TiC-doped NaA1H4 complex hydrides were prepared by hydrogenation of ball-milled Nail/A1 mixture with x TiC powder （x = 0, 5%, 8%, 10%, mole fraction）. The effects of TiC catalyst content on the absorption/desorption...TiC-doped NaA1H4 complex hydrides were prepared by hydrogenation of ball-milled Nail/A1 mixture with x TiC powder （x = 0, 5%, 8%, 10%, mole fraction）. The effects of TiC catalyst content on the absorption/desorption behaviors of the samples were investigated. The results show that TiC can improve the hydriding/dehydriding kinetics of sodium aluminum hydride, the hydriding rate of the sample increases with increasing TiC content. It is found that the TiC-doped NaA1H4 composites have a relatively good cyclic stability. The composite doped with 10% TiC maintains steadily about 4.5% （mass fraction） hydrogen absorption capacity as against about 3.8% （mass fraction） hydrogen desorption capacity over 8 cycles. The particle sizes of the TiC-doped NaA1H4 composites can be reduced to 50-100 nm, which may play an important role in improving the hydriding/dehydriding kinetics.展开更多
基金Project(2010CB631300)supported by the National Basic Research Program of ChinaProjects(50871099,51001090)supported by the National Natural Science Foundation of China+1 种基金Projects(20080440196,200902622)supported by the China Postdoctoral Science FoundationProject(20090101110050)supported by the University Doctoral Foundation of the Ministry of Education,China
文摘TiC-doped NaA1H4 complex hydrides were prepared by hydrogenation of ball-milled Nail/A1 mixture with x TiC powder （x = 0, 5%, 8%, 10%, mole fraction）. The effects of TiC catalyst content on the absorption/desorption behaviors of the samples were investigated. The results show that TiC can improve the hydriding/dehydriding kinetics of sodium aluminum hydride, the hydriding rate of the sample increases with increasing TiC content. It is found that the TiC-doped NaA1H4 composites have a relatively good cyclic stability. The composite doped with 10% TiC maintains steadily about 4.5% （mass fraction） hydrogen absorption capacity as against about 3.8% （mass fraction） hydrogen desorption capacity over 8 cycles. The particle sizes of the TiC-doped NaA1H4 composites can be reduced to 50-100 nm, which may play an important role in improving the hydriding/dehydriding kinetics.