A new kind of multi-dimensional WC-10Co4Cr coating which is composed of nano,submicron,micron WC grains and CoCr alloy,was developed by high velocity oxy-fuel(HVOF)spraying.Porosity,microhardness,fracture toughness an...A new kind of multi-dimensional WC-10Co4Cr coating which is composed of nano,submicron,micron WC grains and CoCr alloy,was developed by high velocity oxy-fuel(HVOF)spraying.Porosity,microhardness,fracture toughness and cavitation erosion resistance of the multi-dimensional coating were investigated in comparison with the bimodal and nanostructured WC?10Co4Cr coatings.Moreover,the cavitation erosion behavior and mechanism of the multi-dimensional coating were explored.Results show that HVOF sprayed multi-dimensional WC-10Co4Cr coating possesses low porosity(≤0.32%)and high fracture toughness without obvious nano WC decarburization during spraying.Furthermore,it is discovered that the multi-dimensional WC-10Co4Cr coating exhibits the best cavitation erosion resistance which is enhanced by approximately 28%and 34%,respectively,compared with the nanostructured and bimodal coatings in fresh water.The superior cavitation resistance of multi-dimensional WC-10Co4Cr coating may originate from the unique micro?nano structure and excellent properties,which can effectively obstruct the formation and propagation of cavitation erosion cracks.展开更多
基金Projects(51422507,51379168)supported by the National Natural Science Foundation of China
文摘A new kind of multi-dimensional WC-10Co4Cr coating which is composed of nano,submicron,micron WC grains and CoCr alloy,was developed by high velocity oxy-fuel(HVOF)spraying.Porosity,microhardness,fracture toughness and cavitation erosion resistance of the multi-dimensional coating were investigated in comparison with the bimodal and nanostructured WC?10Co4Cr coatings.Moreover,the cavitation erosion behavior and mechanism of the multi-dimensional coating were explored.Results show that HVOF sprayed multi-dimensional WC-10Co4Cr coating possesses low porosity(≤0.32%)and high fracture toughness without obvious nano WC decarburization during spraying.Furthermore,it is discovered that the multi-dimensional WC-10Co4Cr coating exhibits the best cavitation erosion resistance which is enhanced by approximately 28%and 34%,respectively,compared with the nanostructured and bimodal coatings in fresh water.The superior cavitation resistance of multi-dimensional WC-10Co4Cr coating may originate from the unique micro?nano structure and excellent properties,which can effectively obstruct the formation and propagation of cavitation erosion cracks.