Rare earth ion （Nd^3＋/Y^3＋） and Al^3＋ codoped α-Ni（OH）2 powers were synthesized by chemical coprecipitation method. The structttre was analyzed with X-ray diffraction （XRD） and thermal gravity （TG）. Cyclic...Rare earth ion （Nd^3＋/Y^3＋） and Al^3＋ codoped α-Ni（OH）2 powers were synthesized by chemical coprecipitation method. The structttre was analyzed with X-ray diffraction （XRD） and thermal gravity （TG）. Cyclic voltammetry （CV） tests were performed to evaluate the proton diffusion coefficients of the samples. The results indicated that codoping of Y-Al and Nd-Al resulted in more water molecules contained within the crystal lattice and accordingly increased the interlayer spacing. In particular, the Y-Al codoped α-Ni（OH）2 showed a turbostratic structure. The calculated diffusion coefficients of the Y-Al codoped α-Ni（OH）2 and Nd-Al codoped α-Ni（OH）2 were 3.5×10^-10cm^2/s and 2.8× 10^-10 cm^2/s, respectively.展开更多
基金the Guangxi Science Research and Technology Developing Foundation (0731001)
文摘Rare earth ion （Nd^3＋/Y^3＋） and Al^3＋ codoped α-Ni（OH）2 powers were synthesized by chemical coprecipitation method. The structttre was analyzed with X-ray diffraction （XRD） and thermal gravity （TG）. Cyclic voltammetry （CV） tests were performed to evaluate the proton diffusion coefficients of the samples. The results indicated that codoping of Y-Al and Nd-Al resulted in more water molecules contained within the crystal lattice and accordingly increased the interlayer spacing. In particular, the Y-Al codoped α-Ni（OH）2 showed a turbostratic structure. The calculated diffusion coefficients of the Y-Al codoped α-Ni（OH）2 and Nd-Al codoped α-Ni（OH）2 were 3.5×10^-10cm^2/s and 2.8× 10^-10 cm^2/s, respectively.