In this study, composite briquettes were prepared using gravity dust and converter sludge as the main materials; these briquettes were subsequently reduced in a tube furnace at 1000-1300℃ for 5-30 min under a nitroge...In this study, composite briquettes were prepared using gravity dust and converter sludge as the main materials; these briquettes were subsequently reduced in a tube furnace at 1000-1300℃ for 5-30 min under a nitrogen atmosphere. The effects of reaction temperature, reaction time, and carbon content on the metallization and dezincification ratios of the composite briquettes were studied. The reduced com- posite briquettes were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and energy-dispersive spectroscopy （EDS）. The results show that the gravity dust and converter sludge are combined into the composite briquettes and a reasonable combination not only improves the performance of the composite briquettes, but also leads to the reduction with no or little reductant and flux. As the re- action temperature is increased and the reaction time is extended, the metallization and dezincification ratios of the composite briquettes in- crease gradually. When the composite briquettes are roasted at 1300℃ for 30 rain, the metallization ratio and dezineification ratio reaches 91.35% and 99.25%, respectively, indicating that most of the iron oxide is reduced and the zinc is almost completely removed. The carbon content is observed to exert a lesser effect on the reduction process; as the C/O molar ratio increases, the metallization and dezincification ra- tios first increase and then decrease.展开更多
Deep eutectic solvents(DESs) are a kind of potential lixiviant for selective metal processing due to their versatile complexation properties. In this study, we investigated the recovery of zinc from zinc oxide dust us...Deep eutectic solvents(DESs) are a kind of potential lixiviant for selective metal processing due to their versatile complexation properties. In this study, we investigated the recovery of zinc from zinc oxide dust using choline chloride-ureaethylene glycol(ChCl-urea-EG) DESs. The zinc extraction efficiency can be up to 85.2% when the slurry concentration is 50 g/L, leaching temperature is 80 °C and stirring speed is 600 r/min. The leaching process is controlled by the diffusion and the corresponding activation energy is 32.1 k J/mol. The resultant solution was directly used for the electrodeposition of zinc. The pure zinc deposit is obtained with a current efficiency of 82.6%. Furthermore, the ChCl-urea-EG DESs can be recycled. This approach is shown to be promising for the recycling of zinc from the zinc-containing dust.展开更多
Basic physicochemical properties of the dust from Laiwu Iron and Steel Co. Ltd. were studied. It is found that C, Zn, K, Na, etc. exist in the fabric filter dust, off gas （OG） sludge, fine ash in converter, and elec...Basic physicochemical properties of the dust from Laiwu Iron and Steel Co. Ltd. were studied. It is found that C, Zn, K, Na, etc. exist in the fabric filter dust, off gas （OG） sludge, fine ash in converter, and electrical field dust in sinter. Among these, OG sludge gives the finest particle, more than 90% of which is less than 2.51 mm. The dust can lead to a serious negative influence on the production of sintering and blast furnaces （BF） if it is recycled in sintering. The briquette and reduction experimental results showed that the qualified strength could be obtained in the case of 8wt% molasses or 4wt% QT-10 added as binders. Also, more than 75% of metallization ratio, more than 95% of dezincing ratio, as well as more than 80% of K and Na removal rates were achieved for the briquettes kept at 1250℃ for 15 min during the direct reduction process. SEM observation indicated that the rates of indirect reduction and carbonization became dominating when the bri-quettes were kept at 1250℃ for 6 min.展开更多
基金financially supported by the National Natural Science Foundation of China(No.U1260202)the National Basic Research Priorities Program of China(No.2012CB720401)the State Key Laboratory of Solid Waste Reuse for Building Materials
文摘In this study, composite briquettes were prepared using gravity dust and converter sludge as the main materials; these briquettes were subsequently reduced in a tube furnace at 1000-1300℃ for 5-30 min under a nitrogen atmosphere. The effects of reaction temperature, reaction time, and carbon content on the metallization and dezincification ratios of the composite briquettes were studied. The reduced com- posite briquettes were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and energy-dispersive spectroscopy （EDS）. The results show that the gravity dust and converter sludge are combined into the composite briquettes and a reasonable combination not only improves the performance of the composite briquettes, but also leads to the reduction with no or little reductant and flux. As the re- action temperature is increased and the reaction time is extended, the metallization and dezincification ratios of the composite briquettes in- crease gradually. When the composite briquettes are roasted at 1300℃ for 30 rain, the metallization ratio and dezineification ratio reaches 91.35% and 99.25%, respectively, indicating that most of the iron oxide is reduced and the zinc is almost completely removed. The carbon content is observed to exert a lesser effect on the reduction process; as the C/O molar ratio increases, the metallization and dezincification ra- tios first increase and then decrease.
基金Project(51764027) supported by the National Natural Science Foundation of ChinaProject(2014CB643404) supported by the National Basic Research Program of China
文摘Deep eutectic solvents(DESs) are a kind of potential lixiviant for selective metal processing due to their versatile complexation properties. In this study, we investigated the recovery of zinc from zinc oxide dust using choline chloride-ureaethylene glycol(ChCl-urea-EG) DESs. The zinc extraction efficiency can be up to 85.2% when the slurry concentration is 50 g/L, leaching temperature is 80 °C and stirring speed is 600 r/min. The leaching process is controlled by the diffusion and the corresponding activation energy is 32.1 k J/mol. The resultant solution was directly used for the electrodeposition of zinc. The pure zinc deposit is obtained with a current efficiency of 82.6%. Furthermore, the ChCl-urea-EG DESs can be recycled. This approach is shown to be promising for the recycling of zinc from the zinc-containing dust.
文摘Basic physicochemical properties of the dust from Laiwu Iron and Steel Co. Ltd. were studied. It is found that C, Zn, K, Na, etc. exist in the fabric filter dust, off gas （OG） sludge, fine ash in converter, and electrical field dust in sinter. Among these, OG sludge gives the finest particle, more than 90% of which is less than 2.51 mm. The dust can lead to a serious negative influence on the production of sintering and blast furnaces （BF） if it is recycled in sintering. The briquette and reduction experimental results showed that the qualified strength could be obtained in the case of 8wt% molasses or 4wt% QT-10 added as binders. Also, more than 75% of metallization ratio, more than 95% of dezincing ratio, as well as more than 80% of K and Na removal rates were achieved for the briquettes kept at 1250℃ for 15 min during the direct reduction process. SEM observation indicated that the rates of indirect reduction and carbonization became dominating when the bri-quettes were kept at 1250℃ for 6 min.