Potentiodynamic polarization measurement was used to investigate the effects of temperature, dissolved ox- ygen concentration and pH on the electrochemical behavior of X70 pipeline steel in simulated solution accordin...Potentiodynamic polarization measurement was used to investigate the effects of temperature, dissolved ox- ygen concentration and pH on the electrochemical behavior of X70 pipeline steel in simulated solution according to the orthogonal testing method. The results showed that temperature, dissolved oxygen concentration and pH had great influence on corrosion current density （icorr） of X70 steel. Corrosion current density of X70 steel was most influenced by dissolved oxygen concentration in simulated solution. The corrosion degree of X70 steel was the least under the environment of low temperature, deficient oxygen and weak acid.展开更多
The corrosion behavior of a weathering steel SPA-C and two acid resistance steels（ S-TEN1 and ND）in sulfuric acid solution was investigated by using potentiodynamic polarization and weight loss measurement technique...The corrosion behavior of a weathering steel SPA-C and two acid resistance steels（ S-TEN1 and ND）in sulfuric acid solution was investigated by using potentiodynamic polarization and weight loss measurement techniques. Both potentiodynamic polarization and weight loss measurement tests indicated that corrosion resistance of these three alloy steels was as follows： ND ~ S-TEN1 〉 SPA-C. Surface analysis of the corroded samples conducted after the immersion test indicated that two layers were formed on the substrates, with the outer layer comprising FeSO4. H20 and the inner layer mainly comprising iron oxides. The addition of Cu, Cr, and Sb refined the corrosion products and improved the adhesion ability between the rust layer and the substrate.展开更多
基金Item Sponsored by National Science and Technology Infrastructure Platforms Construction Projects of China (2005DKA10400)National Science and Technology Support 11th Five-Year Plan of China(2006BAK02B01)
文摘Potentiodynamic polarization measurement was used to investigate the effects of temperature, dissolved ox- ygen concentration and pH on the electrochemical behavior of X70 pipeline steel in simulated solution according to the orthogonal testing method. The results showed that temperature, dissolved oxygen concentration and pH had great influence on corrosion current density （icorr） of X70 steel. Corrosion current density of X70 steel was most influenced by dissolved oxygen concentration in simulated solution. The corrosion degree of X70 steel was the least under the environment of low temperature, deficient oxygen and weak acid.
文摘The corrosion behavior of a weathering steel SPA-C and two acid resistance steels（ S-TEN1 and ND）in sulfuric acid solution was investigated by using potentiodynamic polarization and weight loss measurement techniques. Both potentiodynamic polarization and weight loss measurement tests indicated that corrosion resistance of these three alloy steels was as follows： ND ~ S-TEN1 〉 SPA-C. Surface analysis of the corroded samples conducted after the immersion test indicated that two layers were formed on the substrates, with the outer layer comprising FeSO4. H20 and the inner layer mainly comprising iron oxides. The addition of Cu, Cr, and Sb refined the corrosion products and improved the adhesion ability between the rust layer and the substrate.