Two new isostructural multi-metal beryllium borates, m^3 Li Na4Be4B10O24F（M = Sr（1）, Cd（2））, have been synthesized by spontaneous crystallization. The structures were verified by single-crystal X-ray crystallogr...Two new isostructural multi-metal beryllium borates, m^3 Li Na4Be4B10O24F（M = Sr（1）, Cd（2））, have been synthesized by spontaneous crystallization. The structures were verified by single-crystal X-ray crystallography. The compounds crystallize in the trigonal space group R 3, with a = b = 9.4645（1） A, c = 38.842（8） A, V = 3013.2（6） A3, Z = 6, F（000） = 2568, Dc = 3.005 g/cm^3, Mr = 908.9, R = 0.0327, w R = 0.0678, μ = 8.160 mm-1 for Sr3 Li Na4Be4B10O24F and a = b = 9.3019（8） A, c = 37.782（7） A, V = 2831.12（9） A3, Z = 6, F（000） = 2748, Dc = 3.459 g/cm^3, Mr = 983.24, R = 0.0158, w R = 0.0455, μ = 3.586 mm-1 for Cd3 Li Na4Be4B10O24F. The structures are characterized by an infinite two-dimensional [Be8B16O40F2]∞ double layer bridged by [B12O24] groups like a sandwich structure, while the cations reside in tunnels along different directions. UV-vis-IR diffuse reflectance spectroscopy demonstrates that their cut-off edges are below 200 nm. Thermal analysis shows that they melt incongruently and their melting points are around 740-770 ℃.展开更多
基金supported by the National Natural Science Foundation of China(No.50972149,61138004,51402316)the National Instrumentation Program(No.2012YQ120048)
文摘Two new isostructural multi-metal beryllium borates, m^3 Li Na4Be4B10O24F（M = Sr（1）, Cd（2））, have been synthesized by spontaneous crystallization. The structures were verified by single-crystal X-ray crystallography. The compounds crystallize in the trigonal space group R 3, with a = b = 9.4645（1） A, c = 38.842（8） A, V = 3013.2（6） A3, Z = 6, F（000） = 2568, Dc = 3.005 g/cm^3, Mr = 908.9, R = 0.0327, w R = 0.0678, μ = 8.160 mm-1 for Sr3 Li Na4Be4B10O24F and a = b = 9.3019（8） A, c = 37.782（7） A, V = 2831.12（9） A3, Z = 6, F（000） = 2748, Dc = 3.459 g/cm^3, Mr = 983.24, R = 0.0158, w R = 0.0455, μ = 3.586 mm-1 for Cd3 Li Na4Be4B10O24F. The structures are characterized by an infinite two-dimensional [Be8B16O40F2]∞ double layer bridged by [B12O24] groups like a sandwich structure, while the cations reside in tunnels along different directions. UV-vis-IR diffuse reflectance spectroscopy demonstrates that their cut-off edges are below 200 nm. Thermal analysis shows that they melt incongruently and their melting points are around 740-770 ℃.