The arsenic extraction from the arsenic-containing cobalt and nickel slag,which came from the purification process of zinc sulfate solution in a zinc smelting factory,was investigated.The alkaline leaching method was ...The arsenic extraction from the arsenic-containing cobalt and nickel slag,which came from the purification process of zinc sulfate solution in a zinc smelting factory,was investigated.The alkaline leaching method was proposed according to the mode of occurrence of arsenic in the slag and its amphoteric characteristic.The leaching experiments were conducted in the alkaline aqueous medium,with bubbling of oxygen into the solution,and the optimal conditions for leaching arsenic were determined.The results showed that the extraction rate of arsenic was maximized at 99.10%under the optimal conditions of temperature 140 ℃,NaOH concentration 150 g/L,oxygen partial pressure 0.5 MPa,and a liquid-to-solid ratio 5：1.Based on the solubilities of As2O5,ZnO and PbO in NaOH solution at 25 ℃,a method for the separation of As in the form of sodium arsenate salt from the arsenic-rich leachate via cooling crystallization was established,and the reaction medium could be fully recycled.The crystallization rate was confirmed to reach 88.9%（calculated on the basis of Na3AsO4） upon a direct cooling of the hot leachate down to room temperature.On the basis of redox potentials,the sodium arsenate solution could be further reduced by sulfur dioxide（SO2） gas to arsenite,at a reduction yield of 92%under the suitable conditions.Arsenic trioxide with regular octahedron shape could be prepared successfully from the reduced solution,and further recycled to the purification process to purify the zinc sulfate solution.Also,sodium arsenite solution obtained after the reduction of arsenate could be directly used to purify the zinc sulfate solution.Therefore,the technical scheme of alkaline leaching with pressured oxygen,cooling crystallization,arsenate reduction by SO2 gas,and arsenic trioxide preparation,provides an attractive approach to realize the resource utilization of arsenic-containing cobalt and nickel slag.展开更多
The interaction mechanism between sodium arsenate and fayalite-type copper slag at 1200℃was investigated through XRD,XPS,HRTEM,TCLP and other technical means and methods.The results indicated that the proportions of ...The interaction mechanism between sodium arsenate and fayalite-type copper slag at 1200℃was investigated through XRD,XPS,HRTEM,TCLP and other technical means and methods.The results indicated that the proportions of sodium arsenate in the slag and flue gas phases were approximately 30%and 70%,respectively.The addition of sodium arsenate depolymerized the fayalite structure and changed it from a crystalline state to an amorphous state.The fayalite structural changes indicated that the[AsO_(4)]tetrahedron in sodium arsenate combined with the[SiO_(4)]tetrahedron and[FeO_(4)]tetrahedron through bridging oxygen to form a silicate glass structure.The TCLP test results of the samples before and after the high temperature reaction of fayalite and sodium arsenate showed that after high temperature reaction,fayalite could effectively reduce the leaching toxicity of sodium arsenate,reducing the leaching concentration of arsenic from 3025.52 to 12.8 mg/L before and after reaction,respectively.展开更多
基金Project (2012BAC12B01) supported by the National Key Technologies R&D Program of ChinaProject (2012FJ1010) supported by Science and Technology Major Project of Hunan Province,China
文摘The arsenic extraction from the arsenic-containing cobalt and nickel slag,which came from the purification process of zinc sulfate solution in a zinc smelting factory,was investigated.The alkaline leaching method was proposed according to the mode of occurrence of arsenic in the slag and its amphoteric characteristic.The leaching experiments were conducted in the alkaline aqueous medium,with bubbling of oxygen into the solution,and the optimal conditions for leaching arsenic were determined.The results showed that the extraction rate of arsenic was maximized at 99.10%under the optimal conditions of temperature 140 ℃,NaOH concentration 150 g/L,oxygen partial pressure 0.5 MPa,and a liquid-to-solid ratio 5：1.Based on the solubilities of As2O5,ZnO and PbO in NaOH solution at 25 ℃,a method for the separation of As in the form of sodium arsenate salt from the arsenic-rich leachate via cooling crystallization was established,and the reaction medium could be fully recycled.The crystallization rate was confirmed to reach 88.9%（calculated on the basis of Na3AsO4） upon a direct cooling of the hot leachate down to room temperature.On the basis of redox potentials,the sodium arsenate solution could be further reduced by sulfur dioxide（SO2） gas to arsenite,at a reduction yield of 92%under the suitable conditions.Arsenic trioxide with regular octahedron shape could be prepared successfully from the reduced solution,and further recycled to the purification process to purify the zinc sulfate solution.Also,sodium arsenite solution obtained after the reduction of arsenate could be directly used to purify the zinc sulfate solution.Therefore,the technical scheme of alkaline leaching with pressured oxygen,cooling crystallization,arsenate reduction by SO2 gas,and arsenic trioxide preparation,provides an attractive approach to realize the resource utilization of arsenic-containing cobalt and nickel slag.
文摘探索了以砷酸钠形式回收高砷烟尘碱性浸出液中砷的新工艺,分别进行了直接结晶与氧化结晶实验研究。结果表明,采用双氧水氧化结晶效果明显优于直接结晶效果,在氧化温度30℃、结晶温度30℃、H2O2/As摩尔比0.8、结晶时间2 h、双氧水加入速度0.4 m L/min的优化工艺条件下,砷锑结晶率分别达90%和98%以上。结晶粗产品经溶解、过滤不溶物、蒸发结晶,得到纯化后的砷酸钠(Na3As O4·10H2O)产品,纯度为95.85%。
基金the financial supports from the National Natural Science Foundation of China(No.51634010)National Key R&D Program of China(No.2018YFC1900300).
文摘The interaction mechanism between sodium arsenate and fayalite-type copper slag at 1200℃was investigated through XRD,XPS,HRTEM,TCLP and other technical means and methods.The results indicated that the proportions of sodium arsenate in the slag and flue gas phases were approximately 30%and 70%,respectively.The addition of sodium arsenate depolymerized the fayalite structure and changed it from a crystalline state to an amorphous state.The fayalite structural changes indicated that the[AsO_(4)]tetrahedron in sodium arsenate combined with the[SiO_(4)]tetrahedron and[FeO_(4)]tetrahedron through bridging oxygen to form a silicate glass structure.The TCLP test results of the samples before and after the high temperature reaction of fayalite and sodium arsenate showed that after high temperature reaction,fayalite could effectively reduce the leaching toxicity of sodium arsenate,reducing the leaching concentration of arsenic from 3025.52 to 12.8 mg/L before and after reaction,respectively.
基金This study was supported by the Bureau of Traditional Chinese Medicine of Guizhou Province(QZYY2010)Science and Technology Foundation of Guizhou Province(TZJF2009-41and 2010-5)