The powders of the AA 7075-ZRO2 were mixed by mechanical milling, but it was found that the system presents a few disadvantages when processed by conventional sintering and hot extrusion, since intermetallic phases be...The powders of the AA 7075-ZRO2 were mixed by mechanical milling, but it was found that the system presents a few disadvantages when processed by conventional sintering and hot extrusion, since intermetallic phases between ZrO2 particles and alloying elements were formed. Equal channel angular pressing （ECAP） processing was proposed as an alternative method to consolidate the composite where there is no intermetallic formation. The analysis of the ECAP process showed that the intermediate temperature （220℃） produced a higher consolidation level than conventional sintering and hot extrusion （400 and 500℃, respectively）. This fact was supported by relative density analysis. In the case of the sintered and hot-extruded sample, the relative density exhibited a value of 0.95, while ECAP sample showed a value of 0.98. Hardness values show that microstructural refinement obtained during mechanical milling was preserved during ECAP processing even when it was carded out at 220℃.展开更多
基金supported by Universidad Autónoma de San Luis Potosi, Centro de Investigación en Materiales Avanzados Unidad Chihuahua and Universitat Politècnica de CatalunyaFinancial support by CONACYT is appreciatedfinancial support from FAI-UASLP under the project CI5-FAI-04-45.45
文摘The powders of the AA 7075-ZRO2 were mixed by mechanical milling, but it was found that the system presents a few disadvantages when processed by conventional sintering and hot extrusion, since intermetallic phases between ZrO2 particles and alloying elements were formed. Equal channel angular pressing （ECAP） processing was proposed as an alternative method to consolidate the composite where there is no intermetallic formation. The analysis of the ECAP process showed that the intermediate temperature （220℃） produced a higher consolidation level than conventional sintering and hot extrusion （400 and 500℃, respectively）. This fact was supported by relative density analysis. In the case of the sintered and hot-extruded sample, the relative density exhibited a value of 0.95, while ECAP sample showed a value of 0.98. Hardness values show that microstructural refinement obtained during mechanical milling was preserved during ECAP processing even when it was carded out at 220℃.
基金supported partially by the Australian Research Council with the ARC Centre of excellence for Design in Light Metals and partially by the Defence Materials Technology Centre