The catalytic activity measurement for the NO+CO reaction over CuO/CeO\-2/\%γ\%\|Al\-2O\-3 catalysts at a low\|temperature(200 ℃) shows that the activity is strongly related to ceria loading amount, and both surface...The catalytic activity measurement for the NO+CO reaction over CuO/CeO\-2/\%γ\%\|Al\-2O\-3 catalysts at a low\|temperature(200 ℃) shows that the activity is strongly related to ceria loading amount, and both surface dispersed ceria species and crystalline CeO\-2 shows a significant enhancement on the activity. The effect of ceria species is contributed to their promoting the reduction of copper oxide species.展开更多
Three-dimensionally ordered macro-/mesoporous alumina（3DOM Al2O3）-supported cobalt oxide and platinum nanocatalysts（xPt/yCo3O4/3DOM Al2O3,Pt mass fraction（x%）= 0-1.4%,Co3O4 mass fraction（y%） = 0-9.2%） were pre...Three-dimensionally ordered macro-/mesoporous alumina（3DOM Al2O3）-supported cobalt oxide and platinum nanocatalysts（xPt/yCo3O4/3DOM Al2O3,Pt mass fraction（x%）= 0-1.4%,Co3O4 mass fraction（y%） = 0-9.2%） were prepared using poly（methyl methacrylate） templating,incipient wetness impregnation and polyvinyl alcohol-protected reduction.The resulting xPt/yCo3O4/3DOM Al2O3 samples displayed a high-quality 3DOM architecture with macropores（180-200 nm in diameter） and mesopores（4-6 nm in diameter） together with surface areas in the range of 94 to 102m^2/g.Using these techniques,Co3O4 nanoparticles（NPs,18.3 nm） were loaded on the 3DOM Al2O3 surface,after which Pt NPs（2.3-2.5 nm） were uniformly dispersed on theyCo3O4/3DOM Al2O3.The1.3Pt/8.9Co3O4/3DOM Al2O3 exhibited the best performance for toluene oxidation,with a T（90%） value（the temperature required to achieve 90%toluene conversion） of 160 ℃ at a space velocity of20000 mL g^（-1） h^（-1）.It is concluded that the excellent catalytic performance of the 1.3Pt/8.9Co3O4/3DOM Al2O3 is owing to well-dispersed Pt NPs,the high concentration of adsorbed oxygen species,good low-temperature reducibility,and strong interaction between the Pt and Co3O4 NPs,as well as the unique bimodal porous structure of the support.展开更多
A series of sulfided PtMo/ γ Al 2O 3 catalysts[ w (Mo)=9.0%] with different contents of Pt were characterized by using low temperature FTIR spectroscopy of adsorbed CO, while their HDS activity was investigated with ...A series of sulfided PtMo/ γ Al 2O 3 catalysts[ w (Mo)=9.0%] with different contents of Pt were characterized by using low temperature FTIR spectroscopy of adsorbed CO, while their HDS activity was investigated with thiophene as a model substrate. Experimentally, it was found that no existence of the bands related to the surface complexes of Al 3+ ←CO and Pt 0←CO→Pt 0 was observed at 77 K and that the rate of the thiophene HDS reaction(573 K) is well linearly proportional to the area of the Pt 0←CO band at 2 093 cm -1 with a higher extrapolated HDS rate compared to that of sulfided Mo/ γ Al 2O 3 catalyst at the zero content of platinum. On the basis of the results here, the conclusion may be made that the active monolayer phase of Pt Mo S may be formed over sulfided PtMo/ γ Al 2O 3 catalysts during the sulfidation process and that both Mo 2+ and Pt 0 sites for CO adsorption should be the active reaction centers of thiophene HDS.展开更多
Low-loaded Pd（0.05 wt.%）/Al2O3 catalysts modified by ceria were prepared by impregnation method.Gas phase hydrogenation of acrylonitrile to propionitrile was selected as probe reaction to study the effect of the lig...Low-loaded Pd（0.05 wt.%）/Al2O3 catalysts modified by ceria were prepared by impregnation method.Gas phase hydrogenation of acrylonitrile to propionitrile was selected as probe reaction to study the effect of the light rare earth element cerium on the cataltic activity and stability.Experimental results indicated that addition of a small mount of ceria improved the catalytic activity and stability greatly.The best content of ceria was 3 wt.%,and consecutive impregnation method was prior to co-impregnation method.展开更多
文摘The catalytic activity measurement for the NO+CO reaction over CuO/CeO\-2/\%γ\%\|Al\-2O\-3 catalysts at a low\|temperature(200 ℃) shows that the activity is strongly related to ceria loading amount, and both surface dispersed ceria species and crystalline CeO\-2 shows a significant enhancement on the activity. The effect of ceria species is contributed to their promoting the reduction of copper oxide species.
基金supported by the National High Technology Research and Development Program of China(863 Program,2015AA034603)the National Natural Science Foundation of China(21377008)Foundation on the Creative Research Team Construction Promotion Project of Beijing Municipal Institutions
文摘Three-dimensionally ordered macro-/mesoporous alumina（3DOM Al2O3）-supported cobalt oxide and platinum nanocatalysts（xPt/yCo3O4/3DOM Al2O3,Pt mass fraction（x%）= 0-1.4%,Co3O4 mass fraction（y%） = 0-9.2%） were prepared using poly（methyl methacrylate） templating,incipient wetness impregnation and polyvinyl alcohol-protected reduction.The resulting xPt/yCo3O4/3DOM Al2O3 samples displayed a high-quality 3DOM architecture with macropores（180-200 nm in diameter） and mesopores（4-6 nm in diameter） together with surface areas in the range of 94 to 102m^2/g.Using these techniques,Co3O4 nanoparticles（NPs,18.3 nm） were loaded on the 3DOM Al2O3 surface,after which Pt NPs（2.3-2.5 nm） were uniformly dispersed on theyCo3O4/3DOM Al2O3.The1.3Pt/8.9Co3O4/3DOM Al2O3 exhibited the best performance for toluene oxidation,with a T（90%） value（the temperature required to achieve 90%toluene conversion） of 160 ℃ at a space velocity of20000 mL g^（-1） h^（-1）.It is concluded that the excellent catalytic performance of the 1.3Pt/8.9Co3O4/3DOM Al2O3 is owing to well-dispersed Pt NPs,the high concentration of adsorbed oxygen species,good low-temperature reducibility,and strong interaction between the Pt and Co3O4 NPs,as well as the unique bimodal porous structure of the support.
文摘A series of sulfided PtMo/ γ Al 2O 3 catalysts[ w (Mo)=9.0%] with different contents of Pt were characterized by using low temperature FTIR spectroscopy of adsorbed CO, while their HDS activity was investigated with thiophene as a model substrate. Experimentally, it was found that no existence of the bands related to the surface complexes of Al 3+ ←CO and Pt 0←CO→Pt 0 was observed at 77 K and that the rate of the thiophene HDS reaction(573 K) is well linearly proportional to the area of the Pt 0←CO band at 2 093 cm -1 with a higher extrapolated HDS rate compared to that of sulfided Mo/ γ Al 2O 3 catalyst at the zero content of platinum. On the basis of the results here, the conclusion may be made that the active monolayer phase of Pt Mo S may be formed over sulfided PtMo/ γ Al 2O 3 catalysts during the sulfidation process and that both Mo 2+ and Pt 0 sites for CO adsorption should be the active reaction centers of thiophene HDS.
文摘Low-loaded Pd（0.05 wt.%）/Al2O3 catalysts modified by ceria were prepared by impregnation method.Gas phase hydrogenation of acrylonitrile to propionitrile was selected as probe reaction to study the effect of the light rare earth element cerium on the cataltic activity and stability.Experimental results indicated that addition of a small mount of ceria improved the catalytic activity and stability greatly.The best content of ceria was 3 wt.%,and consecutive impregnation method was prior to co-impregnation method.