2017 aluminum alloy plates with an ultrafine grained （UFG） structure were produced by equal channel angular processing （ECAP） and then were joined by underwater friction stir welding （underwater FSW）. X-ray diff...2017 aluminum alloy plates with an ultrafine grained （UFG） structure were produced by equal channel angular processing （ECAP） and then were joined by underwater friction stir welding （underwater FSW）. X-ray diffractometer （XRD）, transmission electron microscope （TEM）, scanning electron microscope （SEM） and microhardness tester were adopted to investigate the microstructural and mechanical characteristics of the FSW joint. The results indicate that an ultrafine grained microstructure with the mean grain size of-0.7 Ixm is obtained in the weld nugget by using water cooling. However, The FSW joint exhibits softening compared with the ultrafine grained based material and the heat affected zone （HAZ） has the lowest hardness owing to the coarsening of the strengthening precipitates.展开更多
Ultrafine-grained(UFG) hypereutectic Al-23%Si (mass fraction) alloy was achieved through equal-channel angular pressing(EACP) procedure. And the electrochemical properties after various ECAP passes were investigated i...Ultrafine-grained(UFG) hypereutectic Al-23%Si (mass fraction) alloy was achieved through equal-channel angular pressing(EACP) procedure. And the electrochemical properties after various ECAP passes were investigated in neutral NaCl solution. Potentiostatic polarization curves show that the corrosion potential of the ECAPed sample after 4 passes decreases markedly, while the corrosion current density reaches 1.37 times that of the as-cast alloy. However, the φcorr and Jcorr values after 16 passes are improved and approach those of the as-cast alloy. Immersion tests also show that the mass-loss ratio of ECAPed alloy decreases with increasing the pressing pass, which is lowered to 28.7% with the increase of pass number from 4 to 16. Pitting susceptibility of the ECAPed alloy after initial 4 passes is boosted, due to the presence of biggish voids resulted from the breakage of brittle large primary silicon crystals during ECAP. Increasing ECAP pass makes the voids evanesce and results in the homogeneous ultrafine-grained structure, contributing to a higher pitting resistance. These results indicate that enough ECAP passes are beneficial to increasing corrosion resistance of the hypereutectic Al-23%Si alloy.展开更多
基金Projects(50774059, 51074119) supported by the National Natural Science Foundation of China
文摘2017 aluminum alloy plates with an ultrafine grained （UFG） structure were produced by equal channel angular processing （ECAP） and then were joined by underwater friction stir welding （underwater FSW）. X-ray diffractometer （XRD）, transmission electron microscope （TEM）, scanning electron microscope （SEM） and microhardness tester were adopted to investigate the microstructural and mechanical characteristics of the FSW joint. The results indicate that an ultrafine grained microstructure with the mean grain size of-0.7 Ixm is obtained in the weld nugget by using water cooling. However, The FSW joint exhibits softening compared with the ultrafine grained based material and the heat affected zone （HAZ） has the lowest hardness owing to the coarsening of the strengthening precipitates.
基金Project supported by the Japanese Society for the Promotion of Science Project supported by Qing Lan Program (Jiangsu, China)
文摘Ultrafine-grained(UFG) hypereutectic Al-23%Si (mass fraction) alloy was achieved through equal-channel angular pressing(EACP) procedure. And the electrochemical properties after various ECAP passes were investigated in neutral NaCl solution. Potentiostatic polarization curves show that the corrosion potential of the ECAPed sample after 4 passes decreases markedly, while the corrosion current density reaches 1.37 times that of the as-cast alloy. However, the φcorr and Jcorr values after 16 passes are improved and approach those of the as-cast alloy. Immersion tests also show that the mass-loss ratio of ECAPed alloy decreases with increasing the pressing pass, which is lowered to 28.7% with the increase of pass number from 4 to 16. Pitting susceptibility of the ECAPed alloy after initial 4 passes is boosted, due to the presence of biggish voids resulted from the breakage of brittle large primary silicon crystals during ECAP. Increasing ECAP pass makes the voids evanesce and results in the homogeneous ultrafine-grained structure, contributing to a higher pitting resistance. These results indicate that enough ECAP passes are beneficial to increasing corrosion resistance of the hypereutectic Al-23%Si alloy.
基金finacially supported by National Natural Science Foundation of China(51404077)Guangdong Province Natural Science Foundation(2015A030313775)+2 种基金Guangzhou International Science&Technology Cooperation Program(201508030032)Guangdong Academy of Sciences Project(2017GDASCX-0117)Guangzhou Science and Technology Planning Project(ZWY201704003)