The influence of calcium treatment on non-metallic inclusions had been studied when control technology of refining top slag in ladle furnace was used in ultra-low oxygen steelmaking. A sufficient amount aluminium was ...The influence of calcium treatment on non-metallic inclusions had been studied when control technology of refining top slag in ladle furnace was used in ultra-low oxygen steelmaking. A sufficient amount aluminium was added to experimental heats for final deoxidizing during BOF tapping, and the refining top slag with strong reducibility, high basicity and high Al2O3 in ladle furnace was used to produce ultra-low oxygen steel and the transformation of nonmetallic inclusions in molten steel was compared by calcium treatment and no calcium treatment. The results show that the transformation of Al2O3--MgO - Al2O3 spinel-CaO-MgO-Al2O3 complex inclusions has been completed for aluminum deoxidation products and calcium treatment to molten steel is unnecessary when using the control technology of ladle furnace refining top slag to produce ultra-low oxygen steel, and the complex inclusions are liquid at the temperature of steelmaking and easily removable to obtain very high cleanliness steel by flotation. Further- more, the problems of nozzle clogging in casting operations do not happen and the remaining oxide inclusions in steel are the relatively lower melting point complex inclusions.展开更多
The effect of top slag basicity on quality of steel treated with SiFe and SiCaBa alloy as exothermic agent in chemical heating was studied. These experiments were carried out in MoSi 2 laboratory furnace with 0 2?kg...The effect of top slag basicity on quality of steel treated with SiFe and SiCaBa alloy as exothermic agent in chemical heating was studied. These experiments were carried out in MoSi 2 laboratory furnace with 0 2?kg molten steel for equilibrium test and 2?kg molten steel for simulation test respectively. These results showed that the adjusting basicity of top slag with CaO is effective to prevent rephosphorization and resulphurization, and it is possible to dephosphorize and desulphurize and remove the inclusions from molten steel when basicity R of the top slag is adjusted to 2 0-3 10, and SiCaBa alloy is better than SiFe alloy in this relation.展开更多
The effect of top slag basicity on quality of steel treated with SiFe and SiCaBa alloy as exothermic agent in chemical heating was studied.These experiments were carried out in MoSi_2 laboratory furnace with 0.2 kg mo...The effect of top slag basicity on quality of steel treated with SiFe and SiCaBa alloy as exothermic agent in chemical heating was studied.These experiments were carried out in MoSi_2 laboratory furnace with 0.2 kg molten steel for equilibrium test and 2 kg molten steel for simulation test respectively.These results showed that the adjusting basicity of top slag with CaO is effective to prevent rephosphorization and resulphurization,and it is possible to dephosphorize and desulphurize and remove the inclusions from molten steel when basicity R of the top slag is adjusted to 2.0 — 3.10,and SiCaBa alloy is better than SiFe alloy in this relation.展开更多
基金Item Sponsored by National Basic Research Program of China(2010CB630806)
文摘The influence of calcium treatment on non-metallic inclusions had been studied when control technology of refining top slag in ladle furnace was used in ultra-low oxygen steelmaking. A sufficient amount aluminium was added to experimental heats for final deoxidizing during BOF tapping, and the refining top slag with strong reducibility, high basicity and high Al2O3 in ladle furnace was used to produce ultra-low oxygen steel and the transformation of nonmetallic inclusions in molten steel was compared by calcium treatment and no calcium treatment. The results show that the transformation of Al2O3--MgO - Al2O3 spinel-CaO-MgO-Al2O3 complex inclusions has been completed for aluminum deoxidation products and calcium treatment to molten steel is unnecessary when using the control technology of ladle furnace refining top slag to produce ultra-low oxygen steel, and the complex inclusions are liquid at the temperature of steelmaking and easily removable to obtain very high cleanliness steel by flotation. Further- more, the problems of nozzle clogging in casting operations do not happen and the remaining oxide inclusions in steel are the relatively lower melting point complex inclusions.
文摘The effect of top slag basicity on quality of steel treated with SiFe and SiCaBa alloy as exothermic agent in chemical heating was studied. These experiments were carried out in MoSi 2 laboratory furnace with 0 2?kg molten steel for equilibrium test and 2?kg molten steel for simulation test respectively. These results showed that the adjusting basicity of top slag with CaO is effective to prevent rephosphorization and resulphurization, and it is possible to dephosphorize and desulphurize and remove the inclusions from molten steel when basicity R of the top slag is adjusted to 2 0-3 10, and SiCaBa alloy is better than SiFe alloy in this relation.
基金Sponsored by National Natural Science Foundation(59874014)
文摘The effect of top slag basicity on quality of steel treated with SiFe and SiCaBa alloy as exothermic agent in chemical heating was studied.These experiments were carried out in MoSi_2 laboratory furnace with 0.2 kg molten steel for equilibrium test and 2 kg molten steel for simulation test respectively.These results showed that the adjusting basicity of top slag with CaO is effective to prevent rephosphorization and resulphurization,and it is possible to dephosphorize and desulphurize and remove the inclusions from molten steel when basicity R of the top slag is adjusted to 2.0 — 3.10,and SiCaBa alloy is better than SiFe alloy in this relation.