The conversion coating was formed by dipping AA6061 in a fluorotitanate/zirconate acid and amino trimethylene phosphonic acid （ATMP） solution at room temperature. The formation process and the anti-corrosion perform...The conversion coating was formed by dipping AA6061 in a fluorotitanate/zirconate acid and amino trimethylene phosphonic acid （ATMP） solution at room temperature. The formation process and the anti-corrosion performance of the conversion coating were investigated using electrochemical test and salt spray test （SST）, respectively. The electrochemical test shows that the Zr/Ti and ATMP coating improves the corrosion resistance of AA6061 as good as the chromate （VI） coating. But the results of SST show that the corrosion resistance of Zr/Ti and ATMP coating is not as good as the chromate （VI） coating. The corrosion area is less than 2% after 72 h.展开更多
A convenient, efficient and general method has been developed for synthesis of H-phosphonate mono and diesters of AZT and d4T through one-pot reaction of phosphonic acid with AZT or d4T and different alcohols using pi...A convenient, efficient and general method has been developed for synthesis of H-phosphonate mono and diesters of AZT and d4T through one-pot reaction of phosphonic acid with AZT or d4T and different alcohols using pivaloyl chloride as condensing agent under mild conditions.展开更多
基金supported by the Science and Technology Plan Project of Liaoning Province,China(No.2006221011).
文摘The conversion coating was formed by dipping AA6061 in a fluorotitanate/zirconate acid and amino trimethylene phosphonic acid （ATMP） solution at room temperature. The formation process and the anti-corrosion performance of the conversion coating were investigated using electrochemical test and salt spray test （SST）, respectively. The electrochemical test shows that the Zr/Ti and ATMP coating improves the corrosion resistance of AA6061 as good as the chromate （VI） coating. But the results of SST show that the corrosion resistance of Zr/Ti and ATMP coating is not as good as the chromate （VI） coating. The corrosion area is less than 2% after 72 h.
基金Project supported by Excellent Dissertation Foundation by the Chinese Ministry of Education (No. 200222).
文摘A convenient, efficient and general method has been developed for synthesis of H-phosphonate mono and diesters of AZT and d4T through one-pot reaction of phosphonic acid with AZT or d4T and different alcohols using pivaloyl chloride as condensing agent under mild conditions.