The tensile properties and fatigue behavior of an Al-Zn-Mg-Cu alloy were investigated by performing tensile tests and fatigue crack propagation （FCP） tests. The tensile results show that lower aging temperature modi...The tensile properties and fatigue behavior of an Al-Zn-Mg-Cu alloy were investigated by performing tensile tests and fatigue crack propagation （FCP） tests. The tensile results show that lower aging temperature modified retrogression and re-aging （RRA） process enhances the elongation, but reduces the strength of the alloy, as compared to conventional RRA process which employs peak aging temperature. Both ductility and strength, however, are increased by employing a natural aging prior to re-aging based on the former modified RRA process. Fatigue test results show that both routes reduce FCP rate. Especially, the lower re-aging temperature modified RRA process obtains the lowest FCP rate. Natural aging treatment could enhance the nucleation rate of GP zones. A large amount of GP zones could be cut by dislocations, which is responsible for the highest tensile strength and elongation, as well as lower FCP rate.展开更多
基金Project(51171209)supported by the National Natural Science Foundation of ChinaProject(2012CB619506)supported by the National Basic Research Program of Chinasupported by the 2011 Program of Nonferrous Metals and Materials,China
文摘The tensile properties and fatigue behavior of an Al-Zn-Mg-Cu alloy were investigated by performing tensile tests and fatigue crack propagation （FCP） tests. The tensile results show that lower aging temperature modified retrogression and re-aging （RRA） process enhances the elongation, but reduces the strength of the alloy, as compared to conventional RRA process which employs peak aging temperature. Both ductility and strength, however, are increased by employing a natural aging prior to re-aging based on the former modified RRA process. Fatigue test results show that both routes reduce FCP rate. Especially, the lower re-aging temperature modified RRA process obtains the lowest FCP rate. Natural aging treatment could enhance the nucleation rate of GP zones. A large amount of GP zones could be cut by dislocations, which is responsible for the highest tensile strength and elongation, as well as lower FCP rate.