The ZrO2-Al2O3 ceramic composites were prepared by appropriate techniques with commercial ZrO2 and Al2O3 powders as raw materials and Y2O3 as stabilizer. The results indicate that with the introduction of Al2O3 into t...The ZrO2-Al2O3 ceramic composites were prepared by appropriate techniques with commercial ZrO2 and Al2O3 powders as raw materials and Y2O3 as stabilizer. The results indicate that with the introduction of Al2O3 into the ZrO2 matrix where the quantity of additive Y2O3 is 3.5% (mole fraction), the growth of ZrO2 grains is efficiently inhibited, which helps the ZrO2 grains exist in a metastable tetragonal manner; thus higher strength and toughness are acquired. When the content of alumina is 20% (mass fraction), the bending strength and fracture toughness of the composites are 676.7 MPa and 10 MPa·m1/2 respectively, the mechanical behaviors are close to those prepared with ZrO2 and Al2O3 powders synthesized through wet chemical approach. The mechanical behaviors of the composites are well improved owing to the dispersion toughening of alumina grains and phase transformation toughening of zirconia grains.展开更多
Composite ceramics thermal barrier coatings(TBCs) are widely used in the aero-engines field due to their excellent thermal insulation, which improves the service life and durability of the inherent hot components. The...Composite ceramics thermal barrier coatings(TBCs) are widely used in the aero-engines field due to their excellent thermal insulation, which improves the service life and durability of the inherent hot components. The most typical, successful and widely used TBCs material is yttria stabilized zirconia(YSZ). In this paper, fabrication methods, coating structures, materials, failure mechanism and major challenges of YSZ TBCs are introduced and reviewed. The research tendency is put forward as well. This review provides a good understanding of the YSZ TBCs and inspires researchers to discover versatile ideas to improve the TBCs systems.展开更多
管状电解质支撑型固体氧化物燃料电池(SOFC)具有稳定性高、电极选择范围广、易封接等优点,很适合应用于直接碳固体氧化物燃料电池(DC-SOFC)现阶段的基础研究中。为实现管状电解质支撑型SOFC的便捷制备,本研究开发了管状YSZ(钇稳定化氧化...管状电解质支撑型固体氧化物燃料电池(SOFC)具有稳定性高、电极选择范围广、易封接等优点,很适合应用于直接碳固体氧化物燃料电池(DC-SOFC)现阶段的基础研究中。为实现管状电解质支撑型SOFC的便捷制备,本研究开发了管状YSZ(钇稳定化氧化锆)电解质支撑膜的浸渍法制备工艺。组装了电极材料为Ag-GDC(钆掺杂氧化铈)的电解质支撑型SOFC单电池。测试了单电池分别以加湿氢气和担载5%(w,质量分数)Fe的活性炭为燃料,环境空气为氧化剂的电性能。电池的开路电压接近理论值,且扫描电镜分析结果表明电解质膜致密。单电池以活性碳为燃料在800°C取得了280 m W?cm^(-2)的最大功率密度,接近其以加湿氢气为燃料的330 m W?cm^(-2)。交流阻抗谱结果表明YSZ电解质的欧姆电阻是影响电池性能的主要原因。DC-SOFC以恒电流1 A放电,运行了2.1 h,燃料利用率为36%。DC-SOFC二次装载碳燃料后的电性能几乎与初次的性能一样,表明制备的YSZ电解质支撑膜可稳定的应用于DC-SOFCs中。分析了DC-SOFC放电过程中电性能衰减的机制。展开更多
Nanostructured yttria partially stabilized zirconia(YSZ) coatings were prepared by atmospheric plasma spraying(APS) using the conglomeration made by zirconia nanoparticle as the raw materials.The measurement methods,w...Nanostructured yttria partially stabilized zirconia(YSZ) coatings were prepared by atmospheric plasma spraying(APS) using the conglomeration made by zirconia nanoparticle as the raw materials.The measurement methods,which consisted of scanning electron microscopy(SEM),transmission electron microscopy(TEM) and thermal cycling behavior,were used to character the morphology,composition and thermal oxidation behavior of the powder and the coatings.From the results,it was shown that the YSZ coating was the laminar structure,and the elements distribution in the bond and top coat were well-proportioned.The YSZ coatings were composed of fine grains with size ranging from 30 to 110 nm.The laminar layers with columnar grains were surrounded with unmelted parts of the nanostructured powder and some equiaxed grains.In the as-sprayed nanostructured zirconia coatings,there existed pores that were less than 1 μm.The cracks were observed on some of the crystal border.The cyclic oxidation experiment showed that the nanostructured coating had longer thermal cycling lifetime to exhibit the promising thermal cyclic oxidation resistance.The failure of the nanostructured TBC was similar to the failure of conventional APS TBC.展开更多
Yttria stabilized zirconia (YSZ) has widely been used as electrolyte in solid oxide fuel cell (SOFC). The microstructure of YSZ related to the fabrication process was discussed in the paper. With YSZ nano-powders abou...Yttria stabilized zirconia (YSZ) has widely been used as electrolyte in solid oxide fuel cell (SOFC). The microstructure of YSZ related to the fabrication process was discussed in the paper. With YSZ nano-powders about 40-100 nm as raw material, the YSZ adobe was manufactured by tape calendering process. The named three-step sintering process was performed at 1000 ℃ for 2 h, then raised the temperature with normal rate and as soon as up to 1400 ℃, the furnace was controlled at 1250-1300 ℃ for 10-20 h. The high dense YSZs with the relative density of 96%-99% were obtained; the grain size of YSZ could be reduced to 0.5-3 μm. The above result is benefited to co-fired in the electrode-supported SOFCs.展开更多
文摘The ZrO2-Al2O3 ceramic composites were prepared by appropriate techniques with commercial ZrO2 and Al2O3 powders as raw materials and Y2O3 as stabilizer. The results indicate that with the introduction of Al2O3 into the ZrO2 matrix where the quantity of additive Y2O3 is 3.5% (mole fraction), the growth of ZrO2 grains is efficiently inhibited, which helps the ZrO2 grains exist in a metastable tetragonal manner; thus higher strength and toughness are acquired. When the content of alumina is 20% (mass fraction), the bending strength and fracture toughness of the composites are 676.7 MPa and 10 MPa·m1/2 respectively, the mechanical behaviors are close to those prepared with ZrO2 and Al2O3 powders synthesized through wet chemical approach. The mechanical behaviors of the composites are well improved owing to the dispersion toughening of alumina grains and phase transformation toughening of zirconia grains.
文摘Composite ceramics thermal barrier coatings(TBCs) are widely used in the aero-engines field due to their excellent thermal insulation, which improves the service life and durability of the inherent hot components. The most typical, successful and widely used TBCs material is yttria stabilized zirconia(YSZ). In this paper, fabrication methods, coating structures, materials, failure mechanism and major challenges of YSZ TBCs are introduced and reviewed. The research tendency is put forward as well. This review provides a good understanding of the YSZ TBCs and inspires researchers to discover versatile ideas to improve the TBCs systems.
文摘管状电解质支撑型固体氧化物燃料电池(SOFC)具有稳定性高、电极选择范围广、易封接等优点,很适合应用于直接碳固体氧化物燃料电池(DC-SOFC)现阶段的基础研究中。为实现管状电解质支撑型SOFC的便捷制备,本研究开发了管状YSZ(钇稳定化氧化锆)电解质支撑膜的浸渍法制备工艺。组装了电极材料为Ag-GDC(钆掺杂氧化铈)的电解质支撑型SOFC单电池。测试了单电池分别以加湿氢气和担载5%(w,质量分数)Fe的活性炭为燃料,环境空气为氧化剂的电性能。电池的开路电压接近理论值,且扫描电镜分析结果表明电解质膜致密。单电池以活性碳为燃料在800°C取得了280 m W?cm^(-2)的最大功率密度,接近其以加湿氢气为燃料的330 m W?cm^(-2)。交流阻抗谱结果表明YSZ电解质的欧姆电阻是影响电池性能的主要原因。DC-SOFC以恒电流1 A放电,运行了2.1 h,燃料利用率为36%。DC-SOFC二次装载碳燃料后的电性能几乎与初次的性能一样,表明制备的YSZ电解质支撑膜可稳定的应用于DC-SOFCs中。分析了DC-SOFC放电过程中电性能衰减的机制。
基金Project supported by the National Defense Basic Scientific Research Program of China (K0504030206)
文摘Nanostructured yttria partially stabilized zirconia(YSZ) coatings were prepared by atmospheric plasma spraying(APS) using the conglomeration made by zirconia nanoparticle as the raw materials.The measurement methods,which consisted of scanning electron microscopy(SEM),transmission electron microscopy(TEM) and thermal cycling behavior,were used to character the morphology,composition and thermal oxidation behavior of the powder and the coatings.From the results,it was shown that the YSZ coating was the laminar structure,and the elements distribution in the bond and top coat were well-proportioned.The YSZ coatings were composed of fine grains with size ranging from 30 to 110 nm.The laminar layers with columnar grains were surrounded with unmelted parts of the nanostructured powder and some equiaxed grains.In the as-sprayed nanostructured zirconia coatings,there existed pores that were less than 1 μm.The cracks were observed on some of the crystal border.The cyclic oxidation experiment showed that the nanostructured coating had longer thermal cycling lifetime to exhibit the promising thermal cyclic oxidation resistance.The failure of the nanostructured TBC was similar to the failure of conventional APS TBC.
基金The project was financiallysupportedby Ministry of Education,China(No.106087)and 863 Program of National High Technology Research Development Project,China(2005AA501050).
文摘Yttria stabilized zirconia (YSZ) has widely been used as electrolyte in solid oxide fuel cell (SOFC). The microstructure of YSZ related to the fabrication process was discussed in the paper. With YSZ nano-powders about 40-100 nm as raw material, the YSZ adobe was manufactured by tape calendering process. The named three-step sintering process was performed at 1000 ℃ for 2 h, then raised the temperature with normal rate and as soon as up to 1400 ℃, the furnace was controlled at 1250-1300 ℃ for 10-20 h. The high dense YSZs with the relative density of 96%-99% were obtained; the grain size of YSZ could be reduced to 0.5-3 μm. The above result is benefited to co-fired in the electrode-supported SOFCs.