ZnO nanowires（NWs）layers have been synthesized using a two-step chemical solution method on ITO glass substrates coated with ZnO seeds at different immersing times.The structures,morphology and optical properties of...ZnO nanowires（NWs）layers have been synthesized using a two-step chemical solution method on ITO glass substrates coated with ZnO seeds at different immersing times.The structures,morphology and optical properties of the synthesized ZnO NWs have been investigated.The prepared ZnO NWs have an obvious polycrystalline hexangular wurtzite structure and are preferentially oriented along the c-axis（002）.FESEM micrographs showed that the prepared ZnO NWs are close to being vertically grown and more densely at higher immersing times.Poly[2-methoxy-5（2-′-ethyl-hexyloxy）-1,4-phenylenevinylene],MEH-PPV,was used as an active layer to prepare three samples of MEH-PPV/ZnO solar cell based on ZnO NWs that were prepared at different immersing times.A maximum power conversion efficiency of 0.812%was achieved for MEH-PPV/ZnO solar cell prepared at a higher immersing time.The improved efficiency may be attributed to the enhancement of both open-circuit voltage and fill factor.展开更多
A novel unsymmetrical dianhydride containing 4\|(4\|hydroxylphenyl)\|2,3\|phthalazin\|1\|one was synthesized in order to improve the solubility of aromatic polyimides according to the principle of designing new monome...A novel unsymmetrical dianhydride containing 4\|(4\|hydroxylphenyl)\|2,3\|phthalazin\|1\|one was synthesized in order to improve the solubility of aromatic polyimides according to the principle of designing new monomers.This article reported a series of polyimide random copolymers derived from 4,4′ diamino diphenyl sulfone (DAPS),4,4′ oxyl dianiline (ODA) and the new dianhydride\|2 (3,4 dicarboxyl phenyl) 4 (3′,4′ dicarboxyl phenyl oxyl) phenyl 2,3 phthalazine 1 one dianhydride (DAH4) by“one step”solution polycondensation in m cresol with catalystic amount of isoquinoline at 200℃.Some properties of the copolymers were investigated by DSC,TG and mechanical analysis.The result shows that the η inh of copolymers is between 0 64 to 0 71 dL/g in m cresol at 25℃,and the T g of the copolymers are higher than that of pure poliymides containing 4,4′ oxyl dianiline (polymer 5).The relationship between T g and mole percent of DAPS is not obvious.Degradation temperature for 5% weight loss ( T d5 ) of the copolymers occurs all above 470℃ in air.The mechanical properties of the copolymers are lower owing to introducing sulfone groups into polymer’s backbone.In sharp contrast,the copolymers have good solubility and can be easily soluble in 1,1,2,2 tetrachloroethane(TCE), N,N dimethylacetamide(DMAc), N methyl 2 pyrrolidinone (NMP), m cresol and pyridine.Furthermore,the copolymers have better solubility in dimethyl sulfoxide (DMSO) and chloroform than the polyimide derived from DAH4 and ODA.展开更多
文摘ZnO nanowires（NWs）layers have been synthesized using a two-step chemical solution method on ITO glass substrates coated with ZnO seeds at different immersing times.The structures,morphology and optical properties of the synthesized ZnO NWs have been investigated.The prepared ZnO NWs have an obvious polycrystalline hexangular wurtzite structure and are preferentially oriented along the c-axis（002）.FESEM micrographs showed that the prepared ZnO NWs are close to being vertically grown and more densely at higher immersing times.Poly[2-methoxy-5（2-′-ethyl-hexyloxy）-1,4-phenylenevinylene],MEH-PPV,was used as an active layer to prepare three samples of MEH-PPV/ZnO solar cell based on ZnO NWs that were prepared at different immersing times.A maximum power conversion efficiency of 0.812%was achieved for MEH-PPV/ZnO solar cell prepared at a higher immersing time.The improved efficiency may be attributed to the enhancement of both open-circuit voltage and fill factor.
文摘A novel unsymmetrical dianhydride containing 4\|(4\|hydroxylphenyl)\|2,3\|phthalazin\|1\|one was synthesized in order to improve the solubility of aromatic polyimides according to the principle of designing new monomers.This article reported a series of polyimide random copolymers derived from 4,4′ diamino diphenyl sulfone (DAPS),4,4′ oxyl dianiline (ODA) and the new dianhydride\|2 (3,4 dicarboxyl phenyl) 4 (3′,4′ dicarboxyl phenyl oxyl) phenyl 2,3 phthalazine 1 one dianhydride (DAH4) by“one step”solution polycondensation in m cresol with catalystic amount of isoquinoline at 200℃.Some properties of the copolymers were investigated by DSC,TG and mechanical analysis.The result shows that the η inh of copolymers is between 0 64 to 0 71 dL/g in m cresol at 25℃,and the T g of the copolymers are higher than that of pure poliymides containing 4,4′ oxyl dianiline (polymer 5).The relationship between T g and mole percent of DAPS is not obvious.Degradation temperature for 5% weight loss ( T d5 ) of the copolymers occurs all above 470℃ in air.The mechanical properties of the copolymers are lower owing to introducing sulfone groups into polymer’s backbone.In sharp contrast,the copolymers have good solubility and can be easily soluble in 1,1,2,2 tetrachloroethane(TCE), N,N dimethylacetamide(DMAc), N methyl 2 pyrrolidinone (NMP), m cresol and pyridine.Furthermore,the copolymers have better solubility in dimethyl sulfoxide (DMSO) and chloroform than the polyimide derived from DAH4 and ODA.