The SMM properties of the spatially closed Dy（Ⅲ） double-decker Pc complex Dy（obPc）2 （1）, which is equivalent to a pseudo dinuclear complex, are reported. Complex 1 crystallized with ethanol in the crystal latti...The SMM properties of the spatially closed Dy（Ⅲ） double-decker Pc complex Dy（obPc）2 （1）, which is equivalent to a pseudo dinuclear complex, are reported. Complex 1 crystallized with ethanol in the crystal lattice in the monoclinic space group P22/n and was isomorphous with Tb（obPc）2 （3）, which is arranged in a dimer structure along the b axis. The intermetallic Dy-Dy distance was determined to be 0.756 nm. ZMT versus T plots for 1 decreased with a decrease in T, which suggests the existence of an antiferromagnetic （AF） interaction between the Dy3＋ ions. The M-H curve for 1 at 1.8 K showed magnetic hysteresis. In ac susceptibility measurements on a powder sample of 1, which were dependent on the applied ac field, indicating that 1 is an single molecule magnet （SMM）, a maximum appeared at 22 K at an ac frequency 09 of 1488 Hz. The shape of the peaks dras- tically changed, and the peaks did not shift when an Hd~ large enough to suppress the quantum tunneling of the magnetization （QTM） was applied. The energy barrier （A/hc） was estimated to be 44 cm-1 with a pre-exponential factor （r0） of 1.6 × 10-5 s from an Arrhenius plot. Our results suggest that the SMM/magnetic properties of 1 significantly change in a dc magnetic field. These relaxation mechanisms are related to the energy gap of the ground state and to QTM.展开更多
A single host white emitting phosphor, CaLaGa3O7:Dy3+, was synthesized by chemical co-precipitation. Field emission scanning electron microscopy, X-ray diffraction, laser particle size analysis, and photoluminescence ...A single host white emitting phosphor, CaLaGa3O7:Dy3+, was synthesized by chemical co-precipitation. Field emission scanning electron microscopy, X-ray diffraction, laser particle size analysis, and photoluminescence and cathodoluminescence spectra were used to investigate the structural and optical properties of the phosphor. The phosphor particles were composed of microspheres with a slight tendency to agglomerate, and an average diameter was of about 1.0 μm. The Dy3+ ions acted as luminescent centers, and substituted La3+ ions in the single crystal lattice of CaLaGa3O7 where they were located in Cs sites. Under excitation with ultraviolet light and a low voltage electron beam, the CaLaGa3O7:Dy3+ phosphor exhibited the characteristic emission of Dy3+ (4F9/2-6H15/2 and 4F9/2-6H13/2 transitions) with intense yellow emission at about 573 nm. The chromaticity coordinates for the phosphor were in the white region. The relevant luminescence mechanisms of the phosphor are investigated. This phosphor may be applied in both field emission displays and white light-emitting diodes.展开更多
基金financially supported by a Grant-in-Aid for Scientific Research(s) (20225003) from the Ministry of Education, Culture, Sports,Science, and Technology, Japan
文摘The SMM properties of the spatially closed Dy（Ⅲ） double-decker Pc complex Dy（obPc）2 （1）, which is equivalent to a pseudo dinuclear complex, are reported. Complex 1 crystallized with ethanol in the crystal lattice in the monoclinic space group P22/n and was isomorphous with Tb（obPc）2 （3）, which is arranged in a dimer structure along the b axis. The intermetallic Dy-Dy distance was determined to be 0.756 nm. ZMT versus T plots for 1 decreased with a decrease in T, which suggests the existence of an antiferromagnetic （AF） interaction between the Dy3＋ ions. The M-H curve for 1 at 1.8 K showed magnetic hysteresis. In ac susceptibility measurements on a powder sample of 1, which were dependent on the applied ac field, indicating that 1 is an single molecule magnet （SMM）, a maximum appeared at 22 K at an ac frequency 09 of 1488 Hz. The shape of the peaks dras- tically changed, and the peaks did not shift when an Hd~ large enough to suppress the quantum tunneling of the magnetization （QTM） was applied. The energy barrier （A/hc） was estimated to be 44 cm-1 with a pre-exponential factor （r0） of 1.6 × 10-5 s from an Arrhenius plot. Our results suggest that the SMM/magnetic properties of 1 significantly change in a dc magnetic field. These relaxation mechanisms are related to the energy gap of the ground state and to QTM.
基金supported by the Natural Science Foundation Committee of Inner Mongolia (20080404MS0204)the National High Technology Research and Development Program of China (2008AAXXX0310)the Innovation Fund of Inner Mongolia University of Science and Technology (2010NC026)
文摘A single host white emitting phosphor, CaLaGa3O7:Dy3+, was synthesized by chemical co-precipitation. Field emission scanning electron microscopy, X-ray diffraction, laser particle size analysis, and photoluminescence and cathodoluminescence spectra were used to investigate the structural and optical properties of the phosphor. The phosphor particles were composed of microspheres with a slight tendency to agglomerate, and an average diameter was of about 1.0 μm. The Dy3+ ions acted as luminescent centers, and substituted La3+ ions in the single crystal lattice of CaLaGa3O7 where they were located in Cs sites. Under excitation with ultraviolet light and a low voltage electron beam, the CaLaGa3O7:Dy3+ phosphor exhibited the characteristic emission of Dy3+ (4F9/2-6H15/2 and 4F9/2-6H13/2 transitions) with intense yellow emission at about 573 nm. The chromaticity coordinates for the phosphor were in the white region. The relevant luminescence mechanisms of the phosphor are investigated. This phosphor may be applied in both field emission displays and white light-emitting diodes.