Monodispersed silica microspheres with diameter of 353nm were assembled into photonic crystal in ethanol colloidal suspensions of varied silica volume fraction at different temperature and humidity by means of control...Monodispersed silica microspheres with diameter of 353nm were assembled into photonic crystal in ethanol colloidal suspensions of varied silica volume fraction at different temperature and humidity by means of controllable vertical deposition method. The surface morphology and optical properties were studied by SEM and UV-Vis-NIR. It was found that the high-quality silica colloidal photonic crystals were obtained from ethanol solutions with environment temperature between 45℃ and 55℃, humidity between 66% and 76%, the volume fraction of microspheres is between 0.8% and 1.5%. The ordered close-packed photonic crystal fabricated by controllable vertical deposition method had the two photonic bandgaps in the visible light band and near infrared band.展开更多
High-quality SiO2 colloidal crystal multilayers were fabricated from ethanol solutions by the vertical deposition method and the effect of sintering on the optical properties of the samples was investigated. Optical p...High-quality SiO2 colloidal crystal multilayers were fabricated from ethanol solutions by the vertical deposition method and the effect of sintering on the optical properties of the samples was investigated. Optical properties, which are determined by the photonic band structure, were studied by means of light transmission and reflection measurements. The morphology of the samples was characterized by scanning electron microscopy (SEM). SEM images illustrate the ordered close package of the spherical colloids in planes parallel to the substrate surface. In addition, the sample is crackless as a result of an appropriate drying rate. It is shown that with the increase of the sintering final temperature, though the depth and the width of the peak of Bragg diffraction of the sample vary vastly, the peak produces few blue shifts. Optical measurement results were compared favorably to the microstructural properties of the colloidal crystal multilayers.展开更多
基金Aeronautic Science Foundation Programof China( 05G53038)
文摘Monodispersed silica microspheres with diameter of 353nm were assembled into photonic crystal in ethanol colloidal suspensions of varied silica volume fraction at different temperature and humidity by means of controllable vertical deposition method. The surface morphology and optical properties were studied by SEM and UV-Vis-NIR. It was found that the high-quality silica colloidal photonic crystals were obtained from ethanol solutions with environment temperature between 45℃ and 55℃, humidity between 66% and 76%, the volume fraction of microspheres is between 0.8% and 1.5%. The ordered close-packed photonic crystal fabricated by controllable vertical deposition method had the two photonic bandgaps in the visible light band and near infrared band.
基金supported by the National Natural Science Foundation of China(Grant No.69831010).
文摘High-quality SiO2 colloidal crystal multilayers were fabricated from ethanol solutions by the vertical deposition method and the effect of sintering on the optical properties of the samples was investigated. Optical properties, which are determined by the photonic band structure, were studied by means of light transmission and reflection measurements. The morphology of the samples was characterized by scanning electron microscopy (SEM). SEM images illustrate the ordered close package of the spherical colloids in planes parallel to the substrate surface. In addition, the sample is crackless as a result of an appropriate drying rate. It is shown that with the increase of the sintering final temperature, though the depth and the width of the peak of Bragg diffraction of the sample vary vastly, the peak produces few blue shifts. Optical measurement results were compared favorably to the microstructural properties of the colloidal crystal multilayers.