A layer of graphene(GR)particles was successfully deposited at the interface between Co(OH)2 nanoparticles and TiO2 nanotubes,aiming to improve the photoelectrochemical performance of the large-bandgap semiconductor T...A layer of graphene(GR)particles was successfully deposited at the interface between Co(OH)2 nanoparticles and TiO2 nanotubes,aiming to improve the photoelectrochemical performance of the large-bandgap semiconductor TiO2.The obtained Co(OH)2/GR/TiO2 was extensively characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),X-ray photoelectron spectroscopy(XPS),UV–vis absorption spectra and photoluminescence(PL)emission spectra.Electrochemical impedance spectra,photogenerated potential-time(E-t),photocurrent density-time(i-t)and i-E curves and open circuit potential(OCP)curves were measured to investigate the photoelectrochemical activities and photogenerated cathodic protection properties.The results revealed that Co(OH)2/GR/TiO2 exhibits excellent photoelectrochemical and photogenerated cathodic performance due to synergistic effect between Co(OH)2 and graphene.Co(OH)2 and graphene co-modified TiO2 photoanode could provide an effective protection for 304 stainless steel(304 SS)in 3.5 wt%Na Cl solution for 12 h,which would be promising for future practical applications in the field of marine corrosion protection.展开更多
通过连续离子层吸附法(SILAR)在TiO_(2)纳米管上负载Bi_(2)S_(3),通过XRD、SEM、XPS等手段对Bi_(2)S_(3)/TiO_(2)纳米复合材料的形貌、结构、元素组成和价态进行表征。同时在模拟太阳光条件下进行光电化学性能测试。Bi_(2)S_(3)改性后...通过连续离子层吸附法(SILAR)在TiO_(2)纳米管上负载Bi_(2)S_(3),通过XRD、SEM、XPS等手段对Bi_(2)S_(3)/TiO_(2)纳米复合材料的形貌、结构、元素组成和价态进行表征。同时在模拟太阳光条件下进行光电化学性能测试。Bi_(2)S_(3)改性后复合材料的带隙减小,光生载流子复合率大幅下降,当Bi_(2)S_(3)循环5次时,TiO_(2)纳米复合材料的光电化学性能最好。带隙减小到2.9 e V,光电流密度由改性前的200μA·cm^(-2)提升至550μA·cm^(-2),是改性前的2.75倍;将其与304不锈钢耦合后,电位降至-1.0 V,比改性前的耦合电位低80 m V,可以进一步提升对304不锈钢的光生阴极保护效果。展开更多
基金supported financially by the National Natural Science Foundation of China(Nos.51622106 and 51871049)the Fundamental Research Funds for the Central Universities(No.160708001).
文摘A layer of graphene(GR)particles was successfully deposited at the interface between Co(OH)2 nanoparticles and TiO2 nanotubes,aiming to improve the photoelectrochemical performance of the large-bandgap semiconductor TiO2.The obtained Co(OH)2/GR/TiO2 was extensively characterized by X-ray diffraction(XRD),scanning electron microscopy(SEM),transmission electron microscopy(TEM),X-ray photoelectron spectroscopy(XPS),UV–vis absorption spectra and photoluminescence(PL)emission spectra.Electrochemical impedance spectra,photogenerated potential-time(E-t),photocurrent density-time(i-t)and i-E curves and open circuit potential(OCP)curves were measured to investigate the photoelectrochemical activities and photogenerated cathodic protection properties.The results revealed that Co(OH)2/GR/TiO2 exhibits excellent photoelectrochemical and photogenerated cathodic performance due to synergistic effect between Co(OH)2 and graphene.Co(OH)2 and graphene co-modified TiO2 photoanode could provide an effective protection for 304 stainless steel(304 SS)in 3.5 wt%Na Cl solution for 12 h,which would be promising for future practical applications in the field of marine corrosion protection.
文摘通过连续离子层吸附法(SILAR)在TiO_(2)纳米管上负载Bi_(2)S_(3),通过XRD、SEM、XPS等手段对Bi_(2)S_(3)/TiO_(2)纳米复合材料的形貌、结构、元素组成和价态进行表征。同时在模拟太阳光条件下进行光电化学性能测试。Bi_(2)S_(3)改性后复合材料的带隙减小,光生载流子复合率大幅下降,当Bi_(2)S_(3)循环5次时,TiO_(2)纳米复合材料的光电化学性能最好。带隙减小到2.9 e V,光电流密度由改性前的200μA·cm^(-2)提升至550μA·cm^(-2),是改性前的2.75倍;将其与304不锈钢耦合后,电位降至-1.0 V,比改性前的耦合电位低80 m V,可以进一步提升对304不锈钢的光生阴极保护效果。