Mg-Gd-Y-Zr alloys were purified by filtering purification with and without vacuum. The type, morphology, size distribution and volume fraction of inclusion were analyzed with OM and SEM. The effect of inclusion in Mg-...Mg-Gd-Y-Zr alloys were purified by filtering purification with and without vacuum. The type, morphology, size distribution and volume fraction of inclusion were analyzed with OM and SEM. The effect of inclusion in Mg-Gd-Y-Zr alloys on anticorrosion ability was investigated with salt spray test and electrochemical test. The results show that the inclusions in the alloy can be removed effectively by filtering purification. The average size of inclusions in the alloys is decreased from 12.7 μm to 2.0 μm and the volume fraction of inclusions is reduced from 0.30% to 0.04%. With the decrease of the size of inclusions in the alloys, the corrosion rate of the alloys decreases dramatically from 38.8 g/（m 2 ·d） to 2.4 g/（m 2 ·d） in the salt spray test. The corrosion potential increases while the corrosion current decreases and the polarization resistance increases in the electrochemical tests, which indicates that the anticorrosion ability is improved.展开更多
Mg-Gd-Y-Zr alloy was purified by the method of filtering purification. The type, morphology, size distribution and volume fraction of inclusions in the alloy were analyzed using optical microscope and scanning electro...Mg-Gd-Y-Zr alloy was purified by the method of filtering purification. The type, morphology, size distribution and volume fraction of inclusions in the alloy were analyzed using optical microscope and scanning electron microscope, and the effects of the inclusions on the mechanical and corrosion properties of the alloy were investigated. The results indicate that the filtering purification method is effective to remove inclusions in the alloy. By the filtering purification method, the average size of inclusions in the alloy reduces from 12.7 μm to 4.3 μm and the average volume fraction of inclusions in the alloy reduces from 0.26% to 0.06%. The ultimate tensile strength, yield strength and elongation of the alloy are improved from 200 MPa, 156 MPa and 3.4% to 232 MPa, 167 MPa and 7.0%, respectively. The corrosion rate of the alloy decreases dramatically from 38.8g/（mLd） to 2.5 g/（mZ.d） in the salt spray test.展开更多
基金Project(2007CB613700)supported by the National Basic Research Program of China
文摘Mg-Gd-Y-Zr alloys were purified by filtering purification with and without vacuum. The type, morphology, size distribution and volume fraction of inclusion were analyzed with OM and SEM. The effect of inclusion in Mg-Gd-Y-Zr alloys on anticorrosion ability was investigated with salt spray test and electrochemical test. The results show that the inclusions in the alloy can be removed effectively by filtering purification. The average size of inclusions in the alloys is decreased from 12.7 μm to 2.0 μm and the volume fraction of inclusions is reduced from 0.30% to 0.04%. With the decrease of the size of inclusions in the alloys, the corrosion rate of the alloys decreases dramatically from 38.8 g/（m 2 ·d） to 2.4 g/（m 2 ·d） in the salt spray test. The corrosion potential increases while the corrosion current decreases and the polarization resistance increases in the electrochemical tests, which indicates that the anticorrosion ability is improved.
基金Project(2007CB613705)supported by the National Basic Research Program of China
文摘Mg-Gd-Y-Zr alloy was purified by the method of filtering purification. The type, morphology, size distribution and volume fraction of inclusions in the alloy were analyzed using optical microscope and scanning electron microscope, and the effects of the inclusions on the mechanical and corrosion properties of the alloy were investigated. The results indicate that the filtering purification method is effective to remove inclusions in the alloy. By the filtering purification method, the average size of inclusions in the alloy reduces from 12.7 μm to 4.3 μm and the average volume fraction of inclusions in the alloy reduces from 0.26% to 0.06%. The ultimate tensile strength, yield strength and elongation of the alloy are improved from 200 MPa, 156 MPa and 3.4% to 232 MPa, 167 MPa and 7.0%, respectively. The corrosion rate of the alloy decreases dramatically from 38.8g/（mLd） to 2.5 g/（mZ.d） in the salt spray test.