Such characteristics of aluminium strip and foil as soft and thin gauge make tension control one of the key techniques for automation gauge control(AGC). To avoid the disadvantage of traditional mathematical control m...Such characteristics of aluminium strip and foil as soft and thin gauge make tension control one of the key techniques for automation gauge control(AGC). To avoid the disadvantage of traditional mathematical control method which is unfitful for nonlinear hysteresis, the technique for tension AGC fuzzy control was developed and thickness deviation more than 3% of product thickness was achieved consequently in 1 350 mm cold rolling mill of aluminium strip and foil. Additionally, because the gauge of aluminium strip and foil is thin, stage-cooling roll method becomes a key technique for profile control. So stage-cooling roll intelligent control method is developed and pre-coated aluminum foil with good profile less than 10 I (the relative differences in elongation of 0.01%) is produced using the profile control system in 1 400 mm cold rolling mill of aluminium strip and foil.展开更多
Nanocrystalline Mg2Ni-type alloys with nominal compositions of Mg20Ni10–xCux(x=0,1,2,3,4,mass fraction,%) were synthesized by rapid quenching technique.The microstructures of the as-cast and quenched alloys were char...Nanocrystalline Mg2Ni-type alloys with nominal compositions of Mg20Ni10–xCux(x=0,1,2,3,4,mass fraction,%) were synthesized by rapid quenching technique.The microstructures of the as-cast and quenched alloys were characterized by XRD,SEM and HRTEM.The electrochemical hydrogen storage performances were tested by an automatic galvanostatic system.The hydriding and dehydriding kinetics of the alloys were measured using an automatically controlled Sieverts apparatus.The results show that all the as-quenched alloys hold the typical nanocrystalline structure and the rapid quenching does not change the major phase Mg2Ni.The rapid quenching significantly improves the electrochemical hydrogen storage capacity of the alloys,whereas it slightly impairs the cycling stability of the alloys.Additionally,the hydrogen absorption and desorption capacities of the alloys significantly increase with rising quenching rate.展开更多
文摘Such characteristics of aluminium strip and foil as soft and thin gauge make tension control one of the key techniques for automation gauge control(AGC). To avoid the disadvantage of traditional mathematical control method which is unfitful for nonlinear hysteresis, the technique for tension AGC fuzzy control was developed and thickness deviation more than 3% of product thickness was achieved consequently in 1 350 mm cold rolling mill of aluminium strip and foil. Additionally, because the gauge of aluminium strip and foil is thin, stage-cooling roll method becomes a key technique for profile control. So stage-cooling roll intelligent control method is developed and pre-coated aluminum foil with good profile less than 10 I (the relative differences in elongation of 0.01%) is produced using the profile control system in 1 400 mm cold rolling mill of aluminium strip and foil.
基金Project(2007AA03Z227) supported by High-tech Research and Development Program of ChinaProjects(50871050,50701011) supported by the National Natural Science Foundation of China+1 种基金Project(200711020703) supported by the Natural Science Foundation of Inner Mongolia,ChinaProject(NJzy08071) supported by High Education Science Research Project of Inner Mongolia,China
文摘Nanocrystalline Mg2Ni-type alloys with nominal compositions of Mg20Ni10–xCux(x=0,1,2,3,4,mass fraction,%) were synthesized by rapid quenching technique.The microstructures of the as-cast and quenched alloys were characterized by XRD,SEM and HRTEM.The electrochemical hydrogen storage performances were tested by an automatic galvanostatic system.The hydriding and dehydriding kinetics of the alloys were measured using an automatically controlled Sieverts apparatus.The results show that all the as-quenched alloys hold the typical nanocrystalline structure and the rapid quenching does not change the major phase Mg2Ni.The rapid quenching significantly improves the electrochemical hydrogen storage capacity of the alloys,whereas it slightly impairs the cycling stability of the alloys.Additionally,the hydrogen absorption and desorption capacities of the alloys significantly increase with rising quenching rate.
