Slag movement on SiO2-based prism refractories in different slag systems was observed. The cross section shape evolution mechanism was discussed. Two types of shape evolution appear. For PbO-SiO2 slag whose surface te...Slag movement on SiO2-based prism refractories in different slag systems was observed. The cross section shape evolution mechanism was discussed. Two types of shape evolution appear. For PbO-SiO2 slag whose surface tension improves with SiO2 concentration, slag film flows up along four edges under axial Marangoni shear force and wettability. Then, it flows down along four lateral faces under gravity. Corrosion rate at edges is larger than that on lateral faces due to different SiO2 solubilities of ascending and descending flow. Prism cross section shape changes from square to round. For FetO-SiO2 slag whose surface tension reduces with the increase of SiO2 concentration, slag film flows up under the inflence of wettability. Then, it flows down under Marangoni shear force and gravity. Compared to four edges, slag is mainly up and down on four lateral faces due to larger surface tension and size. So, prism cross section shape keeps square.展开更多
基金Projects(U1738101,51804023)supported by the National Natural Science Foundation of ChinaProjects(FRF-TP-18-007A1,FRF-MP-18-007)supported by Fundamental Research Funds for the Central Universities,ChinaProject(2019M650489)supported by China Postdoctoral Science Foundation
文摘Slag movement on SiO2-based prism refractories in different slag systems was observed. The cross section shape evolution mechanism was discussed. Two types of shape evolution appear. For PbO-SiO2 slag whose surface tension improves with SiO2 concentration, slag film flows up along four edges under axial Marangoni shear force and wettability. Then, it flows down along four lateral faces under gravity. Corrosion rate at edges is larger than that on lateral faces due to different SiO2 solubilities of ascending and descending flow. Prism cross section shape changes from square to round. For FetO-SiO2 slag whose surface tension reduces with the increase of SiO2 concentration, slag film flows up under the inflence of wettability. Then, it flows down under Marangoni shear force and gravity. Compared to four edges, slag is mainly up and down on four lateral faces due to larger surface tension and size. So, prism cross section shape keeps square.