采用极化曲线测定、扫描电镜和金相显微镜技术,对比国外优质1050 PS版板基,研究了热处理工艺对板基电蚀性能的影响。结果表明,具有大量细及均匀分布的第二相颗粒和均匀晶粒组织的板基电解腐蚀性能好。经过600℃×3 m in的高温快速...采用极化曲线测定、扫描电镜和金相显微镜技术,对比国外优质1050 PS版板基,研究了热处理工艺对板基电蚀性能的影响。结果表明,具有大量细及均匀分布的第二相颗粒和均匀晶粒组织的板基电解腐蚀性能好。经过600℃×3 m in的高温快速退火处理后的板基微观组织得到细化,均匀性提高,细小弥散的第二相颗粒大量析出,板基电解活化性能增强,腐蚀均匀、稳定,电解腐蚀性能显著提高。展开更多
The evolution of hardness and microstructures of 1050 aluminum alloy prepared by hot rolling and subsequent equal- channel angular pressing at cryogenic temperature (cryoECAP) after annealing at 150?400 °C for 1 ...The evolution of hardness and microstructures of 1050 aluminum alloy prepared by hot rolling and subsequent equal- channel angular pressing at cryogenic temperature (cryoECAP) after annealing at 150?400 °C for 1 h without and with magnetic field of 12 T was investigated. The electron back scattering diffraction pattern (EBSD) and transmission electron microscopy (TEM) were utilized to characterize the grain microstructures and dislocations. It is demonstrated that the hot rolling before cryoECAP produces more equiaxed grains with a smaller average size and a higher fraction of high angle boundaries (HABs) in the subsequent cryoECAPed 1050 aluminum alloy, thus accelerating the recovery and recrystallization of cryoECAPed alloy and produces more homogeneous microstructure during annealing. The magnetic field promotes the recovery and recrystallization and leads to much lower hardness at 150?250 °C, while it can suppress the abnormal grain growth and form more homogeneous grain size distributions annealed at 300?400 °C.展开更多
Technological parameters of asymmetric cast-rolling under multi-energy field were investigated on horizontal twin roll caster（d400 mm×500 mm）, and their effects on structures and properties of 1050 strips were ...Technological parameters of asymmetric cast-rolling under multi-energy field were investigated on horizontal twin roll caster（d400 mm×500 mm）, and their effects on structures and properties of 1050 strips were analyzed by comparing with traditional cast-rolling. Results show that when length of cast-rolling area is 70 mm, melt temperature of head box is 670 °C, cast rolling speed is 1.3 m/min, exciting current is 10 A, center frequency is（13±1） Hz, ultrasonic power is 200 W and ultrasonic frequency is（20±0.2） kHz, the 1050 strip with the best microstructure can be prepared successfully; its center segregated layer disappears; the average grain size is reduced by about 40%; the crystal grains are distributed evenly; micro segregation decreases obviously; the precipitated phases are distributed along the grain boundaries evenly; and the tensile strength, yield strength, elongation and micro-hardness of cast-rolled strip are improved by 22.6%, 23.66%, 38.75% and 9.90%, respectively.展开更多
The capability of the torsion extrusion （TE） process as a severe plastic deformation （SPD） method was compared with the conventional forward extrusion （FE） process. The TE and FE processes were successfully perf...The capability of the torsion extrusion （TE） process as a severe plastic deformation （SPD） method was compared with the conventional forward extrusion （FE） process. The TE and FE processes were successfully performed on AA1050 alloy samples at room temperature. To simulate the above mentioned processes, finite element analysis was carried out using the commercial elasto-plastic finite element analysis ABAQUS/Explicit Simulation. It is shown that load requirement for the TE process is lower than that for the FE process. The equivalent plastic strain calculated by the FEA proved that higher values of strain are imposed to the sample in the TE process. The strain distribution for the TE sample at the final stage of extrusion shows smoother strain gradient in comparison with the one produced by the FE process.展开更多
文摘采用极化曲线测定、扫描电镜和金相显微镜技术,对比国外优质1050 PS版板基,研究了热处理工艺对板基电蚀性能的影响。结果表明,具有大量细及均匀分布的第二相颗粒和均匀晶粒组织的板基电解腐蚀性能好。经过600℃×3 m in的高温快速退火处理后的板基微观组织得到细化,均匀性提高,细小弥散的第二相颗粒大量析出,板基电解活化性能增强,腐蚀均匀、稳定,电解腐蚀性能显著提高。
基金Project(2011CB606403)supported by the State Basic Research Development Program of ChinaProjects(51171044,51174058)supported by the National Natural Science Foundation of ChinaProject(2012CB723307)supported by the State Basic Research Development Program of China
文摘The evolution of hardness and microstructures of 1050 aluminum alloy prepared by hot rolling and subsequent equal- channel angular pressing at cryogenic temperature (cryoECAP) after annealing at 150?400 °C for 1 h without and with magnetic field of 12 T was investigated. The electron back scattering diffraction pattern (EBSD) and transmission electron microscopy (TEM) were utilized to characterize the grain microstructures and dislocations. It is demonstrated that the hot rolling before cryoECAP produces more equiaxed grains with a smaller average size and a higher fraction of high angle boundaries (HABs) in the subsequent cryoECAPed 1050 aluminum alloy, thus accelerating the recovery and recrystallization of cryoECAPed alloy and produces more homogeneous microstructure during annealing. The magnetic field promotes the recovery and recrystallization and leads to much lower hardness at 150?250 °C, while it can suppress the abnormal grain growth and form more homogeneous grain size distributions annealed at 300?400 °C.
基金Project(2014CB046702)supported by National Basic Research Program of China
文摘Technological parameters of asymmetric cast-rolling under multi-energy field were investigated on horizontal twin roll caster（d400 mm×500 mm）, and their effects on structures and properties of 1050 strips were analyzed by comparing with traditional cast-rolling. Results show that when length of cast-rolling area is 70 mm, melt temperature of head box is 670 °C, cast rolling speed is 1.3 m/min, exciting current is 10 A, center frequency is（13±1） Hz, ultrasonic power is 200 W and ultrasonic frequency is（20±0.2） kHz, the 1050 strip with the best microstructure can be prepared successfully; its center segregated layer disappears; the average grain size is reduced by about 40%; the crystal grains are distributed evenly; micro segregation decreases obviously; the precipitated phases are distributed along the grain boundaries evenly; and the tensile strength, yield strength, elongation and micro-hardness of cast-rolled strip are improved by 22.6%, 23.66%, 38.75% and 9.90%, respectively.
基金been conducted using research grants of Islamic Azad University,Shiraz Branch
文摘The capability of the torsion extrusion （TE） process as a severe plastic deformation （SPD） method was compared with the conventional forward extrusion （FE） process. The TE and FE processes were successfully performed on AA1050 alloy samples at room temperature. To simulate the above mentioned processes, finite element analysis was carried out using the commercial elasto-plastic finite element analysis ABAQUS/Explicit Simulation. It is shown that load requirement for the TE process is lower than that for the FE process. The equivalent plastic strain calculated by the FEA proved that higher values of strain are imposed to the sample in the TE process. The strain distribution for the TE sample at the final stage of extrusion shows smoother strain gradient in comparison with the one produced by the FE process.