连铸过程结晶器内的保护渣卷入造成的非金属夹杂物尺寸大、靠近铸坯表面,成为轿车面板等高品质冷轧薄板的主要表面缺陷。本文对鞍钢三炼钢厂生产的 IF 钢连铸板坯表面夹渣缺陷的分布、形态及成分进行研究,观察到表面夹渣存在的两种形式...连铸过程结晶器内的保护渣卷入造成的非金属夹杂物尺寸大、靠近铸坯表面,成为轿车面板等高品质冷轧薄板的主要表面缺陷。本文对鞍钢三炼钢厂生产的 IF 钢连铸板坯表面夹渣缺陷的分布、形态及成分进行研究,观察到表面夹渣存在的两种形式。探讨了贯通型表面夹渣的形成机理,并提出减少表面夹渣的措施。展开更多
Deformation behavior of slab at the straightening stage during continuous casting was simulated by the explicit dynamic finite element method,and the stress distribution along the width direction of the slab and its c...Deformation behavior of slab at the straightening stage during continuous casting was simulated by the explicit dynamic finite element method,and the stress distribution along the width direction of the slab and its change regularity at slab center during continuous casting were obtained.The influence of distribution and change of stress on the propagation of longitudinal cracks on slab surface was discussed.The results show that the tensional stress appears on slab surface at the inner arc side and the compressive stress appears on slab surface at the outer arc side at stages 6-8 in straightening zone during continuous casting.Longitudinal cracks generally appear on slab top surface and do not appear on slab bottom surface,which are also observed in industry.展开更多
基金Project(50634030) supported by the National Natural Science Foundation of ChinaProject(20090042120005) supported by the Doctorate Foundation of the Ministry of Education of ChinaProject(2006CB605208-1) supported by the State Basic Research Program of China
文摘Deformation behavior of slab at the straightening stage during continuous casting was simulated by the explicit dynamic finite element method,and the stress distribution along the width direction of the slab and its change regularity at slab center during continuous casting were obtained.The influence of distribution and change of stress on the propagation of longitudinal cracks on slab surface was discussed.The results show that the tensional stress appears on slab surface at the inner arc side and the compressive stress appears on slab surface at the outer arc side at stages 6-8 in straightening zone during continuous casting.Longitudinal cracks generally appear on slab top surface and do not appear on slab bottom surface,which are also observed in industry.