Ceramic coating incorporated with nano-SiC was obtained on AZ91D magnesium alloy during MAO by adding nano-SiC into the silicate-aluminate-based composite electrolyte. The microstructure, thickness, phase analysis, el...Ceramic coating incorporated with nano-SiC was obtained on AZ91D magnesium alloy during MAO by adding nano-SiC into the silicate-aluminate-based composite electrolyte. The microstructure, thickness, phase analysis, element composition and hardness of the coatings were respectively investigated by scanning electron microscopy（SEM）, film thickness meter, X-ray diffraction （XRD）, energy disperse spectroscopy（EDS） and Vickers hardness tester. The wear resistance of Mg alloy and coatings were evaluated by friction and wear apparatus, while the corrosion resistance of Mg alloy and coatings were evaluated by potentiodynamic polarization test and electrochemical impedance spectroscopy （EIS）. The results show that after adding nano-SiC into the electrolyte, both the striking voltage and final voltage decrease, the size and number of the micropore on the surface of the coating decrease, the thickness and hardness of the coating increase, both the wear resistance and corrosion resistance of the coating raise.展开更多
Zn has been regarded as new kind of potential implant biomaterials due to the desirable biodegradability and good biocompatibility,but the low strength and ductility limit its application in bone repairs.In the presen...Zn has been regarded as new kind of potential implant biomaterials due to the desirable biodegradability and good biocompatibility,but the low strength and ductility limit its application in bone repairs.In the present study,nano-SiC was incorporated into Zn matrix via laser melting,aiming to improve the mechanical performance.The microstructure analysis showed that nano-SiC distributed along Zn grain boundaries.During the laser rapid solidification,nano-SiC particles acted as the sites for heterogeneous nucleation,which resulted in the reduction of Zn grain size from 250μm to 15μm with 2 wt%SiC(Zn-2 SiC).Meanwhile,nano-SiC acted as a reinforcer by virtue of Orowan strengthening and dispersion strengthening.As a consequence,the nanocomposites showed maximal compressive yield strength(121.8±5.3 MPa)and high microhardness(72.24±3.01 HV),which were increased by 441%and 78%,respectively,compared with pure Zn.Moreover,fracture analysis indicated a more ductile fracture of the nanocomposites after the incorporation of nano-SiC In addition,the nanocomposites presented favorable biocompatibility and accelerated degradation caused by intergranular corrosion.These findings suggested that the nano-SiC reinforced Zn biocomposites may be the potential candidates for orthopedic implants.展开更多
The aging-hardening kinetics of powder metallurgy processed 2014Al alloy and its composite have been studied. The existence of n-SiC particulates leads to the increase of peak hardness. Interestingly, the aginghardeni...The aging-hardening kinetics of powder metallurgy processed 2014Al alloy and its composite have been studied. The existence of n-SiC particulates leads to the increase of peak hardness. Interestingly, the aginghardening peak of the composite takes place at earlier time than that of the unreinforced alloy. Transmission electron microscopy（TEM） studies indicated that the major precipitation phases are Al_5Cu_2Mn_3 and θ′（Al_2Cu）. Besides, Ω phase appeared in both specimens at peak hardening condition, which has been rarely observed previously in aluminum metal matrix composites without Ag. Accelerated aging kinetics and increased peak hardness may be attributed to the higher dislocation density resulted from the mismatch of coefficients of thermal expansion between n-SiC and 2014Al matrix. The results are beneficial to fabricating high performance composites for the application in automobile field such as pistons, driveshaft tubes, brake rotors, bicycle frames, railroad brakes.展开更多
基金Project(12504230006) supported by the Priority Academic Program Development of Jiangsu Higher Education Institutions,China
文摘Ceramic coating incorporated with nano-SiC was obtained on AZ91D magnesium alloy during MAO by adding nano-SiC into the silicate-aluminate-based composite electrolyte. The microstructure, thickness, phase analysis, element composition and hardness of the coatings were respectively investigated by scanning electron microscopy（SEM）, film thickness meter, X-ray diffraction （XRD）, energy disperse spectroscopy（EDS） and Vickers hardness tester. The wear resistance of Mg alloy and coatings were evaluated by friction and wear apparatus, while the corrosion resistance of Mg alloy and coatings were evaluated by potentiodynamic polarization test and electrochemical impedance spectroscopy （EIS）. The results show that after adding nano-SiC into the electrolyte, both the striking voltage and final voltage decrease, the size and number of the micropore on the surface of the coating decrease, the thickness and hardness of the coating increase, both the wear resistance and corrosion resistance of the coating raise.
基金supported financially by the National Natural Science Foundation of China (Nos.51705540,81871494 and 81871498)the Hunan Provincial Natural Science Foundation of China (Nos.2018JJ3671 and 2019JJ50588)+6 种基金the GuangdongProvince Higher Vocational Colleges & Schools Pearl River Scholar Funded Scheme (2018)the Open Sharing Fund for the Largescale Instruments and Equipments of Central South Universitythe Project of Hunan Provincial Science and Technology Plan (No.2017RS3008)the Shenzhen Science and Technology Plan Project (No.JCYJ20170817112445033)the National Postdoctoral Program for Innovative Talents (No.BX201700291)the Hunan Science and Technology Innovation Plan (Nos.2018SK2105 and kq1606001)the China Postdoctoral Science Foundation (No. 2018M632983)
文摘Zn has been regarded as new kind of potential implant biomaterials due to the desirable biodegradability and good biocompatibility,but the low strength and ductility limit its application in bone repairs.In the present study,nano-SiC was incorporated into Zn matrix via laser melting,aiming to improve the mechanical performance.The microstructure analysis showed that nano-SiC distributed along Zn grain boundaries.During the laser rapid solidification,nano-SiC particles acted as the sites for heterogeneous nucleation,which resulted in the reduction of Zn grain size from 250μm to 15μm with 2 wt%SiC(Zn-2 SiC).Meanwhile,nano-SiC acted as a reinforcer by virtue of Orowan strengthening and dispersion strengthening.As a consequence,the nanocomposites showed maximal compressive yield strength(121.8±5.3 MPa)and high microhardness(72.24±3.01 HV),which were increased by 441%and 78%,respectively,compared with pure Zn.Moreover,fracture analysis indicated a more ductile fracture of the nanocomposites after the incorporation of nano-SiC In addition,the nanocomposites presented favorable biocompatibility and accelerated degradation caused by intergranular corrosion.These findings suggested that the nano-SiC reinforced Zn biocomposites may be the potential candidates for orthopedic implants.
基金Financial support by the National Basic Research Program of China(“973”Program,No.2012CB619600)the National Natural Science Foundation of China(No.51474111)+2 种基金the Science and Technology Development Project of Jilin Province(No.20160519002JH)support came from the Fundamental Research Funds for the Central Universities(JCKY-QKJC02)the Chang Bai Mountain Scholars Program(2013014)
文摘The aging-hardening kinetics of powder metallurgy processed 2014Al alloy and its composite have been studied. The existence of n-SiC particulates leads to the increase of peak hardness. Interestingly, the aginghardening peak of the composite takes place at earlier time than that of the unreinforced alloy. Transmission electron microscopy（TEM） studies indicated that the major precipitation phases are Al_5Cu_2Mn_3 and θ′（Al_2Cu）. Besides, Ω phase appeared in both specimens at peak hardening condition, which has been rarely observed previously in aluminum metal matrix composites without Ag. Accelerated aging kinetics and increased peak hardness may be attributed to the higher dislocation density resulted from the mismatch of coefficients of thermal expansion between n-SiC and 2014Al matrix. The results are beneficial to fabricating high performance composites for the application in automobile field such as pistons, driveshaft tubes, brake rotors, bicycle frames, railroad brakes.