Hypo-peritectic steels are widely used in various industrial fields because of their high strength,high toughness,high processability,high weldability,and low material cost.However,surface defects are liable to occur ...Hypo-peritectic steels are widely used in various industrial fields because of their high strength,high toughness,high processability,high weldability,and low material cost.However,surface defects are liable to occur during continuous casting,which includes depression,longitudinal cracks,deep oscillation marks,and severe level fluctuation with slag entrapment.The high-efficiency production of hypo-peritectic steels by continuous casting is still a great challenge due to the limited understanding of the mechanism of peritectic solidification.This work reviews the definition and classification of hypo-peritectic steels and introduces the formation tendency of common surface defects related to peritectic solidification.New achievements in the mechanism of peritectic reaction and transformation have been listed.Finally,countermeasures to avoiding surface defects of hypo-peritectic steels duiring continuous casting are summarized.Enlightening certain points in the continuous casting of hypo-peritectic steels and the development of new techniques to overcome the present problems will be a great aid to researchers.展开更多
The micro-characteristics of the streaky marks and the corresponding substrate surface of galvannealed （GA） steel sheets have been investigated using SEM and FIB.The streaky mark area seems to have many cavities,sim...The micro-characteristics of the streaky marks and the corresponding substrate surface of galvannealed （GA） steel sheets have been investigated using SEM and FIB.The streaky mark area seems to have many cavities,similar to craters,which scatter light and make the surface appear darker when compared with the surrounding normal area.Moreover,it is found that the irregularity or difference in steel grain size tends to affect the surface quality of the GA steel sheets.During alloying,the diffusion speed of Zn-Fe on the grain boundary is faster than that at the center of the grain,which results in the selective formation of crater-like morphology in the coating area with larger steel grains.Due to the clear grain boundary of IF steel,apparent streaky marks will be formed on the coating,if the IF steel surface consists of grains of irregular size.展开更多
基金financially supported by the Fundamental Research Funds for the Central Universities(No.FRF-TP-19-017A3)the National Natural Science Foundation of China(No.51874026)。
文摘Hypo-peritectic steels are widely used in various industrial fields because of their high strength,high toughness,high processability,high weldability,and low material cost.However,surface defects are liable to occur during continuous casting,which includes depression,longitudinal cracks,deep oscillation marks,and severe level fluctuation with slag entrapment.The high-efficiency production of hypo-peritectic steels by continuous casting is still a great challenge due to the limited understanding of the mechanism of peritectic solidification.This work reviews the definition and classification of hypo-peritectic steels and introduces the formation tendency of common surface defects related to peritectic solidification.New achievements in the mechanism of peritectic reaction and transformation have been listed.Finally,countermeasures to avoiding surface defects of hypo-peritectic steels duiring continuous casting are summarized.Enlightening certain points in the continuous casting of hypo-peritectic steels and the development of new techniques to overcome the present problems will be a great aid to researchers.
文摘The micro-characteristics of the streaky marks and the corresponding substrate surface of galvannealed （GA） steel sheets have been investigated using SEM and FIB.The streaky mark area seems to have many cavities,similar to craters,which scatter light and make the surface appear darker when compared with the surrounding normal area.Moreover,it is found that the irregularity or difference in steel grain size tends to affect the surface quality of the GA steel sheets.During alloying,the diffusion speed of Zn-Fe on the grain boundary is faster than that at the center of the grain,which results in the selective formation of crater-like morphology in the coating area with larger steel grains.Due to the clear grain boundary of IF steel,apparent streaky marks will be formed on the coating,if the IF steel surface consists of grains of irregular size.