Primary dendrite arm spacing（PDAS） of α phase in directionally solidified Pb-26%Bi（mass fraction） hypo-peritectic alloys was measured by considering the effect of melt convection in cylindrical samples with diffe...Primary dendrite arm spacing（PDAS） of α phase in directionally solidified Pb-26%Bi（mass fraction） hypo-peritectic alloys was measured by considering the effect of melt convection in cylindrical samples with different diameters.The experimental results show the measured PDAS increases with increasing diameter of the sample.At the growth velocity of 5 μm/s,its value changes from 161.5 μm for the sample with 1.8 mm in diameter to 240.4 μm for the sample with 7 mm in diameter.The strong melt convection in large diameter samples causes a high bulk alloy composition and a high concentration gradient in peritectic β phase,resulting in a larger PDAS.Simultaneously,the high concentration gradient could effectively promote the peritectic transformation,enhancing the dissolution of the thin α dendrite.展开更多
The primary dendrite morphology and spacing of DZ125 superalloy have been observed during directional solidification under high thermal gradient about 500 K/cm. The results reveal that the primary dendrite arm spacing...The primary dendrite morphology and spacing of DZ125 superalloy have been observed during directional solidification under high thermal gradient about 500 K/cm. The results reveal that the primary dendrite arm spacing decreases from 94 μm to 35.8 μm with the increase of directional solidification cooling rate from 2.525 K/s to 36.4 K/s. The regression equation of the primary dendrite arm spacings A, versus cooling rate is λ1=0.013（GV）-0.32. The predictions of Kurz/Fisher model and Hunt/Lu model accord reasonably well with the experimental data. The influence of directional solidification rate under variable thermal gradient on the primary dendrite arm spacing has also been investigated.展开更多
Primary dendritic arm spacing(PDAS)is an important microstructure feature of the nickel-base single crystal superalloys.In this paper,a numerical model predicting the PDAS evolution with additive manufacturing paramet...Primary dendritic arm spacing(PDAS)is an important microstructure feature of the nickel-base single crystal superalloys.In this paper,a numerical model predicting the PDAS evolution with additive manufacturing parameters using pulsed laser is established,which combines the theoretical PDAS models with the temperature field calculation model during pulsed laser process.Based on this model,processing maps that related process parameters to the evolution of PDAS are generated.To obtain more accurate prediction model,the parameters of different solidification conditions,G^(-0.5)V^(-0.25) and G^(-0.5)V^(-0.25),are selected to calculate PDAS.The simulation results show that the PDAS increases as the arise of P and t.The processmgPDAS map can accurately predict the evolution of PDAS with pulsed laser process parameters,which is well in accordance with the experimental results.Additionally,the PDAS values calculated by the G^(-0.5)V^(-0.25) are more in line with the experimental results than those calculated by the G^(-0.5)V^(-0.25).展开更多
Al-4.5wt.%Cu alloy has been directionally solidified at constant and abruptly changing withdrawal rates, respectively. The effects of the withdrawal rate on solidification microstructure, primary dendrite arm spacing(...Al-4.5wt.%Cu alloy has been directionally solidified at constant and abruptly changing withdrawal rates, respectively. The effects of the withdrawal rate on solidification microstructure, primary dendrite arm spacing(PDAS) and liquid solute distribution in front of the solid-liquid interface were investigated. The experimental results for the PDAS at a constant withdrawal rate agree well with the values calculated by the Hunt, Trivedi and Hunt-Lu models. At an abrupt change in the withdrawal rate, the maximum to minimum ratio of the PDAS at a given solidification parameter, i.e. λ1max/λ1min, is more than 2, and the PDAS values are remarkably history-dependent. Further, the liquid-solute distribution curve based on theoretical calculation shows that the larger the initial withdrawal rate is, the smaller the minimum of liquid solute concentration in front of the solid-liquid interface is after the abrupt change in withdrawal rate.展开更多
基金Project(50395100)supported by the National Natural Science Foundation of ChinaProject(NCET-07-0692)supported by the New Century Talents Program of the Ministry of Education,ChinaProject(34-TP-2009)supported by Open Project of State Key Laboratory of Solidification Processing,China
文摘Primary dendrite arm spacing（PDAS） of α phase in directionally solidified Pb-26%Bi（mass fraction） hypo-peritectic alloys was measured by considering the effect of melt convection in cylindrical samples with different diameters.The experimental results show the measured PDAS increases with increasing diameter of the sample.At the growth velocity of 5 μm/s,its value changes from 161.5 μm for the sample with 1.8 mm in diameter to 240.4 μm for the sample with 7 mm in diameter.The strong melt convection in large diameter samples causes a high bulk alloy composition and a high concentration gradient in peritectic β phase,resulting in a larger PDAS.Simultaneously,the high concentration gradient could effectively promote the peritectic transformation,enhancing the dissolution of the thin α dendrite.
基金supported by the National Natural Science Foundation of China(50771081,50827102)the National Basic Research Program of China(2006CB605202)
文摘The primary dendrite morphology and spacing of DZ125 superalloy have been observed during directional solidification under high thermal gradient about 500 K/cm. The results reveal that the primary dendrite arm spacing decreases from 94 μm to 35.8 μm with the increase of directional solidification cooling rate from 2.525 K/s to 36.4 K/s. The regression equation of the primary dendrite arm spacings A, versus cooling rate is λ1=0.013（GV）-0.32. The predictions of Kurz/Fisher model and Hunt/Lu model accord reasonably well with the experimental data. The influence of directional solidification rate under variable thermal gradient on the primary dendrite arm spacing has also been investigated.
基金financially supported by the National Key R&D Program of China(No.2017YFB1103800)the National Key R&D Program of China(Nos.2017YFA0700703,2018YFB1106000)+2 种基金the National Natural Science Foundation of China(NSFC)(Nos.51771190,51671189,U1508213)the National High Technology Research and Development Program(863)(No.2014AA041701)the fund of the State Key Laboratory of Solidifi cation Processing in NWPU(No.SKLSP201834)。
文摘Primary dendritic arm spacing(PDAS)is an important microstructure feature of the nickel-base single crystal superalloys.In this paper,a numerical model predicting the PDAS evolution with additive manufacturing parameters using pulsed laser is established,which combines the theoretical PDAS models with the temperature field calculation model during pulsed laser process.Based on this model,processing maps that related process parameters to the evolution of PDAS are generated.To obtain more accurate prediction model,the parameters of different solidification conditions,G^(-0.5)V^(-0.25) and G^(-0.5)V^(-0.25),are selected to calculate PDAS.The simulation results show that the PDAS increases as the arise of P and t.The processmgPDAS map can accurately predict the evolution of PDAS with pulsed laser process parameters,which is well in accordance with the experimental results.Additionally,the PDAS values calculated by the G^(-0.5)V^(-0.25) are more in line with the experimental results than those calculated by the G^(-0.5)V^(-0.25).
基金financially supported by the National Natural Science Foundation of China(No.50971101)the Specialized Research Fund for the Doctoral Program of Higher Education(No.20136102110014)
文摘Al-4.5wt.%Cu alloy has been directionally solidified at constant and abruptly changing withdrawal rates, respectively. The effects of the withdrawal rate on solidification microstructure, primary dendrite arm spacing(PDAS) and liquid solute distribution in front of the solid-liquid interface were investigated. The experimental results for the PDAS at a constant withdrawal rate agree well with the values calculated by the Hunt, Trivedi and Hunt-Lu models. At an abrupt change in the withdrawal rate, the maximum to minimum ratio of the PDAS at a given solidification parameter, i.e. λ1max/λ1min, is more than 2, and the PDAS values are remarkably history-dependent. Further, the liquid-solute distribution curve based on theoretical calculation shows that the larger the initial withdrawal rate is, the smaller the minimum of liquid solute concentration in front of the solid-liquid interface is after the abrupt change in withdrawal rate.