Cu/Al clad strips are prepared using solid?liquid cast-rolling bonding(SLCRB)technique with a d160mm×150mm twin-roll experimental caster.The extent of interfacial reactions,composition of the reaction products,an...Cu/Al clad strips are prepared using solid?liquid cast-rolling bonding(SLCRB)technique with a d160mm×150mm twin-roll experimental caster.The extent of interfacial reactions,composition of the reaction products,and their micro-morphology evolution in the SLCRB process are investigated with scanning electron microscope(SEM),energy dispersive spectrometer(EDS),and X-ray diffraction(XRD).In the casting pool,initial aluminized coating is first generated on the copper strip surface,with the diffusion layer mainly consisting ofα(Al)+CuAl2and growing at high temperatures,with the maximum thickness of10μm.After sequent rolling below the kiss point,the diffusion layer is broken by severe elongation,which leads to an additional crack bond process with a fresh interface of virgin base metal.The average thickness is reduced from10to5μm.The reaction products,CuAl2,CuAl,and Cu9Al4,are dispersed along the rolling direction.Peeling and bending test results indicate that the fracture occurs in the aluminum substrate,and the morphology is a dimple pattern.No crack or separation is found at the bonding interface after90°-180°bending.The presented method provides an economical way to fabricate Cu/Al clad strip directly.展开更多
Based on twin-roll casting, a cast-rolling force model was proposed to predict the rolling force in the bimetal solid-liquid cast-rolling bonding(SLCRB) process. The solid-liquid bonding zone was assumed to be below t...Based on twin-roll casting, a cast-rolling force model was proposed to predict the rolling force in the bimetal solid-liquid cast-rolling bonding(SLCRB) process. The solid-liquid bonding zone was assumed to be below the kiss point(KP). The deformation resistance of the liquid zone was ignored. Then, the calculation model was derived. A 2D thermal-flow coupled simulation was established to provide a basis for the parameters in the model, and then the rolling forces of the Cu/Al clad strip at different rolling speeds were calculated. Meanwhile, through measurement experiments, the accuracy of the model was verified. The influence of the rolling speed, the substrate strip thickness, and the material on the rolling force was obtained. The results indicate that the rolling force decreases with the increase of the rolling speed and increases with the increase of the thickness and thermal conductivity of the substrate strip. The rolling force is closely related to the KP height. Therefore, the formulation of reasonable process parameters to control the KP height is of great significance to the stability of cast-rolling forming.展开更多
Based on twin-roll casting technology and multi-roll groove rolling technology,a Multi-Roll Solid-Liquid Cast-Rolling Bonding(MRSLCRB)process was proposed to fabricate Cu/steel cladding bars,which processes the advant...Based on twin-roll casting technology and multi-roll groove rolling technology,a Multi-Roll Solid-Liquid Cast-Rolling Bonding(MRSLCRB)process was proposed to fabricate Cu/steel cladding bars,which processes the advantages of short flow and high-efficiency.However,it is a typical 3-D thermal-fluid-mechanics coupled problem,and determining cast-rolling force is difficult during the equipment design.Therefore,the geometrical evolution of the cast-rolling area was studied,laying the foundation to establish contact boundary equations and analyze mechanical schematics and metal flow.Then,a 3-D steady-state thermal-fluid coupled simulation model,including casting roll,substrate bar,and cladding metal,was established.The Kissing Point(KP)height,average outlet temperature,and process window were predicted,and simulation results of the three-roll layout indicate that the KP distribution along the circumferential direction can be considered uniform.Hence,the engineering cast-rolling force model was derived based on the differential element method and plane deformation hypothesis.The accuracy was verified by the 3-D finite element model,and the influences of process layouts and technological parameters on the castrolling force were analyzed.Through the indirect multi-field coupled analysis method,the temperature–pressure evolution and reasonable process window can be predicted,which provides a significant basis for guiding equipment design and improving product quality.展开更多
基金Project(51474189)supported by the National Natural Science Foundation of ChinaProject(QN2015214)supported by the Educational Commission of Hebei Province,China
文摘Cu/Al clad strips are prepared using solid?liquid cast-rolling bonding(SLCRB)technique with a d160mm×150mm twin-roll experimental caster.The extent of interfacial reactions,composition of the reaction products,and their micro-morphology evolution in the SLCRB process are investigated with scanning electron microscope(SEM),energy dispersive spectrometer(EDS),and X-ray diffraction(XRD).In the casting pool,initial aluminized coating is first generated on the copper strip surface,with the diffusion layer mainly consisting ofα(Al)+CuAl2and growing at high temperatures,with the maximum thickness of10μm.After sequent rolling below the kiss point,the diffusion layer is broken by severe elongation,which leads to an additional crack bond process with a fresh interface of virgin base metal.The average thickness is reduced from10to5μm.The reaction products,CuAl2,CuAl,and Cu9Al4,are dispersed along the rolling direction.Peeling and bending test results indicate that the fracture occurs in the aluminum substrate,and the morphology is a dimple pattern.No crack or separation is found at the bonding interface after90°-180°bending.The presented method provides an economical way to fabricate Cu/Al clad strip directly.
基金The authors are grateful for the financial supports from the National Natural Science Foundation of China(51974278)the Distinguished Young Fund of Natural Science Foundation of Hebei Province,China(E2018203446).
文摘Based on twin-roll casting, a cast-rolling force model was proposed to predict the rolling force in the bimetal solid-liquid cast-rolling bonding(SLCRB) process. The solid-liquid bonding zone was assumed to be below the kiss point(KP). The deformation resistance of the liquid zone was ignored. Then, the calculation model was derived. A 2D thermal-flow coupled simulation was established to provide a basis for the parameters in the model, and then the rolling forces of the Cu/Al clad strip at different rolling speeds were calculated. Meanwhile, through measurement experiments, the accuracy of the model was verified. The influence of the rolling speed, the substrate strip thickness, and the material on the rolling force was obtained. The results indicate that the rolling force decreases with the increase of the rolling speed and increases with the increase of the thickness and thermal conductivity of the substrate strip. The rolling force is closely related to the KP height. Therefore, the formulation of reasonable process parameters to control the KP height is of great significance to the stability of cast-rolling forming.
基金This study was co-supported by the National Key Research and Development Program,China(No.2018YFA0707300)the National Natural Science Foundation of China(Nos.51974278 and 52205406)+2 种基金China Post Doctoral Science Foundation(No.2023M732572)the Key Science and Technology Project of Shanxi Province,China(No.20191102009)the Fundamental Research Program of Shanxi Province,China(No.202203021212289).
文摘Based on twin-roll casting technology and multi-roll groove rolling technology,a Multi-Roll Solid-Liquid Cast-Rolling Bonding(MRSLCRB)process was proposed to fabricate Cu/steel cladding bars,which processes the advantages of short flow and high-efficiency.However,it is a typical 3-D thermal-fluid-mechanics coupled problem,and determining cast-rolling force is difficult during the equipment design.Therefore,the geometrical evolution of the cast-rolling area was studied,laying the foundation to establish contact boundary equations and analyze mechanical schematics and metal flow.Then,a 3-D steady-state thermal-fluid coupled simulation model,including casting roll,substrate bar,and cladding metal,was established.The Kissing Point(KP)height,average outlet temperature,and process window were predicted,and simulation results of the three-roll layout indicate that the KP distribution along the circumferential direction can be considered uniform.Hence,the engineering cast-rolling force model was derived based on the differential element method and plane deformation hypothesis.The accuracy was verified by the 3-D finite element model,and the influences of process layouts and technological parameters on the castrolling force were analyzed.Through the indirect multi-field coupled analysis method,the temperature–pressure evolution and reasonable process window can be predicted,which provides a significant basis for guiding equipment design and improving product quality.