The crosslinkable trifluoromethylated poly(aryl ethers) terminated with phenylethynyl moieties(11F-PAE-PEP)s were prepared in two step syntheses. The structure of 11F-PAE-PEP was confirmed by FTIR and 1H NMR. The cros...The crosslinkable trifluoromethylated poly(aryl ethers) terminated with phenylethynyl moieties(11F-PAE-PEP)s were prepared in two step syntheses. The structure of 11F-PAE-PEP was confirmed by FTIR and 1H NMR. The crosslinking behavior was studied by DSC. There is a remarkable increase of T g after crosslinking of the poly(aryl ethers). The T g values of crosslinked polymers were 437 and 446 K, respectively. The crosslinked polymers could not be soluble in common organic solvents, such as N,N-dimethylformamide, N,N-dimethylacetamide, N-methyl-2-pyrrolidinone, chloroform, and tetrahydrofuran. The temperatures at a 5% mass loss of the crosslinked polymers in air were above 789 K. They showed a good optical property, too. This kind of polymers will be the promising materials used as the microelectronics and optical waveguide devices.展开更多
C1s and O1s of the 3,5-bitrifluoromethylated poly（aryl ether） terminated with phenylethynyl moieties（2CF3-PAE-PEP） before/after crosslinking were tested by the X-ray photoeletron spectroscopy（XPS）. The measureme...C1s and O1s of the 3,5-bitrifluoromethylated poly（aryl ether） terminated with phenylethynyl moieties（2CF3-PAE-PEP） before/after crosslinking were tested by the X-ray photoeletron spectroscopy（XPS）. The measurements show that some of the C\O bonds in the molecule structure will be broken if the films are crosslinked in the air, which is able to form some new CO bonds with the oxygen in the air. However, the ratios of the groups in the films cured in nitrogen remain the same as that of the uncured samples. It is the the forth harmonic of the stretching vibration of CO bond(4ν<sup>φ<sub>C=O) that causes the absorption loss at the wavelength 1 382 nm.展开更多
文摘The crosslinkable trifluoromethylated poly(aryl ethers) terminated with phenylethynyl moieties(11F-PAE-PEP)s were prepared in two step syntheses. The structure of 11F-PAE-PEP was confirmed by FTIR and 1H NMR. The crosslinking behavior was studied by DSC. There is a remarkable increase of T g after crosslinking of the poly(aryl ethers). The T g values of crosslinked polymers were 437 and 446 K, respectively. The crosslinked polymers could not be soluble in common organic solvents, such as N,N-dimethylformamide, N,N-dimethylacetamide, N-methyl-2-pyrrolidinone, chloroform, and tetrahydrofuran. The temperatures at a 5% mass loss of the crosslinked polymers in air were above 789 K. They showed a good optical property, too. This kind of polymers will be the promising materials used as the microelectronics and optical waveguide devices.
文摘C1s and O1s of the 3,5-bitrifluoromethylated poly（aryl ether） terminated with phenylethynyl moieties（2CF3-PAE-PEP） before/after crosslinking were tested by the X-ray photoeletron spectroscopy（XPS）. The measurements show that some of the C\O bonds in the molecule structure will be broken if the films are crosslinked in the air, which is able to form some new CO bonds with the oxygen in the air. However, the ratios of the groups in the films cured in nitrogen remain the same as that of the uncured samples. It is the the forth harmonic of the stretching vibration of CO bond(4ν<sup>φ<sub>C=O) that causes the absorption loss at the wavelength 1 382 nm.
