Reduction of Bama ilmenite concentrate containing 49.78% TiO2 and 27.96% total Fe by graphite was studied using thermogravimetric analysis system under argon gas ambient from 850 to 1 400 ℃. The reduction degree of B...Reduction of Bama ilmenite concentrate containing 49.78% TiO2 and 27.96% total Fe by graphite was studied using thermogravimetric analysis system under argon gas ambient from 850 to 1 400 ℃. The reduction degree of Bama ilmenite is enhanced with increasing temperature and the molar ratio of carbon to oxygen, and the reaction rate varies with temperature and reduction time simultaneously. The phase transformation, chemical composition, microstructure and morphology of reduced samples were investigated by using X-ray diffractometry, scanning electron microscopy, and energy disperse spectroscopy, respectively. The high content of impurities in Bama ilmenite evidently bates the reduction of ilmenite. Forming the enrichment zone of manganese prevents complete reduction of Fe2+. The reduction products are mostly reduced iron, rutile, reduced rutiles, Ti3O5 and pseudobrookite solid solution. The reduction kinetics was also discussed. The results show that the reduction temperature is a key factor to control reaction rate.展开更多
文摘Reduction of Bama ilmenite concentrate containing 49.78% TiO2 and 27.96% total Fe by graphite was studied using thermogravimetric analysis system under argon gas ambient from 850 to 1 400 ℃. The reduction degree of Bama ilmenite is enhanced with increasing temperature and the molar ratio of carbon to oxygen, and the reaction rate varies with temperature and reduction time simultaneously. The phase transformation, chemical composition, microstructure and morphology of reduced samples were investigated by using X-ray diffractometry, scanning electron microscopy, and energy disperse spectroscopy, respectively. The high content of impurities in Bama ilmenite evidently bates the reduction of ilmenite. Forming the enrichment zone of manganese prevents complete reduction of Fe2+. The reduction products are mostly reduced iron, rutile, reduced rutiles, Ti3O5 and pseudobrookite solid solution. The reduction kinetics was also discussed. The results show that the reduction temperature is a key factor to control reaction rate.