The fabrication of a pyrocarbon coated carbon paper and its application to the gas diffusion lay(GDL) of proton exchange membrane(PEM) fuel cell were described.This carbon paper was fabricated by using conventional ca...The fabrication of a pyrocarbon coated carbon paper and its application to the gas diffusion lay(GDL) of proton exchange membrane(PEM) fuel cell were described.This carbon paper was fabricated by using conventional carbon paper as the precursor,and coating it with pyrocarbon by pyrolyzing propylene via the chemical vapor deposition(CVD) method.For comparison,conventional carbon paper composites were also prepared by using PAN-based carbon fiber felt as the precursor followed by impregnation with resin,molding and heat-treatment.SEM characterization indicates that pyrocarbon is uniformly deposited on the surface of the fiber in the pyrocarbon coated carbon paper and made the fibers of carbon felt bind more tightly.In contrast,there are cracks in matrix and debonding of fibers due to carbonization shrinkage in the conventional carbon paper.Property measurements show that the former has much better conductivity and gas permeability than the latter.In addition,current density-voltage performance tests also reveal that the pyrocarbon coating can improve the properties of carbon paper used for electrode materials of fuel cell.展开更多
The pyrolytic carbon （PyC） coatings were fabricated on A1203 fiber fabrics by the method of chemical vapor deposition （CVD）. The microstructures of A1203 fibers with and without PyC coatings were characterized by ...The pyrolytic carbon （PyC） coatings were fabricated on A1203 fiber fabrics by the method of chemical vapor deposition （CVD）. The microstructures of A1203 fibers with and without PyC coatings were characterized by SEM and Raman spectroscopy. The influence of deposition time of PyC on the DC conductivity （ad） of A1203 filaments and complex permittivity of fabrics at X band （8.2-12.4 GHz） were investigated. The values of Crd and complex permittivity increase with increasing deposition time of PyC. The electron relaxation polarization and conductance loss were supposed to be contributed to the increase of ε＇ and ε＂, respectively. In addition, the reflection loss （RL） of fabrics was calculated. The results show that the microwave absorbing properties of Al2O3 fiber fabrics can be improved by PyC coatings. The best RL results are for 60 min-deposition sample, of which the minimum value is about -40.4 dB at about 9.5 GHz and the absorbing frequency band （AFB） is about 4 GHz.展开更多
基金Project(50772134) supported by the National Natural Science Foundation of ChinaProject(2006CB600901) supported by the National Basic Research Program of China
文摘The fabrication of a pyrocarbon coated carbon paper and its application to the gas diffusion lay(GDL) of proton exchange membrane(PEM) fuel cell were described.This carbon paper was fabricated by using conventional carbon paper as the precursor,and coating it with pyrocarbon by pyrolyzing propylene via the chemical vapor deposition(CVD) method.For comparison,conventional carbon paper composites were also prepared by using PAN-based carbon fiber felt as the precursor followed by impregnation with resin,molding and heat-treatment.SEM characterization indicates that pyrocarbon is uniformly deposited on the surface of the fiber in the pyrocarbon coated carbon paper and made the fibers of carbon felt bind more tightly.In contrast,there are cracks in matrix and debonding of fibers due to carbonization shrinkage in the conventional carbon paper.Property measurements show that the former has much better conductivity and gas permeability than the latter.In addition,current density-voltage performance tests also reveal that the pyrocarbon coating can improve the properties of carbon paper used for electrode materials of fuel cell.
基金Project (51072165) supported by the National Natural Science Foundation of ChinaProject (KP200901) supported by the Fund of the State Key Laboratory of Solidification Processing,China
文摘The pyrolytic carbon （PyC） coatings were fabricated on A1203 fiber fabrics by the method of chemical vapor deposition （CVD）. The microstructures of A1203 fibers with and without PyC coatings were characterized by SEM and Raman spectroscopy. The influence of deposition time of PyC on the DC conductivity （ad） of A1203 filaments and complex permittivity of fabrics at X band （8.2-12.4 GHz） were investigated. The values of Crd and complex permittivity increase with increasing deposition time of PyC. The electron relaxation polarization and conductance loss were supposed to be contributed to the increase of ε＇ and ε＂, respectively. In addition, the reflection loss （RL） of fabrics was calculated. The results show that the microwave absorbing properties of Al2O3 fiber fabrics can be improved by PyC coatings. The best RL results are for 60 min-deposition sample, of which the minimum value is about -40.4 dB at about 9.5 GHz and the absorbing frequency band （AFB） is about 4 GHz.