The age hardening behavior of gravity cast B356 aluminum alloy was investigated by differential scanning calorimetry(DSC), hardness measurements and tensile tests. Three different artificial aging temperatures were se...The age hardening behavior of gravity cast B356 aluminum alloy was investigated by differential scanning calorimetry(DSC), hardness measurements and tensile tests. Three different artificial aging temperatures were selected, namely 155, 165 and 180 °C, with heat treatment time from 40 min to 32 h. DSC analysis results show that cluster formation begins below room temperature(at around-10 °C). Since cluster formation influences the subsequent precipitation of the main strengthening β'' phase, it can be inferred that a delay between solutionizing and artificial aging has a detrimental effect on the mechanical properties of the alloy. It was also confirmed that the hardness and the tensile properties of the alloy reach the maximum values when β'' phase is completely developed during the artificial aging. This happens after 16 h for samples aged at 155 °C, after 6 h for samples aged at 165 °C and after 4 h for samples aged at 180 °C. A subsequent decrease of the mechanical properties, observed only in the sample aged at the highest temperature, with increasing aging time can be associated with the transformation of the coherent β'' phase into the semi-coherent β' phase. Finally, the activation energy associated with the precipitation of β'' phase was calculated to be 57.2 k J/mol.展开更多
The precipitation sequence of η（MgZn2） phase along low-angle grain boundaries in Al-Zn-Mg-Cu alloy was investigated by examining samples aged at 135 ℃ for various times from 5 min to 6 h. High resolution transmiss...The precipitation sequence of η（MgZn2） phase along low-angle grain boundaries in Al-Zn-Mg-Cu alloy was investigated by examining samples aged at 135 ℃ for various times from 5 min to 6 h. High resolution transmission electron microscopy （HRTEM） observations and energy dispersive X-ray spectroscopy （EDX） analysis indicate that the precipitation sequence of η phase along low-angle grain boundaries should be supersaturated solid solution （SSS）→vacancy-rich clusters （VRC）→GP Ⅱ zones→η＇→η. Based on the theory of non-equilibrium grain boundary segregation （NGS） and non-equilibrium grain boundary co-segregation （NGCS）, the excessive solute elements gradually segregate to the grain boundaries by the diffusion of the solute-vacancy complex during aging treatment. The grain boundary segregation plays an important role in the nucleation and growth of VRC, GP Ⅱ zones, η＇ phase as well as η phase.展开更多
基金funded by Regione Lombardia-MIUR (Research Program "2 MILLIMETRI" ID 30152773)
文摘The age hardening behavior of gravity cast B356 aluminum alloy was investigated by differential scanning calorimetry(DSC), hardness measurements and tensile tests. Three different artificial aging temperatures were selected, namely 155, 165 and 180 °C, with heat treatment time from 40 min to 32 h. DSC analysis results show that cluster formation begins below room temperature(at around-10 °C). Since cluster formation influences the subsequent precipitation of the main strengthening β'' phase, it can be inferred that a delay between solutionizing and artificial aging has a detrimental effect on the mechanical properties of the alloy. It was also confirmed that the hardness and the tensile properties of the alloy reach the maximum values when β'' phase is completely developed during the artificial aging. This happens after 16 h for samples aged at 155 °C, after 6 h for samples aged at 165 °C and after 4 h for samples aged at 180 °C. A subsequent decrease of the mechanical properties, observed only in the sample aged at the highest temperature, with increasing aging time can be associated with the transformation of the coherent β'' phase into the semi-coherent β' phase. Finally, the activation energy associated with the precipitation of β'' phase was calculated to be 57.2 k J/mol.
基金Project(51071122)supported by the National Natural Science Foundation of ChinaProject(B08040)supported by the Program of Introducing Talents of Discipline to Universities,China("111"Project)
文摘The precipitation sequence of η（MgZn2） phase along low-angle grain boundaries in Al-Zn-Mg-Cu alloy was investigated by examining samples aged at 135 ℃ for various times from 5 min to 6 h. High resolution transmission electron microscopy （HRTEM） observations and energy dispersive X-ray spectroscopy （EDX） analysis indicate that the precipitation sequence of η phase along low-angle grain boundaries should be supersaturated solid solution （SSS）→vacancy-rich clusters （VRC）→GP Ⅱ zones→η＇→η. Based on the theory of non-equilibrium grain boundary segregation （NGS） and non-equilibrium grain boundary co-segregation （NGCS）, the excessive solute elements gradually segregate to the grain boundaries by the diffusion of the solute-vacancy complex during aging treatment. The grain boundary segregation plays an important role in the nucleation and growth of VRC, GP Ⅱ zones, η＇ phase as well as η phase.