The A356 aluminum alloy wheels were prepared by thixo-forging combined with a low superheat casting process. The as-cast microstructure, microstructure evolution during reheating and the mechanical properties of the t...The A356 aluminum alloy wheels were prepared by thixo-forging combined with a low superheat casting process. The as-cast microstructure, microstructure evolution during reheating and the mechanical properties of the thixo-forged A356 aluminum alloy wheels were investigated. The results show that the A356 aluminum alloy billet with fine, uniform and non-dendritic grains can be obtained when the melt is cast at 635 ℃. When the billet is reheated at 600 ℃ for 60 min, the non-dendritic grains are changed into spherical ones and the billet can be easily thixo-forged into wheels. The tensile strength and elongation of thixo-forged wheels with T6 heat treatment are 327.6 MPa and 7.8%, respectively, which are higher than those of a cast wheel. It is suggested that the thixo-forging combined with the low superheat casting process is an effective technique to produce aluminum alloy wheels with high mechanical properties.展开更多
The A356 aluminum alloy wheels were produced by thixo-forging combined with a low superheat casting process. The as-cast microstructure, microstructure evolution during reheating and the mechanical properties of thixo...The A356 aluminum alloy wheels were produced by thixo-forging combined with a low superheat casting process. The as-cast microstructure, microstructure evolution during reheating and the mechanical properties of thixo-forged wheels made from the A356 aluminum alloy were studied. The results show that the A356 aluminum alloy round billet with fine, uniform and non-dendritic grains can be obtained when the melt is cast at 635 ℃ When the round billet is reheated at 600 ℃ for 60 min, the non-dendritic grains are changed into spherical ones and the round billet can be easily thixo-forged into wheels. The tensile strength, yield strength and elongation of the thixo-forged wheels with T6 heat treatment are 327.6 MPa, 228.3 MPa and 7.8%, respectively, which are higher than those of a cast wheel. It is suggested that the thixo-forging combined with the low superheat casting process is an effective technique to produce aluminum alloy wheels with high mechanical properties.展开更多
The rapid development of electronic packaging industry has resulted in higher requirement for packaging materials.The packaging material of SiC reinforced A356 aluminum alloy was fabricated by mechanical mixing method...The rapid development of electronic packaging industry has resulted in higher requirement for packaging materials.The packaging material of SiC reinforced A356 aluminum alloy was fabricated by mechanical mixing method,and the SiCp/Al composite billet was formed by thixo-forging to manufacture the electronic packaging shell.The microstructure of the produced part was investigated.Two different thixo-forging procedures for manufacturing electronic packaging shell were analyzed.The results show that after being heated to 600 ℃ and held for 3 h,SiCp has good compatibility with A356 aluminum alloy and the SiCp/A356 composite billet can meet the requirements of thixo-forging.When the billet was remelted to 580℃,held for 10 min,the homogeneous microstructure with the best thixo-formability can be realized.The thixo-forging of electronic packaging shell is feasible.展开更多
In order to investigate the formability of metal material in semisolid state, a series of experiments were carried out by thixo-forging the complex part of aluminum alloy AlSi7Mg. Through changing the upper punch, alu...In order to investigate the formability of metal material in semisolid state, a series of experiments were carried out by thixo-forging the complex part of aluminum alloy AlSi7Mg. Through changing the upper punch, aluminum parts with different upper-cup dimensions can be successfully produced. The numerical simulation was conducted for investigating the forming limits of AlSi7Mg during thixo-forging. It is found that the simulation result is in good agreement with the experiment one.展开更多
A new technology thixo-die-forging of the composite in pseudo-semi-solid state was proposed based on the powder metallurgy technology combing with semi-solid metal process, and the cup shells with Al/Al2O3 composite w...A new technology thixo-die-forging of the composite in pseudo-semi-solid state was proposed based on the powder metallurgy technology combing with semi-solid metal process, and the cup shells with Al/Al2O3 composite was prepared successfully. The metallographic analysis and performance test show that the microstructure of parts is dense and mechanical properties axe excellent with the volume fraction of Al is 37%. The bend strength and fracture toughness of the composite are about 570- 690 MPa and 8.5-16.8 MPa·m^1/2, respectively. Comparing with reaction in situ and high temperature oxidation technologies the bending strength and fracture toughness are improved greatly. At the same time, it shows that the technology parameters have great influences on the properties. So it is feasible to prepare metal/ceramics composites by the proposed technology.展开更多
基金Project(2012B090600051)supported by the Guangdong Provincial Department of Science and Technology,ChinaProject(2013EG115006)supported by the Special Program for Technology Development from the Ministry of Science and Technology of China
文摘The A356 aluminum alloy wheels were prepared by thixo-forging combined with a low superheat casting process. The as-cast microstructure, microstructure evolution during reheating and the mechanical properties of the thixo-forged A356 aluminum alloy wheels were investigated. The results show that the A356 aluminum alloy billet with fine, uniform and non-dendritic grains can be obtained when the melt is cast at 635 ℃. When the billet is reheated at 600 ℃ for 60 min, the non-dendritic grains are changed into spherical ones and the billet can be easily thixo-forged into wheels. The tensile strength and elongation of thixo-forged wheels with T6 heat treatment are 327.6 MPa and 7.8%, respectively, which are higher than those of a cast wheel. It is suggested that the thixo-forging combined with the low superheat casting process is an effective technique to produce aluminum alloy wheels with high mechanical properties.
基金financially supported by the Science and Technology Innovation Foundation of Guangzhou Research Institute of Non-ferrous Metals(2009A10)the Guangdong Province Cooperation Project of Industry,Education and Academy(2012B090600051)
文摘The A356 aluminum alloy wheels were produced by thixo-forging combined with a low superheat casting process. The as-cast microstructure, microstructure evolution during reheating and the mechanical properties of thixo-forged wheels made from the A356 aluminum alloy were studied. The results show that the A356 aluminum alloy round billet with fine, uniform and non-dendritic grains can be obtained when the melt is cast at 635 ℃ When the round billet is reheated at 600 ℃ for 60 min, the non-dendritic grains are changed into spherical ones and the round billet can be easily thixo-forged into wheels. The tensile strength, yield strength and elongation of the thixo-forged wheels with T6 heat treatment are 327.6 MPa, 228.3 MPa and 7.8%, respectively, which are higher than those of a cast wheel. It is suggested that the thixo-forging combined with the low superheat casting process is an effective technique to produce aluminum alloy wheels with high mechanical properties.
基金Project (2007AA03Z119) supported by the National High Technology Research and Development Program of Chinaprojects (2102029,2072012) supported by Beijing Natural Science Foundation,China
文摘The rapid development of electronic packaging industry has resulted in higher requirement for packaging materials.The packaging material of SiC reinforced A356 aluminum alloy was fabricated by mechanical mixing method,and the SiCp/Al composite billet was formed by thixo-forging to manufacture the electronic packaging shell.The microstructure of the produced part was investigated.Two different thixo-forging procedures for manufacturing electronic packaging shell were analyzed.The results show that after being heated to 600 ℃ and held for 3 h,SiCp has good compatibility with A356 aluminum alloy and the SiCp/A356 composite billet can meet the requirements of thixo-forging.When the billet was remelted to 580℃,held for 10 min,the homogeneous microstructure with the best thixo-formability can be realized.The thixo-forging of electronic packaging shell is feasible.
基金supported by the National High-Tech Research and Development Program of China(No.2007AA03Z119)the National Natural Science Foundation of Beijing (No.2072012 and No.2102029 )
文摘In order to investigate the formability of metal material in semisolid state, a series of experiments were carried out by thixo-forging the complex part of aluminum alloy AlSi7Mg. Through changing the upper punch, aluminum parts with different upper-cup dimensions can be successfully produced. The numerical simulation was conducted for investigating the forming limits of AlSi7Mg during thixo-forging. It is found that the simulation result is in good agreement with the experiment one.
基金supported by National Natural Science Foundation of China(No50705018)Postdoctoral Foundation of China (No20070420847)
文摘A new technology thixo-die-forging of the composite in pseudo-semi-solid state was proposed based on the powder metallurgy technology combing with semi-solid metal process, and the cup shells with Al/Al2O3 composite was prepared successfully. The metallographic analysis and performance test show that the microstructure of parts is dense and mechanical properties axe excellent with the volume fraction of Al is 37%. The bend strength and fracture toughness of the composite are about 570- 690 MPa and 8.5-16.8 MPa·m^1/2, respectively. Comparing with reaction in situ and high temperature oxidation technologies the bending strength and fracture toughness are improved greatly. At the same time, it shows that the technology parameters have great influences on the properties. So it is feasible to prepare metal/ceramics composites by the proposed technology.