Aluminas were prepared by precipitation of aqueous aluminum nitrate solution using ammonium carbonate and ammonium hydroxide as precipitation agent respectively. The prepared samples were characterized by TG/DTA, XRD,...Aluminas were prepared by precipitation of aqueous aluminum nitrate solution using ammonium carbonate and ammonium hydroxide as precipitation agent respectively. The prepared samples were characterized by TG/DTA, XRD, surface area, pore volume and average pore diameter and the results were compared. The activity and stability of the close-coupled catalysts supported by aluminas prepared by different precipitating agent were compated. The alumina formed by ammonium carbonate showed larger surface area, pore volume, average pore diameter, higher thermal stability and better support property than that formed by ammonium hydroxide. The precusor of NH4Al(OH)2CO3 in the ammonium cabonate process was responsible for the difference.展开更多
The catalytic activity measurement for the NO+CO reaction over CuO/CeO\-2/\%γ\%\|Al\-2O\-3 catalysts at a low\|temperature(200 ℃) shows that the activity is strongly related to ceria loading amount, and both surface...The catalytic activity measurement for the NO+CO reaction over CuO/CeO\-2/\%γ\%\|Al\-2O\-3 catalysts at a low\|temperature(200 ℃) shows that the activity is strongly related to ceria loading amount, and both surface dispersed ceria species and crystalline CeO\-2 shows a significant enhancement on the activity. The effect of ceria species is contributed to their promoting the reduction of copper oxide species.展开更多
文摘Aluminas were prepared by precipitation of aqueous aluminum nitrate solution using ammonium carbonate and ammonium hydroxide as precipitation agent respectively. The prepared samples were characterized by TG/DTA, XRD, surface area, pore volume and average pore diameter and the results were compared. The activity and stability of the close-coupled catalysts supported by aluminas prepared by different precipitating agent were compated. The alumina formed by ammonium carbonate showed larger surface area, pore volume, average pore diameter, higher thermal stability and better support property than that formed by ammonium hydroxide. The precusor of NH4Al(OH)2CO3 in the ammonium cabonate process was responsible for the difference.
文摘The catalytic activity measurement for the NO+CO reaction over CuO/CeO\-2/\%γ\%\|Al\-2O\-3 catalysts at a low\|temperature(200 ℃) shows that the activity is strongly related to ceria loading amount, and both surface dispersed ceria species and crystalline CeO\-2 shows a significant enhancement on the activity. The effect of ceria species is contributed to their promoting the reduction of copper oxide species.