The TiO2/vermiculite composites were prepared by in-situ hydrolyzing reaction and in-situ dehydrating reaction of tetrabutyl titanate-hexadecyl trimethyl ammonium bromide intercalated vermiculite. The structural phase...The TiO2/vermiculite composites were prepared by in-situ hydrolyzing reaction and in-situ dehydrating reaction of tetrabutyl titanate-hexadecyl trimethyl ammonium bromide intercalated vermiculite. The structural phase transition of TiO2 in TiO2/vermiculite composites calcined at different temperatures was characterized by using XRD and Raman. The results show that at calcination temperature of 800℃ appeared the anatase phase of TiO2 in TiO2/vermiculite nanocomposites, while pure TiO2 is all converted to rutile at the same temperature. The average crystal size of TiO2 in TiO2/vermiculite nanocomposites and pure TiO2 both increase with the calcination temperature. The average grain size of TiO2 in TiO2/vermiculite nanocomposites is less than that of pure TiO2 at the same calcination temperature. The results also show that the silicon-oxygen structure in layered vermiculite structure can effectively depress the phase transformation from anatase to rutile, thus enhancing the transition temperature and inhibitting the growth of anatase crystals.展开更多
文摘The TiO2/vermiculite composites were prepared by in-situ hydrolyzing reaction and in-situ dehydrating reaction of tetrabutyl titanate-hexadecyl trimethyl ammonium bromide intercalated vermiculite. The structural phase transition of TiO2 in TiO2/vermiculite composites calcined at different temperatures was characterized by using XRD and Raman. The results show that at calcination temperature of 800℃ appeared the anatase phase of TiO2 in TiO2/vermiculite nanocomposites, while pure TiO2 is all converted to rutile at the same temperature. The average crystal size of TiO2 in TiO2/vermiculite nanocomposites and pure TiO2 both increase with the calcination temperature. The average grain size of TiO2 in TiO2/vermiculite nanocomposites is less than that of pure TiO2 at the same calcination temperature. The results also show that the silicon-oxygen structure in layered vermiculite structure can effectively depress the phase transformation from anatase to rutile, thus enhancing the transition temperature and inhibitting the growth of anatase crystals.