A S 2O 2- 8/ZrO 2 Al 2O 3 type solid superacid catalyst was prepared from ZrOCl 2·8H 2O, AlCl 3· 6H 2O and (NH 4) 2S 2O 8 by coprecipitation, maceration and calcination processes. Their crystal structures an...A S 2O 2- 8/ZrO 2 Al 2O 3 type solid superacid catalyst was prepared from ZrOCl 2·8H 2O, AlCl 3· 6H 2O and (NH 4) 2S 2O 8 by coprecipitation, maceration and calcination processes. Their crystal structures and acidities were determined by XRD and Hammett method, respectively. The activity of the catalyst was studied as function of Al 2O 3 content, calcination temperature and time in the esterification of acetic acid with butanol, and a conversion of 96 5% was obtained. The catalyst gave also higher yields in syntheses of ketals and acetals: cyclohexanone ethylene ketal(86 2%), acetophenone ethylene ketal(78 5%), acetylacetic ester ketal(88 5%), benzaldehyde glycol acetal(76 3%). The chemical structures of the products were confirmed by IR spectra.展开更多
The new nanosolid superacid catalyst SO42-/TiO2 is compounded with nanometer chemical technology. This catalyst SO42-/TiO2 has good catalytic effects on esterificational reactions of ethylic acid and ethyl alcohol. It...The new nanosolid superacid catalyst SO42-/TiO2 is compounded with nanometer chemical technology. This catalyst SO42-/TiO2 has good catalytic effects on esterificational reactions of ethylic acid and ethyl alcohol. It has many other advantages such as strong water proof quality, being able to be used repeatedly, being easy to be reclaimed, non corroding, non polluting. So it is a green industrial catalyst which is helpful to the environment and possesses wide prospect of applications. The crystallo process, specific surface area and sulphur content of the SO42-/TiO2 system have been studied with the method of XRD, XPS and the chemical analysis, the result of which indicates that catalytic activity and acid strength of SO42-/TiO2 is affected by the H2SO4 saturant concentration, baking temperature, precipitating condition, specific surface area and sulphur content. The best preparation conditions of SO42-/TiO2 are: ageing temperature at 0℃, 0.5mol·L-1 of H2SO4 concentration, baking temperature at 500℃and 3 hours of baking time.展开更多
文摘A S 2O 2- 8/ZrO 2 Al 2O 3 type solid superacid catalyst was prepared from ZrOCl 2·8H 2O, AlCl 3· 6H 2O and (NH 4) 2S 2O 8 by coprecipitation, maceration and calcination processes. Their crystal structures and acidities were determined by XRD and Hammett method, respectively. The activity of the catalyst was studied as function of Al 2O 3 content, calcination temperature and time in the esterification of acetic acid with butanol, and a conversion of 96 5% was obtained. The catalyst gave also higher yields in syntheses of ketals and acetals: cyclohexanone ethylene ketal(86 2%), acetophenone ethylene ketal(78 5%), acetylacetic ester ketal(88 5%), benzaldehyde glycol acetal(76 3%). The chemical structures of the products were confirmed by IR spectra.
文摘The new nanosolid superacid catalyst SO42-/TiO2 is compounded with nanometer chemical technology. This catalyst SO42-/TiO2 has good catalytic effects on esterificational reactions of ethylic acid and ethyl alcohol. It has many other advantages such as strong water proof quality, being able to be used repeatedly, being easy to be reclaimed, non corroding, non polluting. So it is a green industrial catalyst which is helpful to the environment and possesses wide prospect of applications. The crystallo process, specific surface area and sulphur content of the SO42-/TiO2 system have been studied with the method of XRD, XPS and the chemical analysis, the result of which indicates that catalytic activity and acid strength of SO42-/TiO2 is affected by the H2SO4 saturant concentration, baking temperature, precipitating condition, specific surface area and sulphur content. The best preparation conditions of SO42-/TiO2 are: ageing temperature at 0℃, 0.5mol·L-1 of H2SO4 concentration, baking temperature at 500℃and 3 hours of baking time.