通过考察水与表面活性剂的摩尔比(R),TEOS的量、氨水的量及包壳次数对基于Triton X 100/环已烷/正已醇/水反相微乳液体系制备二氧化硅纳米颗粒尺寸的影响,开展了基于反相微乳液法的尺寸可控性二氧化硅纳米颗粒制备研究.结果表明:在其他...通过考察水与表面活性剂的摩尔比(R),TEOS的量、氨水的量及包壳次数对基于Triton X 100/环已烷/正已醇/水反相微乳液体系制备二氧化硅纳米颗粒尺寸的影响,开展了基于反相微乳液法的尺寸可控性二氧化硅纳米颗粒制备研究.结果表明:在其他参数都恒定的情况下,通过改变微乳液体系中上述某一组分的量,可以在一定程度上实现二氧化硅纳米颗粒的尺寸可控性合成.首先,水与表面活性剂的摩尔比(R)对二氧化硅纳米颗粒的尺寸影响最大,随着R值的增大,颗粒的粒径逐渐减小,当R值达到18时,二氧化硅纳米颗粒的形貌变得不再是很规则的球形结构,并且分散性降低,团聚现象明显;其次是氨水的量,随着氨水量的增多,颗粒的粒径先减小,之后不再发生明显变化;另外随着包壳次数的增多,颗粒的粒径随之增大,并且颗粒之间的分散性也有所提高;但是TEOS的量对颗粒粒径的影响不明显.展开更多
Size-controlled synthesis of two-dimensional(2D)catalysts with low stacking numbers and small nanoflake lengths is crucial for promoting the catalytic performance in diverse heterogeneous catalysis.Herein,we report a ...Size-controlled synthesis of two-dimensional(2D)catalysts with low stacking numbers and small nanoflake lengths is crucial for promoting the catalytic performance in diverse heterogeneous catalysis.Herein,we report a facile and general“surface curvature-confined synthesis”strategy to modulate the slab lengths and stacking numbers of 2D transition metal sulfides by controlling the strain induced by different surface curvature of supports.An efficient NiMo sulfide with shorter slab length(average 3.71 nm),less stacking number(1–2 layers)and more edge active sites is synthesized onto ZSM-5 zeolites with the average size of 100 nm,which shows superior kHDS value of dibenzothiophene(14.05×10^−7 mol/(g·s)),enhanced stability up to 80 h,and high direct desulfurization selectivity(>95%).This design concept is also proved to be generally applicable to modulate the slab lengths and stacking numbers of other 2D catalysts such as MoS2 and WS2 nanoflakes,which shows great potentials for developing more ultrasmall 2D catalysts with controlled sizes and excellent catalytic activities.展开更多
文摘通过考察水与表面活性剂的摩尔比(R),TEOS的量、氨水的量及包壳次数对基于Triton X 100/环已烷/正已醇/水反相微乳液体系制备二氧化硅纳米颗粒尺寸的影响,开展了基于反相微乳液法的尺寸可控性二氧化硅纳米颗粒制备研究.结果表明:在其他参数都恒定的情况下,通过改变微乳液体系中上述某一组分的量,可以在一定程度上实现二氧化硅纳米颗粒的尺寸可控性合成.首先,水与表面活性剂的摩尔比(R)对二氧化硅纳米颗粒的尺寸影响最大,随着R值的增大,颗粒的粒径逐渐减小,当R值达到18时,二氧化硅纳米颗粒的形貌变得不再是很规则的球形结构,并且分散性降低,团聚现象明显;其次是氨水的量,随着氨水量的增多,颗粒的粒径先减小,之后不再发生明显变化;另外随着包壳次数的增多,颗粒的粒径随之增大,并且颗粒之间的分散性也有所提高;但是TEOS的量对颗粒粒径的影响不明显.
基金This work was supported by the National Key R&D Program of China(No.2018YFE0201704)the National Natural Science Foundation of China(Nos.21631004,21801069,21571054,and 21901064)+2 种基金the Fundamental Research Funds for Central Universities(Nos.3072019CFJ1502 and RCYJTD201801)the University Program for Young Scholars with Creative Talents in Heilongjiang Province(No.UNPYSCT-2018013)Heilongjiang Provincial Postdoctoral Science Foundation(No.LBH-Z18232)and the Heilongjiang University Excellent Youth Foundation.
文摘Size-controlled synthesis of two-dimensional(2D)catalysts with low stacking numbers and small nanoflake lengths is crucial for promoting the catalytic performance in diverse heterogeneous catalysis.Herein,we report a facile and general“surface curvature-confined synthesis”strategy to modulate the slab lengths and stacking numbers of 2D transition metal sulfides by controlling the strain induced by different surface curvature of supports.An efficient NiMo sulfide with shorter slab length(average 3.71 nm),less stacking number(1–2 layers)and more edge active sites is synthesized onto ZSM-5 zeolites with the average size of 100 nm,which shows superior kHDS value of dibenzothiophene(14.05×10^−7 mol/(g·s)),enhanced stability up to 80 h,and high direct desulfurization selectivity(>95%).This design concept is also proved to be generally applicable to modulate the slab lengths and stacking numbers of other 2D catalysts such as MoS2 and WS2 nanoflakes,which shows great potentials for developing more ultrasmall 2D catalysts with controlled sizes and excellent catalytic activities.