Solution-phase hydrogen reduction(Sp HR)was introduced into V_(2)O_(3)preparation to overcome disadvantages of traditional reduction roasting,which include a long process,high energy consumption,and generation of poll...Solution-phase hydrogen reduction(Sp HR)was introduced into V_(2)O_(3)preparation to overcome disadvantages of traditional reduction roasting,which include a long process,high energy consumption,and generation of pollution.The research mainly focuses onφ-pH diagrams and kinetics of SpHR.Thermodynamic analysis ofφ-pH diagrams for the V-H_(2)O system demonstrates that V_(2)O_(3)preparation via Sp HR requires a high temperature,a high vanadium concentration,and sufficient hydrogen in acidic solution.Kinetic analyses show that the activation energy of V_(2)O_(3)preparation via SpHR is 38.0679 k J/mol,indicating that the reduction is controlled by a combination of interfacial chemical reaction and internal diffusion.Effects of H;partial pressure(slope K=0.05246)on the reaction rate is not as significant as the vanadium concentration(K=1.58872).V_(2)O_(3)crystals with a purity of 99.59%and a vanadium precipitation rate of 99.83%were obtained under the following conditions:pH=5-6,c(V_(2)O_(3))=0.5 mol/L,p(H;)=4 MPa,m(PdCl;)=10 mg,T=250℃,and t=2.5 h.展开更多
基金financially supported by the National Key R&D Program of China(No.2020YFC1909700)Outstanding Young and Middle-aged Science and Technology Innovation Team Project of Hubei Province,China(No.T201802)the National Natural Science Foundation of China(No.52004187)。
文摘Solution-phase hydrogen reduction(Sp HR)was introduced into V_(2)O_(3)preparation to overcome disadvantages of traditional reduction roasting,which include a long process,high energy consumption,and generation of pollution.The research mainly focuses onφ-pH diagrams and kinetics of SpHR.Thermodynamic analysis ofφ-pH diagrams for the V-H_(2)O system demonstrates that V_(2)O_(3)preparation via Sp HR requires a high temperature,a high vanadium concentration,and sufficient hydrogen in acidic solution.Kinetic analyses show that the activation energy of V_(2)O_(3)preparation via SpHR is 38.0679 k J/mol,indicating that the reduction is controlled by a combination of interfacial chemical reaction and internal diffusion.Effects of H;partial pressure(slope K=0.05246)on the reaction rate is not as significant as the vanadium concentration(K=1.58872).V_(2)O_(3)crystals with a purity of 99.59%and a vanadium precipitation rate of 99.83%were obtained under the following conditions:pH=5-6,c(V_(2)O_(3))=0.5 mol/L,p(H;)=4 MPa,m(PdCl;)=10 mg,T=250℃,and t=2.5 h.