A new design route was presented to fabricate cobalt aluminum-layered double hydroxide(CoAl-LDH)thin layers whichgrow on carbon spheres(CSs)through a growth method.The CoAl-LDH thin layers consist of nanoflakes with a...A new design route was presented to fabricate cobalt aluminum-layered double hydroxide(CoAl-LDH)thin layers whichgrow on carbon spheres(CSs)through a growth method.The CoAl-LDH thin layers consist of nanoflakes with a thickness of20nm.The galvanostatic charge-discharge test of the CoAl-LDH/CSs composite shows a great specific capacitance of1198F/g at1A/g(based on the mass of the CoAl-LDH/CSs composite)in6mol/L KOH solution,and the composite displays an impressive specificcapacitance of920F/g even at a high current density of10A/g.Moreover,the composite remains a specific capacitance of928F/gafter1000cycles at2A/g,and the specific capacitance retention is84%,indicating that the composite has high specific capacitance,excellent rate capability and good cycling stability in comparison to pristine CoAl-LDH.展开更多
基金Project(2022YFB3803300)supported by the National Key Research and Development Program of ChinaProject(52173192)supported by the National Natural Science Foundation of ChinaProject(2023JJ40040)supported by the Natural Science Foundation of Hunan Province,China。
基金Project(21471162) supported by the National Natural Science Foundation of ChinaProject(2015H6016) supported by the Science and Technology Project of Fujian Province,China
文摘A new design route was presented to fabricate cobalt aluminum-layered double hydroxide(CoAl-LDH)thin layers whichgrow on carbon spheres(CSs)through a growth method.The CoAl-LDH thin layers consist of nanoflakes with a thickness of20nm.The galvanostatic charge-discharge test of the CoAl-LDH/CSs composite shows a great specific capacitance of1198F/g at1A/g(based on the mass of the CoAl-LDH/CSs composite)in6mol/L KOH solution,and the composite displays an impressive specificcapacitance of920F/g even at a high current density of10A/g.Moreover,the composite remains a specific capacitance of928F/gafter1000cycles at2A/g,and the specific capacitance retention is84%,indicating that the composite has high specific capacitance,excellent rate capability and good cycling stability in comparison to pristine CoAl-LDH.