Microarray chip including genechip has been of great application in fields of biology, quarantine, pharmacy and so on. Most of microarray chips were prepared by spotting aqueous droplet on the surface of substrate. Du...Microarray chip including genechip has been of great application in fields of biology, quarantine, pharmacy and so on. Most of microarray chips were prepared by spotting aqueous droplet on the surface of substrate. Due to 'coffee-ring stain effect' , there always was a denser perimeter where sample was concentrated during the process of droplet drying after spotting. So the ununiformity of spot caused by 'coffee-ring stain effect' was one troublesome problem of the chip quality. Herein, superhydrophilic spot arrays on superhydrophobic AAO surface were fabricated to ease the 'coffee-ring stain effect' . Furthermore, a protein array is prepared on this patterned surface where immunoreactions are carried out. As a result, spot uniformity is greatly improved in a wide range of concentration and volume.展开更多
In this paper, thickness uniformity of poly（9,9-di-n-octylfluorene） films patterned by inkjet printing was im- proved by the use of solvent mixtures （a solvent with higher volatility, higher surface energy and lowe...In this paper, thickness uniformity of poly（9,9-di-n-octylfluorene） films patterned by inkjet printing was im- proved by the use of solvent mixtures （a solvent with higher volatility, higher surface energy and lower viscosity, with another solvent with lower volatility, lower surface energy and higher viscosity）. The average thickness of inkjet printed poly（9,9-di-n-octylfluorene） films was increased from ca. 30 nm to ca. 100 nm when solvent mixtures were used instead of pure chlorobenzene. More flat PFO films were formed instead of the original films with con- cave-lens like cross-section formed by coffee ring effect. This improvement was explained by combination of in- tense Marangoni flow at early drying process and weak complementary flow at the later drying process formed in the solvent mixture. Patterned poly（9,9-di-n-octylfluorene） films were used for fabrication of electroluminescence devices with improved electronic property. Array of pixels with about 80% effective light-emitting area was ob- tained.展开更多
Polymer thin film with uniform thickness and flat surface profile is the key point for polymer light emitting diodes(PLEDs) by inkjet printing. However, the coffee ring effect is usually observed due to the mismatch b...Polymer thin film with uniform thickness and flat surface profile is the key point for polymer light emitting diodes(PLEDs) by inkjet printing. However, the coffee ring effect is usually observed due to the mismatch between the evaporation of the solvent and the decrease of solution volume, which promotes the formation of radial flow from the interior of the drop to the edge. In this paper, coffee ring effects of inkjet printed poly(spirobifluorene) films were proposed to be restrained by decreasing capillary force by adding co-solvent with high boiling point and high viscosity to the main solvent. The low evaporation rate of the co-solvent can reduce the driving force of the radial flow; meanwhile the high viscosity of the co-solvent can increase the resistance of the radial flow. Thus, polymer films with improve uniformity can be obtained due to the suppression of the radial flow. The device performance was greatly improved under the condition of proper film thickness and film uniformity and the maximum luminous efficiency of devices with inkjet printed poly(spirobifluorene) can reach 80% of the spin-coated devices.展开更多
文摘Microarray chip including genechip has been of great application in fields of biology, quarantine, pharmacy and so on. Most of microarray chips were prepared by spotting aqueous droplet on the surface of substrate. Due to 'coffee-ring stain effect' , there always was a denser perimeter where sample was concentrated during the process of droplet drying after spotting. So the ununiformity of spot caused by 'coffee-ring stain effect' was one troublesome problem of the chip quality. Herein, superhydrophilic spot arrays on superhydrophobic AAO surface were fabricated to ease the 'coffee-ring stain effect' . Furthermore, a protein array is prepared on this patterned surface where immunoreactions are carried out. As a result, spot uniformity is greatly improved in a wide range of concentration and volume.
基金This work was subsidized by the National Natural Science Foundation of China，the Ministry of Science and Technology of China
文摘In this paper, thickness uniformity of poly（9,9-di-n-octylfluorene） films patterned by inkjet printing was im- proved by the use of solvent mixtures （a solvent with higher volatility, higher surface energy and lower viscosity, with another solvent with lower volatility, lower surface energy and higher viscosity）. The average thickness of inkjet printed poly（9,9-di-n-octylfluorene） films was increased from ca. 30 nm to ca. 100 nm when solvent mixtures were used instead of pure chlorobenzene. More flat PFO films were formed instead of the original films with con- cave-lens like cross-section formed by coffee ring effect. This improvement was explained by combination of in- tense Marangoni flow at early drying process and weak complementary flow at the later drying process formed in the solvent mixture. Patterned poly（9,9-di-n-octylfluorene） films were used for fabrication of electroluminescence devices with improved electronic property. Array of pixels with about 80% effective light-emitting area was ob- tained.
基金financially supported by the National Natural Science Foundation of China (Nos. 21574130, 51473161, 51873212)the Ministry of Science and Technology of China (No. 2015CB655001)National Key R&D Program of "Strategic Advanced Electronic Materials" (Nos. 2016YFB0401301, 2016YFB04011001)
文摘Polymer thin film with uniform thickness and flat surface profile is the key point for polymer light emitting diodes(PLEDs) by inkjet printing. However, the coffee ring effect is usually observed due to the mismatch between the evaporation of the solvent and the decrease of solution volume, which promotes the formation of radial flow from the interior of the drop to the edge. In this paper, coffee ring effects of inkjet printed poly(spirobifluorene) films were proposed to be restrained by decreasing capillary force by adding co-solvent with high boiling point and high viscosity to the main solvent. The low evaporation rate of the co-solvent can reduce the driving force of the radial flow; meanwhile the high viscosity of the co-solvent can increase the resistance of the radial flow. Thus, polymer films with improve uniformity can be obtained due to the suppression of the radial flow. The device performance was greatly improved under the condition of proper film thickness and film uniformity and the maximum luminous efficiency of devices with inkjet printed poly(spirobifluorene) can reach 80% of the spin-coated devices.