The difference of sintering crunodes of metal powders and fibers is discussed. The mathematical model of the surface diffusion described by the difference in mean curvature is defined as a Hamilton-Jacobi-type equatio...The difference of sintering crunodes of metal powders and fibers is discussed. The mathematical model of the surface diffusion described by the difference in mean curvature is defined as a Hamilton-Jacobi-type equation, and the model is numerically solved by the level set method. The three-dimensional numerical simulations of two metal powders and fibers(the fiber angle is 0° or 90°) are implemented by this mathematical model, respectively. The numerical simulation results accord with the experimental ones. The sintering neck growth trends of metal powders and metal fibers are similar. The sintering neck radius of metal fibers is larger than that of metal powders. The difference of the neck radius is caused by the difference of geometric structure which makes an important influence on the curvature affecting the migration rate of atoms.展开更多
Sintered metals are characterized by the high porosity(8%)and voids/micro-cracks in microns.Inelastic behavior of the materials is coupled with micro-crack propagation and coalescence of open voids.In the present work...Sintered metals are characterized by the high porosity(8%)and voids/micro-cracks in microns.Inelastic behavior of the materials is coupled with micro-crack propagation and coalescence of open voids.In the present work the damage evolution of the sintered iron under multi-axial monotonic loading conditions was investigated experimentally and computationally.The tests indicated that damage of the sintered iron initiated already at a stress level much lower than the macroscopic yield stress.The damage process can be divided into the stress-dominated elastic damage and the plastic damage described by the plastic strain.Based on the uniaxial tensile tests an elastic-plastic continuum damage model was developed which predicts both elastic damage and plastic damage in the sintered iron under general multi-axial monotonic loading conditions.Computational predictions agree with experiments with different multi-axial loading paths.A phenomenological continuum damage model for the sintered metal is developed based on the experimental observations to predict the inelastic behavior and damage process to failure under multi-axial loading conditions.The proposed damage model is experimentally verified under different loading conditions.展开更多
基金Projects(51174236,51134003)supported by the National Natural Science Foundation of ChinaProject(2011CB606306)supported by the National Basic Research Program of ChinaProject(PMM-SKL-4-2012)supported by the Opening Project of State Key Laboratory of Porous Metal Materials(Northwest Institute for Nonferrous Metal Research),China
文摘The difference of sintering crunodes of metal powders and fibers is discussed. The mathematical model of the surface diffusion described by the difference in mean curvature is defined as a Hamilton-Jacobi-type equation, and the model is numerically solved by the level set method. The three-dimensional numerical simulations of two metal powders and fibers(the fiber angle is 0° or 90°) are implemented by this mathematical model, respectively. The numerical simulation results accord with the experimental ones. The sintering neck growth trends of metal powders and metal fibers are similar. The sintering neck radius of metal fibers is larger than that of metal powders. The difference of the neck radius is caused by the difference of geometric structure which makes an important influence on the curvature affecting the migration rate of atoms.
基金supported by the National Natural Science Foundation of China(Grant No.51175041)
文摘Sintered metals are characterized by the high porosity(8%)and voids/micro-cracks in microns.Inelastic behavior of the materials is coupled with micro-crack propagation and coalescence of open voids.In the present work the damage evolution of the sintered iron under multi-axial monotonic loading conditions was investigated experimentally and computationally.The tests indicated that damage of the sintered iron initiated already at a stress level much lower than the macroscopic yield stress.The damage process can be divided into the stress-dominated elastic damage and the plastic damage described by the plastic strain.Based on the uniaxial tensile tests an elastic-plastic continuum damage model was developed which predicts both elastic damage and plastic damage in the sintered iron under general multi-axial monotonic loading conditions.Computational predictions agree with experiments with different multi-axial loading paths.A phenomenological continuum damage model for the sintered metal is developed based on the experimental observations to predict the inelastic behavior and damage process to failure under multi-axial loading conditions.The proposed damage model is experimentally verified under different loading conditions.