at pH 4,and the opposite effect was observed in the nearly neutral solution.The corrosion rate increased firstly with increasing Cl^-concentration and then decreased in the saturated H2S/CO2solution at pH 6.The corrosion products were mainly composed of two kinds of iron sulfide.Sulfide FeS（1-x） was a kind of tetragonal crystal,whereas the other was the hexagonal/monoclinic iron sulfide Fe（1-x）S.The corrosion film that was mainly composed of FeS（1-x） did not confer a protective effect on the base metal.The atomic ratio of Fe/S was more than 1 for FeS（1-x）.The appearance of sulfide FeS（1-x） resembled a square block or small,needlelike,flocculent particles.The atomic ratio of Fe/S was less than 1 for Fe（1-x）S,and the corrosion film mainly composed of Fe（1-x）S conferred some protective property on the base metal.The sulfide FeS（1-x） exhibited a long claviform morphology with a hexagonal or quadrilateral cross-sectional shape.
基金supported by National Natural Science Foundation of China(51275204)
文摘The resistance spot welding of 6063-T6 aluminum alloy and 16Mn steel was studied by nugget alloying. The results indicated that the Al-steel joint had characteristics of welding-brazing. The nugget zone consisted mainly of α-Al solid solution with dislocations and fine Mg2Si particles. The interface zone had a double-layer structure： Fe2Al5 layer at steel side and Fe4Al13 layer at Al nugget side. The nugget alloying has a significant effect on the joint properties by changing phase composition and refinement of grains. When alloy elements Cu, Zn, Ti and Ni were added, the tensile shear load of Al-steel joints reached 2 780 N, 2 910 N, 2 915 N and 2 929 N respectively, which increased by 24. 1%, 29.9%, 30. 1% and 30. 7% respectively compared with that （2 241 N） of joint without nugget alloying. Therefore, it is an effective way for improving mechanical properties of resistance spot welded Al-steel joints.