The effect of quenching rate on the electrical conductivity and microstructure of thick plates of incumbent AA7050 was investigated by employing Jominy end quench test. The electrical conductivity measurement and micr...The effect of quenching rate on the electrical conductivity and microstructure of thick plates of incumbent AA7050 was investigated by employing Jominy end quench test. The electrical conductivity measurement and microstructural observation were conducted at different distances from the quenched end. The results indicate that the average cooling rates decrease with increasing the distance from the quenched end of the bar in the quench sensitive temperature range. However, the electrical conductivity increases with the increase of distance from the quenched end. The surface parts of the plate were fully recrystallized, while partial recrystallization took place at the quarter and center parts of the plate. The quench induced grain boundary precipitates became remarkably coarser and discontinuously distributed with increasing distance from the quenched end of the bar. Plenty of heterogeneous precipitates were observed to nucleate on A13Zr dispersoids when the distance from the quenched end was greater than 38mm.展开更多
The microstructure of an alloy is affected intensively by the cooling process.To figure out the inherent relation between the cooling rate and microstructure of an advanced nickel-based superalloy,experimental and num...The microstructure of an alloy is affected intensively by the cooling process.To figure out the inherent relation between the cooling rate and microstructure of an advanced nickel-based superalloy,experimental and numerical studies on the cooling process were conducted.Specifically,the measurement was performed concerning both the temperature of the specimen during the end-quench test and the size of the secondaryγ′phase of the specimen after that.The heat transfer coefficient of the quenched surface was determined by the inverse heat transfer method for simulation.The results show that the cooling rate of the quenched surface exceeds 1574 K/min.Based on the averaged cooling rate obtained from the simulation and the measured size of the secondaryγ′phase,an empirical correlation in a double logarithmic relationship between them is proposed.The relationship is verified by the experiment with specified cooling rates.展开更多
The quench sensitivity of 6351 alloy was determined by the time temperature-transformation（TTT） curves and time temperature-property（TTP） curves by an interrupted quench technique with measurement of as-aged hardn...The quench sensitivity of 6351 alloy was determined by the time temperature-transformation（TTT） curves and time temperature-property（TTP） curves by an interrupted quench technique with measurement of as-aged hardness and as-quenched electro-conductivity.The microstructure transformation during isothermal treatment was studied by the transmission electron microscopy（TEM） and Avrami equation.The results showed that the electro-conductivity of the 6351 alloy increased and the hardness decreased with prolonging the holding time at a certain isothermal temperature.The TEM observation indicated that the supersaturated solid solution decomposed and needles β″ precipitated at the initial stage of isothermal holding.With the prolongation of holding time at the nose temperature,rod β＇ and plate β phases formed.The isothermal transformation rate at 360℃ was the fastest,and became slow at 280℃ and reached the slowest at 440℃.The nose temperatures of the TTT and TTP curves were about 360℃ and the high quench sensitive temperature range was 230 430℃.The quench factor analysis indicated that the cooling rate should be more than 15℃/s in the quench sensitive areas in order to get optimal mechanical properties.展开更多
针对我国国产反应堆严重事故分析程序的发展需要,西安交通大学开发了一体化严重事故分析程序(modular severe accident analysis program,MOSAP)。为了验证MOSAP程序在再淹没期间相关模型的合理性和准确性,以QUENCH-06实验为例,利用MOSA...针对我国国产反应堆严重事故分析程序的发展需要,西安交通大学开发了一体化严重事故分析程序(modular severe accident analysis program,MOSAP)。为了验证MOSAP程序在再淹没期间相关模型的合理性和准确性,以QUENCH-06实验为例,利用MOSAP程序对实验进行建模,并将MOSAP程序的计算结果与实验结果以及国际通用程序的计算结果进行了对比。结果表明,对于包壳轴向温度、包壳氧化层厚度和氢气产量,MOSAP程序计算结果与实验值和国际通用程序计算结果符合良好。在计算包壳轴向温度和氧化层厚度方面,MOSAP程序计算结果优于国际通用程序计算结果。文中结论对MOSAP程序堆内模块验证和整个模块的验证具有一定的参考意义。展开更多
基金Project (50904010) supported by the National Natural Science Foundation of ChinaProject (2010DFB50340) supported by the China International Science and Technology Cooperation
文摘The effect of quenching rate on the electrical conductivity and microstructure of thick plates of incumbent AA7050 was investigated by employing Jominy end quench test. The electrical conductivity measurement and microstructural observation were conducted at different distances from the quenched end. The results indicate that the average cooling rates decrease with increasing the distance from the quenched end of the bar in the quench sensitive temperature range. However, the electrical conductivity increases with the increase of distance from the quenched end. The surface parts of the plate were fully recrystallized, while partial recrystallization took place at the quarter and center parts of the plate. The quench induced grain boundary precipitates became remarkably coarser and discontinuously distributed with increasing distance from the quenched end of the bar. Plenty of heterogeneous precipitates were observed to nucleate on A13Zr dispersoids when the distance from the quenched end was greater than 38mm.
基金Project(2016YFB0700300) supported by the National Key Research and Development Program of ChinaProject(2019zzts262) supported by the Postgraduate Independent Exploration and Innovation Program of Central South University,China
文摘The microstructure of an alloy is affected intensively by the cooling process.To figure out the inherent relation between the cooling rate and microstructure of an advanced nickel-based superalloy,experimental and numerical studies on the cooling process were conducted.Specifically,the measurement was performed concerning both the temperature of the specimen during the end-quench test and the size of the secondaryγ′phase of the specimen after that.The heat transfer coefficient of the quenched surface was determined by the inverse heat transfer method for simulation.The results show that the cooling rate of the quenched surface exceeds 1574 K/min.Based on the averaged cooling rate obtained from the simulation and the measured size of the secondaryγ′phase,an empirical correlation in a double logarithmic relationship between them is proposed.The relationship is verified by the experiment with specified cooling rates.
基金Project(2012M511552) supported by China Postdoctoral Science FoundationProject(2009A080205001) supported by the State Key Fundamental Research Program of China
文摘The quench sensitivity of 6351 alloy was determined by the time temperature-transformation（TTT） curves and time temperature-property（TTP） curves by an interrupted quench technique with measurement of as-aged hardness and as-quenched electro-conductivity.The microstructure transformation during isothermal treatment was studied by the transmission electron microscopy（TEM） and Avrami equation.The results showed that the electro-conductivity of the 6351 alloy increased and the hardness decreased with prolonging the holding time at a certain isothermal temperature.The TEM observation indicated that the supersaturated solid solution decomposed and needles β″ precipitated at the initial stage of isothermal holding.With the prolongation of holding time at the nose temperature,rod β＇ and plate β phases formed.The isothermal transformation rate at 360℃ was the fastest,and became slow at 280℃ and reached the slowest at 440℃.The nose temperatures of the TTT and TTP curves were about 360℃ and the high quench sensitive temperature range was 230 430℃.The quench factor analysis indicated that the cooling rate should be more than 15℃/s in the quench sensitive areas in order to get optimal mechanical properties.
文摘针对我国国产反应堆严重事故分析程序的发展需要,西安交通大学开发了一体化严重事故分析程序(modular severe accident analysis program,MOSAP)。为了验证MOSAP程序在再淹没期间相关模型的合理性和准确性,以QUENCH-06实验为例,利用MOSAP程序对实验进行建模,并将MOSAP程序的计算结果与实验结果以及国际通用程序的计算结果进行了对比。结果表明,对于包壳轴向温度、包壳氧化层厚度和氢气产量,MOSAP程序计算结果与实验值和国际通用程序计算结果符合良好。在计算包壳轴向温度和氧化层厚度方面,MOSAP程序计算结果优于国际通用程序计算结果。文中结论对MOSAP程序堆内模块验证和整个模块的验证具有一定的参考意义。