Effects of modified triethanolamine as cement grinding aids on particles characteristics and mechanical property of cement were studied, and its reaction mechanism was analyzed by IR, Zeta potential, SEM, XRD and TG-D...Effects of modified triethanolamine as cement grinding aids on particles characteristics and mechanical property of cement were studied, and its reaction mechanism was analyzed by IR, Zeta potential, SEM, XRD and TG-DTA. The results show that the content of 3-32 μm particles for cement with 0.015% modified triethanolamine（M-TEA） is increased by 12.4%, and the compressive strengths of cement with 0.03% M-TEA are increased by 5.5 and 8.2 MPa at 3 and 28 days, respectively. And both the grinding and enhancement effects of M-TEA on cement are better than triethanolamine. The mechanism analysis shows that M-TEA not only has the amino and hydroxyl groups of TEA, but also has the ester, carbonyl, carboxyl groups which easily combine with metal ions of cement minerals, resulting in that M-TEA can promote surface adsorption and shield the unsaturated charges in the surface and crack section of particles, thus particles reunion is prevented and grinding efficiency is improved. Enhancement of M-TEA on cement mainly lies in that it can promote or induce hydration reaction of cement mineral with gypsum and water, which accelerates formation of hydration products, and then improves the structure and morphology of cement hydration products, thus the uniformity and compactness of product structure is increased.展开更多
基金Funded by the National Natural Science Foundation of China(No.50872151)
文摘Effects of modified triethanolamine as cement grinding aids on particles characteristics and mechanical property of cement were studied, and its reaction mechanism was analyzed by IR, Zeta potential, SEM, XRD and TG-DTA. The results show that the content of 3-32 μm particles for cement with 0.015% modified triethanolamine（M-TEA） is increased by 12.4%, and the compressive strengths of cement with 0.03% M-TEA are increased by 5.5 and 8.2 MPa at 3 and 28 days, respectively. And both the grinding and enhancement effects of M-TEA on cement are better than triethanolamine. The mechanism analysis shows that M-TEA not only has the amino and hydroxyl groups of TEA, but also has the ester, carbonyl, carboxyl groups which easily combine with metal ions of cement minerals, resulting in that M-TEA can promote surface adsorption and shield the unsaturated charges in the surface and crack section of particles, thus particles reunion is prevented and grinding efficiency is improved. Enhancement of M-TEA on cement mainly lies in that it can promote or induce hydration reaction of cement mineral with gypsum and water, which accelerates formation of hydration products, and then improves the structure and morphology of cement hydration products, thus the uniformity and compactness of product structure is increased.