The influences of BaCu（B2O5） （BCB） addition on sintering, microstructure and microwave dielectric properties of Li2MgTi308 ceramics were investigated using X-ray diffractometry, scanning electron microscopy and mi...The influences of BaCu（B2O5） （BCB） addition on sintering, microstructure and microwave dielectric properties of Li2MgTi308 ceramics were investigated using X-ray diffractometry, scanning electron microscopy and microwave dielectric measurements. The experimental results show that a small amount of BaCu（B2O5） addition can effectively reduce the sintering temperature to 900℃, and induce only a limited degradation of the microwave dielectric properties. Typically, the best microwave dielectric properties of er24.5, Q×f =24 622 GHz, rf=4.2×10-6℃ -1 are obtained for 1.0% BCB-doped Li2MgTi3O8 ceramics sintered at 900℃ for 3 h. The BCB-doped Li2MgTi3O8 ceramics can be compatible with Ag electrode, which may be a strong candidate for low temperature co-fired ceramics applications.展开更多
Yttria nanocrystalline powder doped with 9% lanthanum was synthesized by co-precipitation method using ammonia for pH adjusting. After calcinations, finer particles with narrow distribution and large surface area were...Yttria nanocrystalline powder doped with 9% lanthanum was synthesized by co-precipitation method using ammonia for pH adjusting. After calcinations, finer particles with narrow distribution and large surface area were obtained. After dry pressing, samples were sintered at 1500℃―1700℃ for 4 h in vacuum to produce transparent polycrystalline ceramics with uniform grains. Samples with 9 mol% lanthanum were transparent in visible light after being sintered at 1500℃ for 4 h. The grain sizes increased with lanthanum doping compared with those of pure yttria transparent ceramic sintered at the same conditions. Relative density of the transparent ceramic was 99.7%. The in-line transmittance was 73% at 580 nm wavelength after milling and polishing.展开更多
Amorphous SiBCNAl powders were prepared via a mechanical alloying (MA) technique using crystalline silicon (Si), hexagonal boron nitride (h-BN), graphite (C), and aluminum (Al) as starting materials. SiBCNAl powders w...Amorphous SiBCNAl powders were prepared via a mechanical alloying (MA) technique using crystalline silicon (Si), hexagonal boron nitride (h-BN), graphite (C), and aluminum (Al) as starting materials. SiBCNAl powders were consolidated by a hot pressing (HP) technique at 1800 °C under a pressure of 30 MPa in argon and nitrogen. The sintering atmosphere had a great influence on the microstructures and mechanical properties of the ceramics. The two ceramics had different phase compositions and fracture surface morphologies. For the ceramics sintered in argon, flexural strength, fracture toughness, elastic modulus and Vickers hardness were 421.90 MPa, 3.40 MPa·m1/2, 174.10 GPa, and 12.74 GPa, respectively. For the ceramics sintered in nitrogen, the mechanical properties increased, except for the Vickers hardness, and the values of the above properties were 526.80 MPa, 5.25 MPa·m1/2, 222.10 GPa, and 11.63 GPa, respectively.展开更多
CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning ...CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. It is found that there are SiO2 and some unknown phases in CBS glass melting liquid from 1 300 ℃ to 1 500 ℃ and the amount of these phases decreases with the increase of the melting temperature. The CBS glass melted at 1 450 ℃ could be sintered from 830 ℃ to 930 ℃ and the bulk densities of the samples are all higher than 2.4 g/cm^3. From the points of the properties and energy conservation, the melting temperature of 1 450 ℃ is the optimal melting temperature. The glass ceramic sintered at 850 ℃ exhibits better dielectric properties： er=6.33, tan6=2.2×10^-3 at 10 GHz, and the major phases of the samples are CaSiO3, CaB2O4 and SiO2.展开更多
基金Project(2010GXNSFA013029) supported by the Natural Science Foundation of Guangxi Province,ChinaProject(101059529) supported by National Undergraduate Innovation Program of the Ministry of Education of China
文摘The influences of BaCu（B2O5） （BCB） addition on sintering, microstructure and microwave dielectric properties of Li2MgTi308 ceramics were investigated using X-ray diffractometry, scanning electron microscopy and microwave dielectric measurements. The experimental results show that a small amount of BaCu（B2O5） addition can effectively reduce the sintering temperature to 900℃, and induce only a limited degradation of the microwave dielectric properties. Typically, the best microwave dielectric properties of er24.5, Q×f =24 622 GHz, rf=4.2×10-6℃ -1 are obtained for 1.0% BCB-doped Li2MgTi3O8 ceramics sintered at 900℃ for 3 h. The BCB-doped Li2MgTi3O8 ceramics can be compatible with Ag electrode, which may be a strong candidate for low temperature co-fired ceramics applications.
基金Supported by the Shanghai Science and Technology Committee(Grant No.07DJ14001)State Key Laboratory of High Performance Ceramics and Superfine Microstructures
文摘Yttria nanocrystalline powder doped with 9% lanthanum was synthesized by co-precipitation method using ammonia for pH adjusting. After calcinations, finer particles with narrow distribution and large surface area were obtained. After dry pressing, samples were sintered at 1500℃―1700℃ for 4 h in vacuum to produce transparent polycrystalline ceramics with uniform grains. Samples with 9 mol% lanthanum were transparent in visible light after being sintered at 1500℃ for 4 h. The grain sizes increased with lanthanum doping compared with those of pure yttria transparent ceramic sintered at the same conditions. Relative density of the transparent ceramic was 99.7%. The in-line transmittance was 73% at 580 nm wavelength after milling and polishing.
基金Project supported by the National Natural Science Foundation of China (No 50902031)the Development Program for Outstanding Young Teachers in Harbin Institute of Technology (No HITQNJS2009064)
文摘Amorphous SiBCNAl powders were prepared via a mechanical alloying (MA) technique using crystalline silicon (Si), hexagonal boron nitride (h-BN), graphite (C), and aluminum (Al) as starting materials. SiBCNAl powders were consolidated by a hot pressing (HP) technique at 1800 °C under a pressure of 30 MPa in argon and nitrogen. The sintering atmosphere had a great influence on the microstructures and mechanical properties of the ceramics. The two ceramics had different phase compositions and fracture surface morphologies. For the ceramics sintered in argon, flexural strength, fracture toughness, elastic modulus and Vickers hardness were 421.90 MPa, 3.40 MPa·m1/2, 174.10 GPa, and 12.74 GPa, respectively. For the ceramics sintered in nitrogen, the mechanical properties increased, except for the Vickers hardness, and the values of the above properties were 526.80 MPa, 5.25 MPa·m1/2, 222.10 GPa, and 11.63 GPa, respectively.
基金Project(2007AA03Z0455) supported by the National High Technology Research and Development Program of ChinaProject(BE2010194) supported by Science&Technology Pillar Program of Jiangsu Province, China+1 种基金Project(KF201103) supported by the State Key Laboratory of New Ceramic and Fine Processing, Tsinghua University, ChinaProject supported by the Priority Academic Development of Jiangsu Higher Education Institutions, China
文摘CaO-B203-SiO2 （CBS） glass powders are prepared by conventional glass melting method at different melting temperatures whose properties and microstructures are characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. It is found that there are SiO2 and some unknown phases in CBS glass melting liquid from 1 300 ℃ to 1 500 ℃ and the amount of these phases decreases with the increase of the melting temperature. The CBS glass melted at 1 450 ℃ could be sintered from 830 ℃ to 930 ℃ and the bulk densities of the samples are all higher than 2.4 g/cm^3. From the points of the properties and energy conservation, the melting temperature of 1 450 ℃ is the optimal melting temperature. The glass ceramic sintered at 850 ℃ exhibits better dielectric properties： er=6.33, tan6=2.2×10^-3 at 10 GHz, and the major phases of the samples are CaSiO3, CaB2O4 and SiO2.