Three-dimensional honeycomb-structured magnesium （Mg） scaffolds with interconnected pores of accurately controlled pore size and porosity were fabricated by laser perforation technique. Biodegradable and bioactiveβ...Three-dimensional honeycomb-structured magnesium （Mg） scaffolds with interconnected pores of accurately controlled pore size and porosity were fabricated by laser perforation technique. Biodegradable and bioactiveβ- tricalcium phosphate （β-TCP） coatings were prepared on and the biodegradation mechanism was simply evaluated the porous Mg to further improve its biocompatibility, in vitro. It was found that the mechanical properties of this type of porous Mg significantly depended on its porosity. Elastic modulus and compressive strength similar to human bones could be obtained for the porous Mg with porosity of 42.6%-51%. It was observed that the human osteosarcoma cells （UMR106） were well adhered and proliferated on the surface of the β- TCP coated porous Mg, which indicates that theβ-TCP coated porous Mg is promising to be a bone tissue engineering scaffold material.展开更多
基金supported by Chinese Academy of Sciences (The Applied Research of Bioactive Bone Implantation Materials, No. KGCX2-YW-207)
文摘Three-dimensional honeycomb-structured magnesium （Mg） scaffolds with interconnected pores of accurately controlled pore size and porosity were fabricated by laser perforation technique. Biodegradable and bioactiveβ- tricalcium phosphate （β-TCP） coatings were prepared on and the biodegradation mechanism was simply evaluated the porous Mg to further improve its biocompatibility, in vitro. It was found that the mechanical properties of this type of porous Mg significantly depended on its porosity. Elastic modulus and compressive strength similar to human bones could be obtained for the porous Mg with porosity of 42.6%-51%. It was observed that the human osteosarcoma cells （UMR106） were well adhered and proliferated on the surface of the β- TCP coated porous Mg, which indicates that theβ-TCP coated porous Mg is promising to be a bone tissue engineering scaffold material.