Binary metal oxide（MnOx-A/TiO2）catalysts were prepared by adding the second metal to manganese oxides supported on titanium dioxide（TiO2）,where,A indicates Fe2O3,WO3,MoO3,and Cr2O3.Their catalytic activity,N2 sele...Binary metal oxide（MnOx-A/TiO2）catalysts were prepared by adding the second metal to manganese oxides supported on titanium dioxide（TiO2）,where,A indicates Fe2O3,WO3,MoO3,and Cr2O3.Their catalytic activity,N2 selectivity,and SO2 poisonous tolerance were investigated.The catalytic performance at low temperatures decreased in the following order：Mn-W/TiO2〉Mn-Fe/TiO2〉Mn-Cr/TiO2〉Mn-Mo/TiO2,whereas the N2 selectivity decreased in the order：Mn-Fe/TiO2〉Mn-W/TiO2〉Mn-Mo/TiO2〉Mn-Cr/TiO2.In the presence of 0.01%SO2 and 6%H2O,the NOx conversions in the presence of Mn-W/TiO2,Mn-Fe/TiO2,or Mn-Mo/TiO2 maintain 98.5%,95.8%and 94.2%, respectively,after 8 h at 120°C at GHSV 12600 h？ 1 .As effective promoters,WO3 and Fe2O3 can increase N2 selectivity and the resistance to SO2 of MnOx/TiO2 significantly.The Fourier transform infrared（FTIR）spectra of NH3 over WO3 show the presence of Lewis acid sites.The results suggest that WO3 is the best promoter of MnOx/TiO2,and Mn-W/TiO2 is one of the most active catalysts for the low temperature selective catalytic reduction of NO with NH3.展开更多
文摘Binary metal oxide（MnOx-A/TiO2）catalysts were prepared by adding the second metal to manganese oxides supported on titanium dioxide（TiO2）,where,A indicates Fe2O3,WO3,MoO3,and Cr2O3.Their catalytic activity,N2 selectivity,and SO2 poisonous tolerance were investigated.The catalytic performance at low temperatures decreased in the following order：Mn-W/TiO2〉Mn-Fe/TiO2〉Mn-Cr/TiO2〉Mn-Mo/TiO2,whereas the N2 selectivity decreased in the order：Mn-Fe/TiO2〉Mn-W/TiO2〉Mn-Mo/TiO2〉Mn-Cr/TiO2.In the presence of 0.01%SO2 and 6%H2O,the NOx conversions in the presence of Mn-W/TiO2,Mn-Fe/TiO2,or Mn-Mo/TiO2 maintain 98.5%,95.8%and 94.2%, respectively,after 8 h at 120°C at GHSV 12600 h？ 1 .As effective promoters,WO3 and Fe2O3 can increase N2 selectivity and the resistance to SO2 of MnOx/TiO2 significantly.The Fourier transform infrared（FTIR）spectra of NH3 over WO3 show the presence of Lewis acid sites.The results suggest that WO3 is the best promoter of MnOx/TiO2,and Mn-W/TiO2 is one of the most active catalysts for the low temperature selective catalytic reduction of NO with NH3.
文摘研究了Mn-W/TiO2用于NH3选择性催化还原NOx体系的催化反应性能,探索了不同温度条件下该催化剂对抗不同SO2浓度的抗毒性能。结果显示WO3能够增加活性酸中心的数量和酸性,是MnOx/TiO2非常有效的助催化剂。在气体体积空速(gaseous hourly space velocity,GHSV)为18900h-1时100～350℃范围内,Mn-W/TiO2催化剂还原NOx的转化率高达80.3%～99.6%,N2选择性达100%～98.7%。当反应气中有0.01%SO2和6%H2O时,120℃NOx转化率可维持在98.5%,当SO2浓度超过0.01%时,则需将反应温度升高到250℃以上才可消除其干扰,而当SO2浓度高达0.07%时,300℃下转化率可长期维持在99%,达到了商用V-W/TiO2催化剂的水平。对于NH3选择性还原NOx体系Mn-W/TiO2显示了极好的催化性能,是目前抗SO2毒性最强的催化剂之一。试验发现,低温条件下,SO2对Mn-W/TiO2催化剂的影响是可逆的,随着反应温度的提高,活性将自然恢复。