The N,S co-doped porous carbon nanofibers were fabricated by the carbonization of[Zn_(2)(tdc)_(2)(MA)]n MOFs/polyacrylonitrile nanofibers composite,which was produced by the electrospinning technology.The electrochemi...The N,S co-doped porous carbon nanofibers were fabricated by the carbonization of[Zn_(2)(tdc)_(2)(MA)]n MOFs/polyacrylonitrile nanofibers composite,which was produced by the electrospinning technology.The electrochemical results show that the N,S co-doped porous carbon nanofibers can achieve capacity of 201.2 mAh·g^(-1)at the current density of 0.05 A·g^(-1).Furthermore,the reversible capacity still has 161.3 mAh·g^(-1)even at a high current density of 1 A·g^(-1)after 600 cycles.The superior electrochemical performance shows that the N,S co-doped porous carbon nanofibers electrode material can be used as an ideal anode material for sodium-ion batteries.展开更多
Proton exchange membrane fuel cells suffer from the sluggish kinetics of the oxygen reduction reaction(ORR)and the high cost of Pt catalysts.In the present work,a high‐performance ORR catalystbased on Fe,N,S‐doped p...Proton exchange membrane fuel cells suffer from the sluggish kinetics of the oxygen reduction reaction(ORR)and the high cost of Pt catalysts.In the present work,a high‐performance ORR catalystbased on Fe,N,S‐doped porous carbon(FeNS‐PC)was synthesized using melamine formaldehyderesin as C and N precursors,Fe(SCN)3as Fe and S precursors,and CaCl2as a template via a two‐stepheat treatment without a harsh template removal step.The results show that the catalyst treated at900℃(FeNS‐PC‐900)had a high surface area of775m2/g,a high mass activity of10.2A/g in anacidic medium,and excellent durability;the half‐wave potential decreased by only20mV after10000potential cycles.The FeNS‐PC‐900catalyst was used as the cathode in a proton exchangemembrane fuel cell and delivered a peak power density of0.49W/cm2.FeNS‐PC‐900therefore hasgood potential for use in practical applications.展开更多
文摘The N,S co-doped porous carbon nanofibers were fabricated by the carbonization of[Zn_(2)(tdc)_(2)(MA)]n MOFs/polyacrylonitrile nanofibers composite,which was produced by the electrospinning technology.The electrochemical results show that the N,S co-doped porous carbon nanofibers can achieve capacity of 201.2 mAh·g^(-1)at the current density of 0.05 A·g^(-1).Furthermore,the reversible capacity still has 161.3 mAh·g^(-1)even at a high current density of 1 A·g^(-1)after 600 cycles.The superior electrochemical performance shows that the N,S co-doped porous carbon nanofibers electrode material can be used as an ideal anode material for sodium-ion batteries.
基金supported by the National Basic Research Program of China (973 Program,2015CB932303)the National Natural Science Founda-tion of China (21373175,21621091)~~
文摘Proton exchange membrane fuel cells suffer from the sluggish kinetics of the oxygen reduction reaction(ORR)and the high cost of Pt catalysts.In the present work,a high‐performance ORR catalystbased on Fe,N,S‐doped porous carbon(FeNS‐PC)was synthesized using melamine formaldehyderesin as C and N precursors,Fe(SCN)3as Fe and S precursors,and CaCl2as a template via a two‐stepheat treatment without a harsh template removal step.The results show that the catalyst treated at900℃(FeNS‐PC‐900)had a high surface area of775m2/g,a high mass activity of10.2A/g in anacidic medium,and excellent durability;the half‐wave potential decreased by only20mV after10000potential cycles.The FeNS‐PC‐900catalyst was used as the cathode in a proton exchangemembrane fuel cell and delivered a peak power density of0.49W/cm2.FeNS‐PC‐900therefore hasgood potential for use in practical applications.