Ceramic coating was deposited on TiAl alloy substrate by micro-arc oxidation(MAO)in a silicate-aluminate electrolyte solution with additives including sodium citrate,graphite and sodium tungstate.The microstructures a...Ceramic coating was deposited on TiAl alloy substrate by micro-arc oxidation(MAO)in a silicate-aluminate electrolyte solution with additives including sodium citrate,graphite and sodium tungstate.The microstructures and compositions were analyzed by SEM,EDX and XRD.The corrosion and wear properties of the coatings were investigated by potentiodynamic polarization and ball-on-disc wear test,respectively.The results show that the MAO coatings consist of WO3,Ti2O3,graphite and Al2O3 besides Al2TiO5 and Al2SiO5.With additives in the electrolyte,the working voltage at the micro-arc discharge stage decreases,and the ceramic coating gets smoother and more compact.The corrosion current density of MAO coating is much lower than that of TiAl substrate.It can be reduced from 9.81×10-8A/cm 2to 3.02×10-10A/cm 2 .The MAO coatings composed of hard Al2O3,WO3 and Ti2O3 obviously improve the wear resistance of TiAl alloy.The wear rate is-3.27×10-7g/(N·m).展开更多
A theoretical study was carried out into membrane transport phenomena.Formulae for calculating the membrane transport resistance and transmembrane mass flux were given,variations in membrane resistance and moisture fl...A theoretical study was carried out into membrane transport phenomena.Formulae for calculating the membrane transport resistance and transmembrane mass flux were given,variations in membrane resistance and moisture flux with the membrane sorption constant(C)under various humidity conditions were analyzed,and the value of C corresponding to the minimum membrane resistance or the maximum moisture flux was obtained.The results show that the membrane resistance and moisture flux relate not only to C but also to the relative humidities on both sides of the membrane.As C increases,membrane resistance initially decreases but then increases,i.e.,a minimum occurs,while the moisture flux first decreases and then increases,i.e.,a maximum occurs.The membrane resistance and moisture flux reach their extrema at the same value of C,which is determined by the relative humidities on both sides of the membrane.To reduce the membrane resistance,the value of C should be chosen based on the humidity conditions.展开更多
基金Project(2006KG03) supported by the Science and Technology Program of Shannxi Province, China
文摘Ceramic coating was deposited on TiAl alloy substrate by micro-arc oxidation(MAO)in a silicate-aluminate electrolyte solution with additives including sodium citrate,graphite and sodium tungstate.The microstructures and compositions were analyzed by SEM,EDX and XRD.The corrosion and wear properties of the coatings were investigated by potentiodynamic polarization and ball-on-disc wear test,respectively.The results show that the MAO coatings consist of WO3,Ti2O3,graphite and Al2O3 besides Al2TiO5 and Al2SiO5.With additives in the electrolyte,the working voltage at the micro-arc discharge stage decreases,and the ceramic coating gets smoother and more compact.The corrosion current density of MAO coating is much lower than that of TiAl substrate.It can be reduced from 9.81×10-8A/cm 2to 3.02×10-10A/cm 2 .The MAO coatings composed of hard Al2O3,WO3 and Ti2O3 obviously improve the wear resistance of TiAl alloy.The wear rate is-3.27×10-7g/(N·m).
基金supported by the National Natural Science Foundation of China(50576040)
文摘A theoretical study was carried out into membrane transport phenomena.Formulae for calculating the membrane transport resistance and transmembrane mass flux were given,variations in membrane resistance and moisture flux with the membrane sorption constant(C)under various humidity conditions were analyzed,and the value of C corresponding to the minimum membrane resistance or the maximum moisture flux was obtained.The results show that the membrane resistance and moisture flux relate not only to C but also to the relative humidities on both sides of the membrane.As C increases,membrane resistance initially decreases but then increases,i.e.,a minimum occurs,while the moisture flux first decreases and then increases,i.e.,a maximum occurs.The membrane resistance and moisture flux reach their extrema at the same value of C,which is determined by the relative humidities on both sides of the membrane.To reduce the membrane resistance,the value of C should be chosen based on the humidity conditions.
