The permittivity of low grade Panzhuhua ilmenite ore at 2.45 GHz in the temperatures from 20 ℃ up to 100 ℃ was measured using the technology of open-ended coaxial sensor combined with theoretical computation. The re...The permittivity of low grade Panzhuhua ilmenite ore at 2.45 GHz in the temperatures from 20 ℃ up to 100 ℃ was measured using the technology of open-ended coaxial sensor combined with theoretical computation. The results show that both the real （ε′） and imaginary （ε′） part of complex permittivity （ε′-jε′） of the ilmenite significantly increase with temperature. The loss tangent （tanδ） is a quadratic function of temperature, and the penetration depth of ilmenite decreases with temperature increase from 20 ℃to 100 ℃ The increase of the sample temperature under microwave radiation displays a nonlinear relationship between the temperature （T） and microwave heating time （t）. The positive feedback interaction between complex permittivity and sample temperature amplifies the interaction between ilmenite and the microwave radiation. The optimum dimensions for uniform heat deposition vary from 10 cm to 5 cm （about two power penetration depths） in a sample being irradiated from both sides in a 2.45 GHz microwave field when temperature increases from room temperature to 100 ℃展开更多
The hydrogen reduction of Panzhihua ilmenite concentrate in the temperature range of 900?1050 °C was systematicallyinvestigated by thermogravimetric analysis (TG), X-ray diffraction (XRD) and scanning electron mi...The hydrogen reduction of Panzhihua ilmenite concentrate in the temperature range of 900?1050 °C was systematicallyinvestigated by thermogravimetric analysis (TG), X-ray diffraction (XRD) and scanning electron microscopy (SEM) methods. It wasshown that the products of the Panzhihua ilmenite reduced at 900 °C were metallic iron and rutile. Above 1000 °C, ferrouspseudobrookite solid solution was generated. During the reduction process, element Mg gradually concentrated to form Mg-rich zonewhich can influence the metallization process. The reduction reaction proceeded topochemically and its related reduction kineticswere also discussed. The kinetics of the reduction indicated that the rate-controlling step was the diffusion process. The apparentactivation energy of the hydrogen reduction of Panzhihua ilmenite was calculated to be 117.56 kJ/mol, which was larger than that ofsynthetic ilmenite under the same reduction condition.展开更多
基金Projects(51090385,5114703)supported by the National Natural Science Foundation of ChinaProject(2012DFA70570)supported by the International S&T Cooperation Program of ChinaProject(2011FZ038)supported by the Applied Basic Research Project of Yunnan Province
文摘The permittivity of low grade Panzhuhua ilmenite ore at 2.45 GHz in the temperatures from 20 ℃ up to 100 ℃ was measured using the technology of open-ended coaxial sensor combined with theoretical computation. The results show that both the real （ε′） and imaginary （ε′） part of complex permittivity （ε′-jε′） of the ilmenite significantly increase with temperature. The loss tangent （tanδ） is a quadratic function of temperature, and the penetration depth of ilmenite decreases with temperature increase from 20 ℃to 100 ℃ The increase of the sample temperature under microwave radiation displays a nonlinear relationship between the temperature （T） and microwave heating time （t）. The positive feedback interaction between complex permittivity and sample temperature amplifies the interaction between ilmenite and the microwave radiation. The optimum dimensions for uniform heat deposition vary from 10 cm to 5 cm （about two power penetration depths） in a sample being irradiated from both sides in a 2.45 GHz microwave field when temperature increases from room temperature to 100 ℃
基金Project(2014CB643403)supported by the National Basic Research Program of ChinaProjects(51225401,51304132,51574164)supported by the National Natural Science Foundation of China+1 种基金Project(14JC1491400)supported by the Science and Technology Commissions of Shanghai Municipality,ChinaProject(2013GZ0146)supported by the Sichuan Province,China
文摘The hydrogen reduction of Panzhihua ilmenite concentrate in the temperature range of 900?1050 °C was systematicallyinvestigated by thermogravimetric analysis (TG), X-ray diffraction (XRD) and scanning electron microscopy (SEM) methods. It wasshown that the products of the Panzhihua ilmenite reduced at 900 °C were metallic iron and rutile. Above 1000 °C, ferrouspseudobrookite solid solution was generated. During the reduction process, element Mg gradually concentrated to form Mg-rich zonewhich can influence the metallization process. The reduction reaction proceeded topochemically and its related reduction kineticswere also discussed. The kinetics of the reduction indicated that the rate-controlling step was the diffusion process. The apparentactivation energy of the hydrogen reduction of Panzhihua ilmenite was calculated to be 117.56 kJ/mol, which was larger than that ofsynthetic ilmenite under the same reduction condition.